Ultrafast high-temperature sintering (UHS) is an innovative sintering technique that can densify ceramics in a few seconds, dramatically reducing the carbon footprint and firing costs. In this work, the feasibility of applying UHS in Gd-doped ceria (GDC) and GDC-Er-stabilized bismuth oxide (ESB) composite powders was investigated. At high UHS currents (22-24 A), a fully dense GDC sample with a large grain size was obtained. Nonetheless, most of the GDC pellets exhibited micro/macro cracks, which were reduced by lowering the sample thickness. Moreover, the GDC-ESB composite sample exhibits no cracks or fragmentation at all, thanks to ESB as a sintering aid. This type of sample was further characterized from an electrochemical and electromechanical point of view. The GDC-ESB material displays an ionic conductivity value of ~1.5 x 10−2 S/cm at 600 °C and frequency-stable (0.1-350 Hz) room temperature electrostriction strain coefficient of ~10−18 (m/V)2.
Cytowania
-
0
CrossRef
-
0
Web of Science
-
1
Scopus
Autorzy (7)
-
Ahsanul Kabir
-
Emanuele De Bona
-
Maxim Varenik
-
Mattia Biesuz
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.oceram.2024.100551
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Open Ceramics
nr 17,
ISSN: - Język:
- angielski
- Rok wydania:
- 2024
- Opis bibliograficzny:
- Kabir A., Lemieszek B., Karczewski J., De Bona E., Varenik M., Molin S., Biesuz M.: Ultrafast high-temperature sintering (UHS) of cerium oxide-based compound// Open Ceramics -Vol. 17, (2024), s.100551-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.oceram.2024.100551
- Źródła finansowania:
-
- PRIME programme of the German Academic Exchange Service (DAAD) with funds from the German Federal Ministry of Education and Research (BMBF) and JECS Trust-Fund Contract-2021275 and Departments of Excellence 2023–27” program (L.232/2016)
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 54 razy
Publikacje, które mogą cię zainteresować
Gigantic electro-chemo-mechanical properties of nanostructured praseodymium doped ceria
- V. B. Tinti,
- A. Kabir,
- J. K. Han
- + 2 autorów
Electrical conductivity of nanostructured acceptor-doped ceria fabricated by spark plasma sintering (SPS)
- A. Kabir,
- S. Colding-Jørgensen,
- S. Molin
- + 1 autorów
New synthesis route of highly porous InxCo4Sb12 with strongly reduced thermal conductivity
- N. Gostkowska-Lekner,
- B. Trawinski,
- A. Kosonowski
- + 5 autorów