Abstrakt
The paper presents the results of NDT examinations, metallographic tests and risk assessment of degradation related to corrosion of amine regeneration unit in a desulphurisation system. Intensive corrosion resulting from acid gases environment upon water condensation causes perforation of the pipeline. Detailed analysis reveals cracking related to the mechanism of wet H2S. Hydrogen penetration, resulting from the wet H2S process, causes a decrease in mechanical properties of steel and an increase in hydrogen content inside steel. Corrosion results mostly from high stream velocity, the presence of acid gases (with high ammonia content), the presence of amine and low stream temperature.
Cytowania
-
0
CrossRef
-
0
Web of Science
-
0
Scopus
Autorzy (6)
-
Maciej Kalinowski
-
Igor Lasota
-
Piotr Maruszewski
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION
nr 75,
strony 78 - 785,
ISSN: 0947-5117 - Język:
- angielski
- Rok wydania:
- 2024
- Opis bibliograficzny:
- Orlikowski J., Kalinowski M., Lasota I., Maruszewski P., Szociński M., Darowicki K.: Wet H2S corrosion and degradation of pipeline in amine regeneration system// MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION -Vol. 75,iss. 6 (2024), s.78-785
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1002/maco.202314252
- Źródła finansowania:
-
- Publikacja bezkosztowa
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 81 razy
Publikacje, które mogą cię zainteresować
Effect of wet Hydrogen Sulfide on Carbon Steels Degradation in Refinery Based on Case Study
- J. Orlikowski,
- A. Jażdżewska,
- İ. Uygur
- + 3 autorów
Wpływ środowiska na absorpcję wodoru przez stale 26H2MF i 34HNM
- B. Świeczko-Żurek,
- E. Łunarska-Borowiecka,
- A. Zieliński