Water absorption and blistering of glass fibre-reinforced polymer marine laminates with nanoparticle-modified coatings

Abstrakt

Macro and microstructural damage was studied in typical glass fibre-reinforced polymer laminates with two types of coating systems – (a) isophtalic gel coat: pure or mixed with SiO2 nanoparticles 5 wt% (5%N) or 10 wt% (10%N) and (b) a two-layer coating system: urethane-modified vinyl ester-based gel coat and additional polyester barrier coat layer. Accelerated tests were performed at 50C for 50 days for specimens with nanoparticle-modified gel and for the specimens with or without a barrier coat. Long-term ageing behaviour at 23C was assessed for the two-layer systems. Nanoparticle-reinforced specimens (10%) showed some advantage over ‘barrier coat systems’ in terms of blister incubation time (16 and 13 days, respectively), while for 5% and 0% nanoparticles, blister incubation times were 3 and 7 days, respectively. Round and/or acicular blisters were observed on the examined surfaces. The varying size, shape and distribution of blisters was illustrated by macro and micrographs showing various failure modes associated with surface blisters.

Cytowania

  • 2 2

    CrossRef

  • 0

    Web of Science

  • 1 9

    Scopus

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Słowa kluczowe

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuł w czasopiśmie wyróżnionym w JCR
Opublikowano w:
JOURNAL OF COMPOSITE MATERIALS nr 48, strony 2805 - 2813,
ISSN: 0021-9983
Język:
angielski
Rok wydania:
2014
Opis bibliograficzny:
Landowski M., Budzik M., Imielińska K.: Water absorption and blistering of glass fibre-reinforced polymer marine laminates with nanoparticle-modified coatings// JOURNAL OF COMPOSITE MATERIALS. -Vol. 48, nr. 23 (2014), s.2805-2813
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1177/0021998313503877
Weryfikacja:
Politechnika Gdańska

wyświetlono 141 razy

Publikacje, które mogą cię zainteresować

Meta Tagi