Thermoelectric properties of bismuth-antimony-telluride alloys obtained by reduction of oxide reagents
Abstrakt
The BieSbeTe alloys with different Bi/Sb/Te ratio were fabricated by an innovative method. For that purpose the oxide reagents were melted at high temperature, then quenched to form pellets, milled to a powder and finally reduced in hydrogen at various temperatures. Complex structures consisting of connected thin layers forming a continuous path between nano- and micrometer size grains have been obtained. The electrical conductivity, Seebeck coefficient and thermal conductivity have been determined over temperature range from 196 to þ300 C in argon atmosphere. The highest figure of merit in the whole temperature range was found for Bi0.4Sb1.6Te3 compound reduced at 400 C for 10 h in hydrogen atmosphere. At a near-room temperature the figure of merit of this compound was found to be equal to 0.7.
Cytowania
-
1 2
CrossRef
-
0
Web of Science
-
1 3
Scopus
Autorzy (4)
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
MATERIALS CHEMISTRY AND PHYSICS
nr 177,
strony 353 - 359,
ISSN: 0254-0584 - Język:
- angielski
- Rok wydania:
- 2016
- Opis bibliograficzny:
- Bochentyn B., Miruszewski T., Karczewski J., Kusz B.: Thermoelectric properties of bismuth-antimony-telluride alloys obtained by reduction of oxide reagents// MATERIALS CHEMISTRY AND PHYSICS. -Vol. 177, (2016), s.353-359
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.matchemphys.2016.04.039
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 145 razy
Publikacje, które mogą cię zainteresować
Hydrogen degradation of pre-oxidized zirconium alloys
- A. Szoka,
- G. Gajowiec,
- A. Zieliński
- + 3 autorów