Be-Na-(Li)-Si oxide glasses containing up to 15 mol% of BeO were prepared. Their structure was characterized by X-ray powder diffraction and Raman as well as infrared spectroscopic techniques, while their chemical compositions were examined by Inductively Coupled Plasma Optical Emission Spectrometry. All materials were found to be amorphous and contain Al contaminations from minor dissolution of the alumina crucibles. The results of Raman and IR spectroscopies showed that BeO addition to Na-(Li)-Si glass systems resulted in the formation of [BeO4/2]2− tetrahedra which are inserted into the silicate glass network, demonstrating the intermediate glass-forming role of BeO. In parallel, the effective destruction of Si-O-Si bridges was observed by vibrational spectroscopy. The glass transition temperature was studied by Differential Thermal Analysis and found to range from about 431 °C to 551 °C. A significant increase in Tg by 70 °C was found as SiO2 was substituted by up to 15 mol% BeO.
Cytowania
-
1 4
CrossRef
-
0
Web of Science
-
1 5
Scopus
Autorzy (8)
-
Sharafat Ali profesor
- Linnæus University Department of Built Environment and Energy Technology,
-
Doris Möncke profesor
- Alfred University Inamori School of Engineering at the New York State College of Ceramics
-
N Tagiara
- National Hellenic Research Foundation Theoretical and Physical Chemistry Institute
-
Efstratios Kamitsos profesor
- National Hellenic Research Foundation Theoretical and Physical Chemistry Institute
-
H Segawa
- National Institute for Materials Science
-
Mirva Eriksson DR
- Stockholm University Department of Inorganic Chemistry
-
Bo Jonson profesor
- Linnæus University Department of Built Environment and Energy Technology,
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jnoncrysol.2019.119532
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
JOURNAL OF NON-CRYSTALLINE SOLIDS
nr 521,
strony 1 - 10,
ISSN: 0022-3093 - Język:
- angielski
- Rok wydania:
- 2019
- Opis bibliograficzny:
- Wójcik N. A., Ali S., Möncke D., Tagiara N., Kamitsos E., Segawa H., Eriksson M., Jonson B.: The influence of Be addition on the structure and thermal properties of alkali-silicate glasses// JOURNAL OF NON-CRYSTALLINE SOLIDS. -Vol. 521, (2019), s.1-10
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jnoncrysol.2019.119532
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 161 razy
Publikacje, które mogą cię zainteresować
Investigation of the structural and thermal properties of aluminum-rich Ca–Al–Si–O–N glasses
- S. Ali,
- J. Ryl,
- A. S. Hakeem
- + 2 autorów
The effect of nitrogen on the structure and thermal properties of beryllium-containing Na-(Li)-Si-O-N glasses
- N. Wójcik,
- B. Jonson,
- D. Möncke
- + 4 autorów
Influence of synthesis conditions on glass formation, structure and thermal properties in the Na 2 O-CaO-P 2 O 5 system doped with Si 3 N 4 and Mg
- N. A. Wójcik,
- B. Jonson,
- D. Möncke
- + 6 autorów