Filtry
wszystkich: 1971
wybranych: 175
-
Katalog
- Publikacje 1262 wyników po odfiltrowaniu
- Czasopisma 15 wyników po odfiltrowaniu
- Konferencje 4 wyników po odfiltrowaniu
- Osoby 33 wyników po odfiltrowaniu
- Projekty 1 wyników po odfiltrowaniu
- Kursy Online 14 wyników po odfiltrowaniu
- Wydarzenia 1 wyników po odfiltrowaniu
- Dane Badawcze 641 wyników po odfiltrowaniu
Filtry wybranego katalogu
Wyniki wyszukiwania dla: multifunctional microwave component
-
Electronic transition dipole moment functions of the first singlet Delta gerade and first triplet Delta ungerade states of the Lithium dimer
Dane BadawczeElectronic transition dipole moment functions (ETDMF) of the first singlet Delta gerade (1sDg) and first triplet Delta ungerade (1tDu) states have been calculated for the Lithium dimer. ETDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. The results of the four ETDMFs have been obtained...
-
Electronic transition dipole moment functions of the second triplet Sigma ungerade plus state of the Lithium dimer
Dane BadawczeElectronic transition dipole moment functions (ETDMF) of the second triplet Sigma ungerade plus (2tSu+) state have been calculated for the Lithium dimer. ETDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. The results of the five ETDMFs have been obtained by the nonrelativistic multireference...
-
Electronic transition dipole moment functions of the second singlet Sigma ungerade plus and second triplet Sigma gerade plus states of the Lithium dimer
Dane BadawczeElectronic transition dipole moment functions (ETDMF) of the second singlet Sigma ungerade plus (2sSu+) and second triplet Sigma gerade plus (2tSg+) states have been calculated for the Lithium dimer. ETDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. The results of the four ETDMFs...
-
Electronic transition dipole moment functions of the third singlet Sigma gerade plus state of the Lithium dimer
Dane BadawczeElectronic transition dipole moment functions (ETDMF) of the third singlet Sigma gerade plus (3sSg+) state have been calculated for the Lithium dimer. ETDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. The results of the five ETDMFs have been obtained by the nonrelativistic multireference...
-
Electronic transition dipole moment functions of the first singlet Sigma ungerade plus and first triplet Sigma gerade plus states of the Lithium dimer
Dane BadawczeElectronic transition dipole moment functions (ETDMF) of the first singlet Sigma ungerade plus (1sSu+) and first triplet Sigma gerade plus (1tSg+) states have been calculated for the Lithium dimer. ETDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. The results of the four ETDMFs...
-
Electronic transition dipole moment functions of the third triplet Sigma ungerade plus state of the Lithium dimer
Dane BadawczeElectronic transition dipole moment functions (ETDMF) of the third triplet Sigma ungerade plus (3tSu+) state have been calculated for the Lithium dimer. ETDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. The results of the five ETDMFs have been obtained by the nonrelativistic multireference...
-
Electronic transition dipole moment functions of the fourth triplet Sigma ungerade plus state of the Lithium dimer
Dane BadawczeElectronic transition dipole moment functions (ETDMF) of the fourth triplet Sigma ungerade plus (4tSu+) state have been calculated for the Lithium dimer. ETDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. The results of the five ETDMFs have been obtained by the nonrelativistic multireference...
-
Electronic transition dipole moment functions of the fourth singlet Sigma gerade plus state of the Lithium dimer
Dane BadawczeElectronic transition dipole moment functions (ETDMF) of the fourth singlet Sigma gerade plus (4sSg+) state have been calculated for the Lithium dimer. ETDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. The results of the five ETDMFs have been obtained by the nonrelativistic multireference...
-
Electronic transition dipole moment functions of the first singlet Pi gerade and first triplet Pi gerade states of the Lithium dimer
Dane BadawczeElectronic transition dipole moment functions (ETDMF) of the first singlet Pi gerade (1sPg) and first triplet Pi gerade (1tPg) states have been calculated for the Lithium dimer. ETDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. The results of the four ETDMFs have been obtained...
-
Electronic transition dipole moment functions of the second singlet Sigma gerade plus state of the Lithium dimer
Dane BadawczeElectronic transition dipole moment functions (ETDMF) of the second singlet Sigma gerade plus (2sSg+) state have been calculated for the Lithium dimer. ETDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. The results of the five ETDMFs have been obtained by the nonrelativistic multireference...
-
Electronic transition dipole moment functions of the fifth singlet Sigma gerade plus state of the Lithium dimer
Dane BadawczeElectronic transition dipole moment functions (ETDMF) of the fifth singlet Sigma gerade plus (5sSg+) state have been calculated for the Lithium dimer. ETDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. The results of the five ETDMFs have been obtained by the nonrelativistic multireference...
-
Electronic transition dipole moment functions of the third singlet Sigma ungerade plus and third triplet Sigma gerade plus states of the Lithium dimer
Dane BadawczeElectronic transition dipole moment functions (ETDMF) of the third singlet Sigma ungerade plus (3sSu+) and third triplet Sigma gerade plus (3tSg+) states have been calculated for the Lithium dimer. ETDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. The results of the four ETDMFs...
