The influence of the welding environment on the properties of Tekken joints made from S355J2C+N steel

Abstrakt

There are three main methods of underwater welding: dry, wet and intermediate between them, by using the local dry chamber. Due to low costs, the most common method is the wet welding with the use of covered electrodes. Water as a welding environment carries out a lot of problems. The first is limited visibility and instability of the welding arc. The biggest problem during underwater welding is high susceptibility to cold cracking, resulting from the increased diffusible hydrogen content in deposited metal and high stress values. In the work, Tekken joints from S355J2C+N steel were made in air and in water environment. The joints were subjected to non-destructive visual (VT) and penetrant (PT) tests. Then, macroscopic tests and hardness measurements were performed. The results confirm the literature reports that the water environment causes an increase in hardness in the heat affected zone (HAZ), which promotes the formation of cracks in welding joints.

Cytowania

  • 0

    CrossRef

  • 0

    Web of Science

  • 0

    Scopus

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
Opublikowano w:
Przegląd Spawalnictwa strony 8 - 12,
ISSN: 0033-2364
Język:
angielski
Rok wydania:
2019
Opis bibliograficzny:
Tomków J., Janeczek A.: The influence of the welding environment on the properties of Tekken joints made from S355J2C+N steel// Przegląd Spawalnictwa. -., nr. 1 (2019), s.8-12
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.26628/wtr.v91i1.997
Źródła finansowania:
  • Działalność statusowa
Weryfikacja:
Politechnika Gdańska

wyświetlono 4 razy

Publikacje, które mogą cię zainteresować

Meta Tagi