Surface treatment of C80U steel by long CO2 laser pulses
PublikacjaThe paper presents the results of laser-melted C80U steel. The processed steel was placed between two permanent magnets and laser beam whose scanning velocity was 10 mm/s. CO2 laser beam was working in pulse mode. Pulses were generated at 100% of the average preset power of 700W, with 45 ms irradiation, zero interval between pulses and beginning of pulse repetition upon the achievement of the average laser power. During the operation,...
-
Application of guided wave propagation in diagnostics of steel bridge components
PublikacjaEarly detection of potential defects and identification of their location are necessary to ensure safe, reliable and long-term use of engineering structures. Non-destructive diagnostic tests based on guided wave propagation are becoming more popular because of the possibility to inspect large areas during a single measurement with a small number of sensors. The aim of this study is the application of guided wave propagation in...
-
Thermal Fatigue Influence of Laser Treated Tool Steel Surface
Publikacja -
Application of guided waves in the evaluation of steel-concrete adhesive connection
Publikacja -
The degradation mechanisms of a nanobainitic steel under cavitation erosion conditions
Publikacja -
Evaluation of recycled tyre steel fibres adhesion to cement matrix
Publikacja -
The Effectiveness of Polymer Damper in Damage Reduction of Temporary Steel Grandstand
PublikacjaA large number of accidents involving damage of temporary grandstands during different types of events were observed in the past. The aim of the paper is to analyse numerically the effectiveness of a polymer damper in damage reduction of a temporary steel scaffolding grandstand exposed to dynamic load due to jumping. The element has been installed as a diagonal one at the back part of the structure. The method has been compared...
-
Application of polymer element in reduction of temporary steel grandstand vibrations
PublikacjaThe numerical analysis focused on reduction of vibrations of a temporary steel scaffolding grandstand has been conducted in this paper. These types of structures are regularly subjected to dynamic loads which, in conjunction with light and quite slender structural members, may induce dangerous vibrations. To increase their safety, temporary steel grandstands are usually strengthened with the diagonal stiffeners of tubular cross...
-
The response of three colliding models of steel towers to seismic excitation
PublikacjaA number of past and recent observations have confirmed that collisions between adjacent, insufficiently-separated structures occurring as a result of seismic excitation (structural pounding) may result in serious damage to structural elements and can even lead to their total destruction. This paper summarises the results obtained from a shaking table experimental study which investigated structural pounding between three adjacent...
-
Hardened Steel Surface Waviness Created by Rolling Burnishing Process
PublikacjaThe surface of the finishing machined parts is defined mainly by roughness parameters. Growing demands on the part, especially mating sliding or rolling, require the specification of additional parameters, such as waviness parameters, particularly when there is significant resistance to seizing or noise reduction. This paper presents surface waviness characteristics of hardened burnished steel.
-
The Roughness of the Hardened Steel Surface Created by the Rolling-Burnishing Process
PublikacjaBurnishing hard materials can be used as an alternative finishing process. this paper presents the results of burnishing hardened steel. The article discusses surface deformation that occurs during this process and depends on the selected parameters of the geometric structure of the force applied for surface burnishing.
-
Deformations of the steel schell of a vertical cylindrical tank caused by underpressure
PublikacjaUnderpressure in a tank with a fixed roof may arise in the final stage of its construction as well as during its usage. This article presents stages of deformations of the tank shell and their development from the occurrence of the first deformation to either removal of the causes of underpressure or cracking of the steel shell.
-
Temper bead welding of S420G2+M steel in water environment
PublikacjaThe article presents the idea of the use of Temper Bead Welding (TBW) technique to improve the weldability of high strength steel at underwater wet welding conditions. Wet welding method with the use of covered electrodes is described. This work shows results of metallographic examinations and hardness measurements of samples of S420G2+M steel with weld beads performed under water. It has been shown that Temper Bead Welding technique...
-
Numerical modal analysis of a vertical rising steel water gate
PublikacjaVertical rising steel water gates are very common not only in Poland and Germany but also in other countries of the world. Their popularity is mainly attributed to their simplicity of construction, which makes their production process cheaper and faster when compared to other solutions. The aim of this paper is to conduct a numerical modal analysis to examine the eigenvalues and eigenmodes of a vertical rising steel gate. Two cases...
-
Launching of steel bridge girder. Application of nonlinear shell models
PublikacjaThe paper describes the final technology of launching the steel bridge superstructure. The original technology failed in the first construction stage. Local damage of steel webs caused by plastic buckling stopped the procedure. In the effect of damage a new consulting team was employed to solve the problem and redesign a technology of constructing. The key element of the new solution was developed with great help of non-linear...
