Abstrakt
In elements of steel structures working at low temperatures, there is a risk of appearance of brittle fracture. This risk is reduced through the use of certified materials having guaranteed strength at a given temperature. A method which is most frequently used to determine brittle fracture toughness is the Charpy impact test, preformed for a given temperature. For offshore structures intended to work in the arctic climat e, the certifying institutions more and more often require Crack Tip Opening Displacement (CTOD) tests instead of conventional impact tests, especially for steel and welded joints of more than 40 mm in thickness in the case of high-strength steel, and more than 50 mm for the remaining steels. The geometry of specimens and the test procedure are standardised; however, these standards provide some margin for specimen notch depth. The paper analyses the effect of notch depth difference, within the range permitted by the standards, on the recorded CTOD values of a given material. The analysis was performed via numerical modelling of destruction of specimens with different notch geometries and further verification of the obtained numerical results in laboratory tests. The calculations were carried out at the Academic Computer Centre in Gdansk.
Cytowania
-
2
CrossRef
-
0
Web of Science
-
2
Scopus
Autorzy (2)
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2478/pomr-2018-0058
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
Polish Maritime Research
nr 25,
strony 85 - 91,
ISSN: 1233-2585 - Język:
- angielski
- Rok wydania:
- 2018
- Opis bibliograficzny:
- Kowalski J., Kozak J.: THE EFFECT OF NOTCH DEPTH ON CTOD VALUES IN FRACTURE TESTS OF STRUCTURAL STEEL ELEMENTS// Polish Maritime Research. -Vol. 25, iss. 2(98) (2018), s.85-91
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2478/pomr-2018-0058
- Źródła finansowania:
-
- Działalność statutowa/subwencja
- Weryfikacja:
- Politechnika Gdańska
Powiązane datasety
- dane badawcze EH36 steel for shipbuilding - fracture documentation for CTOD test (plate thicnkness 60mm), a0/W = 0.6
- dane badawcze EH36 steel for shipbuilding (plate thicnkness 40 mm) - CMOD - force record, a0/W = 0.5
- dane badawcze EH36 steel for shipbuilding (plate thicnkness 40 mm) - CMOD - force record, a0/W = 0.6
- dane badawcze EH36 steel for shipbuilding - fracture documentation for CTOD test (plate thicnkness 40mm), a0/W = 0.5
- dane badawcze EH36 steel for shipbuilding - fracture SEM investigation (plate thicnkness 30mm), a0/W = 0.6
- dane badawcze EH36 steel for shipbuilding - fracture SEM investigation (plate thicnkness 30mm), a0/W = 0.5
- dane badawcze EH36 steel for shipbuilding - fracture documentation for CTOD test (plate thicnkness 30mm), a0/W = 0.6
- dane badawcze EH36 steel for shipbuilding - fracture documentation for CTOD test (plate thicnkness 30mm), a0/W = 0.5
- dane badawcze EH36 steel for shipbuilding - Charpy impact test reslut in vary tempetatures
- dane badawcze EH36 steel for shipbuilding - fracture documentation for CTOD test (plate thicnkness 40mm), a0/W = 0.6
wyświetlono 160 razy