-
Electronic transition dipole moment functions of the second singlet Pi gerade and second triplet Pi gerade states of the Lithium dimer
Dane BadawczeElectronic transition dipole moment functions (ETDMF) of the second singlet Pi gerade (2sPg) and second triplet Pi gerade (2tPg) states have been calculated for the Lithium dimer. ETDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. The results of the four ETDMFs have been obtained...
-
Electronic transition dipole moment functions of the fifth triplet Sigma ungerade plus state of the Lithium dimer
Dane BadawczeElectronic transition dipole moment functions (ETDMF) of the fifth triplet Sigma ungerade plus (5tSu+) state have been calculated for the Lithium dimer. ETDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. The results of the five ETDMFs have been obtained by the nonrelativistic multireference...
-
Electronic transition dipole moment functions of the first singlet Sigma gerade plus state of the Lithium dimer
Dane BadawczeElectronic transition dipole moment functions (ETDMF) of the first singlet Sigma gerade plus (1sSg+) state have been calculated for the Lithium dimer. ETDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. The results of the five ETDMFs have been obtained by the nonrelativistic multireference...
-
Electronic transition dipole moment functions of the first triplet Sigma ungerade plus state of the Lithium dimer
Dane BadawczeElectronic transition dipole moment functions (ETDMF) of the first triplet Sigma ungerade plus (1tSu+) state have been calculated for the Lithium dimer. ETDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. The results of the five ETDMFs have been obtained by the nonrelativistic multireference...
-
Nonlinear impedance of vanadate glasses containing BaTiO3
Dane BadawczeThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic annealed at 423 K was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic annealed at 423 K was measured by impedance spectroscopy method.
-
Non-linear impedance of V2O5 nanorods obtained at 923K
Dane BadawczeThe DataSet contains the non-linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of vanadate glass-ceramics containing BaTiO3
Dane BadawczeThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Nonlinear high temperature impedance of 35P2O5-30Fe2O3-35Nb2O5 glass
Dane BadawczeThe nonlinear high temperature impedance of iron- phosphate glasses doped with niobium oxide was measured. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH) and Nb2O5 (≥99.9%, PLUKA AG) were...
-
The magnetic field measurements in selected places of the industrial building
Dane BadawczeThe dataset is part of a comprehensive study on the assessment of the electromagnetic field intensity in a building of an operating industrial plant. Detailed results of magnetic field measurements, carried out in selected places of this building, are presented.
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Electric field maps of an astable multivibrator in frequency range from 30 MHz to 3 GHz
Dane BadawczeThe data presents a result of near field measurements of electromagnetic emissions radiated from the PCB of a small electronic device. An efficient method of modelling the magnetic and electric field emissions is the measurements in the near field using electric and magnetic probes. The attached files contain electric field maps created on based measurements...
-
Nonlinear high temperature impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 glass
Dane BadawczeThe nonlinear high temperature impedance of iron- phosphate glasses doped with niobium oxide was measured. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG)...
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.88 mm was measured at 693 K with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of temperature and frequency for Bi2VO5.5 ceramic of thickness 2.52 mm was measured at different A.C. voltage with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 1.63 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 1.63 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 813 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeNonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 813 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass heat-treated for 3 hours at 693 K, measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of partially crystallized 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 4.03 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 4.03 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.91 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.91 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of frequency for Bi2VO5.5 ceramic of thickness 2.88 mm was measured at high temperature range with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance of 5(2Bi2O3-V2O5)-95SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 5(2Bi2O3-V2O5)-95SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass heat-treated for 10 hours at 693 K, measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of partially crystallized 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage and temperature for Bi2VO5.5 ceramic of thickness 2.52 mm (after first heat-treatment at 913 K) was measured at different frequencies with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Simulation of ship spiral test for ballast and full load conditions
Dane BadawczeThe data show the results of the spiral test for the simplified ship model, taking into account two states of loading: ballast and full load. The data set contains the results of time simulation for sea state 10 on the Beaufort scale: changes in rudder angle delta_tab[deg]; angular velocity r_tab[deg/s]; surge velocity u_tab (m/s); sway velocity v_tab...
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured at high temperature range with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 613 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeNonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 613 K was measured by impedance spectroscopy method.
-
Instantaneous power signal measurements for bearing diagnostics
Dane BadawczeBearing diagnostics can be carried out based on the method, which relies on the measurement and analysis of the variability of the signal instantaneous power, defined as the product of instantaneous current and voltage power supplied to the engines. Bearing damage causes the appearance of deformations, which are in the form of additional harmonic components...
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(Bi2VO5.5)-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 annealed glass at 593 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 annealed glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of as-quenched 40Bi2VO5.5-60SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of as-quenched 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 30Bi2VO5.5-70SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 30Bi2VO5.5-70SrB4O7 glass was measured by impedance spectroscopy method.