-
Application of guided waves in the evaluation of steel-concrete adhesive connection
PublikacjaThe aim of the paper is the application of guided waves in the evaluation of a condition state of adhesive connection between steel and concrete. The study concerns a push-out specimen consisting of two steel plates glued to opposite faces of a concrete cube with the use of structural adhesive. Wave propagation in the specimen without external load is investigated both experimentally and numerically. The second stage of the investigation...
-
THE INTERACTION BETWEEN STEEL COLUMN CHORD AND CLOSELY SPACED REINFORCEMENT.
PublikacjaNowadays, more often than before, civil engineering designers are willing to use steel build-up members composed of single or doubled cold-formed chords interconnected using different mechanical connectors. This paper subject is an analysis of cooperation of a closely spaced built-up cold-formed chord interconnected with series of bolts that are located along the length of the member in a specific spacing. This distance along the...
-
Analysis of guided wave propagation in adhesive joints of steel rods
PublikacjaThe aim of the study is the elastic wave propagation in adhesive joints of metal rods that are one of the simplest kind of glue connections. They are consisted of two metal members and an adhesive layer joining two parts together. The analysis is directed to technical diagnostics of such type of connections. Longitudinal and transversal guided waves were excited in prepared joints. Signals of propagating waves were registered in...
-
Influence of pitting corrosion on strength of steel ships and offshore structures
PublikacjaPraca dotyczy wpływu korozji wżerowej na własności mechaniczne stali o zwykłej i podwyższonej wytrzymałości oraz na wytrzymałość stalowych konstrukcji przy obciążeniach statycznych i quasi- statycznych. Artykuł oparty jest głównie na japońskich publikacjach. W próbie rozciągania, korozja wżerowa obniża nieznacznie obciążenie odpowiadające granicy plastyczności Re(nieznacznie) i wytrzymałości na rozciąganie Rm (silniej, redukuje...
-
Experimental study on earthquake-induced pounding between steel structures
PublikacjaPounding between adjacent structures has been repeatedly observed during major earthquakes. The phenomenon may cause some local damage at the points of interactions, it may also lead to substantial destruction, permanent deformations or total collapse of colliding structures. The effects of earthquake-induced structural pounding have been studied for more than three decades now. However, most of the studies concerned masonry as...
-
Influence of Material Thickness on the Ductile Fracture of Steel Plates for Shipbuilding
PublikacjaIn the shipbuilding industry, the risk of brittle fractures is relatively high because some units operate in arctic or subarcticzones and use high thickness (up to 100 mm) steel plates in their structures. This risk is limited by employing certifiedmaterials with a specific impact strength, determined using the Charpy method (for a given design temperature) and byexercising control over the welding processes (technology qualification,...
-
Underwater wet welding of S1300 ultra-high strength steel
PublikacjaMarine Structures Volume 81, January 2022, 103120 Underwater wet welding of S1300 ultra-high strength steel Author links open overlay panelJacekTomkówGrzegorzRogalski https://doi.org/10.1016/j.marstruc.2021.103120 Get rights and content Under a Creative Commons licenseopen access Highlights • Technological method of S1300 steel underwater weldability improving was proposed. • Number of cracks and hardness of welded joints was...
-
Hydrogen delayed cracking of high-strength 14hnmbcu steel in seawater
PublikacjaOceniano podatność na niszczenie wodorowe stali o wysokiej wytrzymałości i jej połączeń spawanych przy stałym obciążeniu w wodzie morskiej. Badania przeprowadzono na próbkach okrągłych z karbem w środowisku wody morskiej przy potencjale korozyjnym oraz przy polaryzacji katodowej. Badano stal gatunku 14HNMBCu o minimalnej granicy plastyczności 690 MPa oraz jej połączenia spawane automatycznie łukiem krytym i ręcznie łukowo elektrodą...
-
Hydrogen degradation of the 26H2MF alloy steel in H2SO4 and hydrocarbon environments.
PublikacjaSTAL 26H2MF ZOSTALA PODDANA RÓZNEJ OBRÓBCE CIEPLNEJ, PO KTÓREJ UZYSKAŁA ONA RÓŻNĄ MIKROSTRUKTURĘ ORAZ CHARAKTER PRZEŁOMU. WYKONANO PRÓBY POWOLNEGO ODKSZTAŁCANIA W ROZCIEŃCZONYM KWASIE SIARKOWYM, PALIWIE CIĘZKIM I PRZEPRACOWANYM OLEJU SILNIKOWYM PRZEPRACOWANYM.
-
Assessment of structural changes in IN-519 cast steel reformer tubes.
