Visible light photoactivity of TiO2loaded with monometallic(Au or Pt) and bimetallic (Au/Pt) nanoparticles

Abstrakt

TiO2modified with monometallic (Au or Pt) and bimetallic (Au/Pt) nanoparticles have been preparedusing a water-in-oil microemulsion system (water/AOT/cyclohexane) followed by calcination step. Theeffect of metal ratio, reducing agent type (NaBH4or N2H4), TiO2matrix type (P-25, ST-01, TiO-5, TiO2nano-tubes or TiO2obtained by TIP hydrolysis) as well as calcination temperature (from 350 to 650◦C) weresystematically investigated. Obtained photocatalysts were characterized by UV–vis diffuse-reflectancespectroscopy (DRS), BET surface area measurements, scanning transmission microscopy (STEM), X-raydiffraction analysis (XRD), and X-ray photoelectron spectroscopy (XPS). Photocatalytic activity undervisible light ( > 420 nm) has been estimated in phenol degradation reaction in aqueous phase. Theresults showed that phenol degradation rate under visible light in the presence of TiO2loaded with Au/Ptnanoparticles differed from 0.7 to 2.2 mol dm−3min−1for samples prepared using different reducingagent. Sodium borohydride (NaBH4) favors formation of smaller Au/Pt nanoparticles and higher amountgold in Au/Pt is in the form of electronegative species (Auı−) resulted in higher photoactivity. TiO2obtained by TIP hydrolysis in microemulsion system seems to be the best support for Au/Pt nanoparticlesfrom all among investigated matrix. It was also observed that enhancement of calcination temperaturefrom 450 to 650◦C resulted in rapid drop of Au/Pt-TiO2photoactivity under visible light due to surfacearea shrinkage, crystal structure change and probably change in Au/Pt nanoparticles morphology.

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuł w czasopiśmie wyróżnionym w JCR
Opublikowano w:
APPLIED SURFACE SCIENCE nr 317, strony 1131 - 1142,
ISSN: 0169-4332
Język:
angielski
Rok wydania:
2014
Opis bibliograficzny:
Gołąbiewska A., Lisowski W., Jarek M., Nowaczyk G., Zielińska-Jurek A., Zaleska-Medynska A.: Visible light photoactivity of TiO2loaded with monometallic(Au or Pt) and bimetallic (Au/Pt) nanoparticles// APPLIED SURFACE SCIENCE. -Vol. 317, (2014), s.1131-1142
Weryfikacja:
Politechnika Gdańska

wyświetlono 10 razy

Publikacje, które mogą cię zainteresować

Meta Tagi