PublikacjaPrzedstawiono zmiany struktury rur katalitycznych ze staliwa austenitycznego IN-519 po długotrwałej eksploatacji w reformerze metanu.
-
Stability analyses of a cylindrical steel silo with corrugated sheets and columns
PublikacjaW artykule przedstawiono wyniki obliczeń stateczności silosów z blachy falistej ze słupami. Wykonano analizy linowe i analizy nieliniowe stosując metody elementów skończonych. W obliczeniach uwzględniono model przestrzenny powłokowy oraz uproszczony model przestrzenny z blachy ortotropowej z belkami. Wyniki numeryczne porównano z Eurokodem.
-
Dissimilar underwater wet welding of HSLA steels
PublikacjaThe high-strength low-alloy S460ML and S460N steels were chosen for underwater wet welding of dissimilar T-joints using covered electrodes. For improving the quality of joints, the temper bead welding (TBW) method was used. The application of TBW in pad welding conditions has been investigated earlier but the possibility of usage of this technique in welded joints was not analyzed. The main aim of the study was to check the influence...
-
The home-made in situ passive flux sampler for the measurement of monoterpene emission flux: preliminary studies
PublikacjaThe paper presents the construction and metrological characteristics of the home-made in situ passive flux sampler, an analytical tool representing small-scale emission chambers working in situ and passively sampling analytes from the gaseous phase. The sorption element was a cylindrical container made of stainless steel net, packed with a carbon sorbent bed-graphitized charcoal, Carbograph 4 (35/50mesh). The recommended working/exposure...
-
Determination of pitting corrosion stage of stainless steel by galvanodynamic impedance spectroscopy
PublikacjaThis paper investigates the methodology for differentiation of multistep process of pitting corrosion of AISI 304 stainless steel in the environment of iron (III) chloride. Measurements were performed using Galvanodynamic Electrochemical Impedance Spectroscopy (GDEIS). Application of this methodology allowed monitoring of natural corrosion process without external current (IDC = 0A) nor potential perturbation of the system. Applied...
-
Modal analysis of a fish-belly flap type of steel water gate
PublikacjaABSTRACT: The results of a modal analysis of the fish-belly flap type of steel water gate are presented in the paper. The analysis was conducted for a detailed numerical model of the structure using four-node quadrilateral shell elements. The study was focused on the examination of the influence of positioning of the flap gate and hydrostatic pressure of water on the eigenvalues and eigenmodes of the structure. The results of the study...
-
MnCo2O4 deposited by spray pyrolysis as a protective layer for stainless steel interconects
PublikacjaStainless steel interconnects working in Solid Oxide Fuel Cells stacks are exposed to high temperature resulting in their corrosion. Protective layers for the hydrogen and oxygen sides are necessary to protect the interconnect material, prolongate the stack lifetime and maintain the output power. In this paper MnCo2O4 protective layer for the oxygen side of the interconnect is deposited by spray pyrolysis and is examined.
-
Modal analysis of temporary steel grandstand equipped with different bracing systems
PublikacjaThe aim of this paper is to present the results of numerical analysis focused on temporary steel scaffolding grandstand. The investigation has been devoted to modal analysis where modes of free vibrations and corresponding natural frequencies have been estimated and compared. The structure was equipped with different types of stiffener members. One on them is a typical tubular stiffener, while the second one is spe-cially designed...
-
Photocatalytic Decomposition of Air Pollutants using Electrodeposited Photocatalysts on Stainless Steel
PublikacjaThe aim of research was to develop an immobilization method for photocatalysts, which is an alternative to the sol-gel or dip coating methods and can be simply scaled up for technical applications. The investigated photocatalyst was TiO2, which was electrochemically deposited onto a cathode made of stainless steel. This deposited film was photocatalytically active. In order to enhance the photoactivity of the TiO2 film, commercially...
-
The Impact of Crushed Rock Spoil on Pitting Corrosion of Selected Stainless Steel
PublikacjaThe paper presents the results of the pitting resistance investigations of selected stainless steels in the chloride environment and the simultaneous impact of erosive factors using the cyclic polarization technique. Additionally, using electrochemical techniques, ie: electrochemical impedance spectroscopy (EIS) and measurement of corrosion potential, the behavior of the passive layer of selected stainless steels in the environment...
-
Comparative analysis of numerical models of arch-shaped steel sheet sections
Publikacja -
Experimental Verification of Natural Vibration Models of Steel-concrete Composite Beams
Publikacja -
Vibration of Steel–Concrete Composite Beams Using the Timoshenko Beam Model
Publikacja -
Effect of annealing temperature on slurry erosion resistance of ferritic X10CrAlSi18 steel
PublikacjaIn the present work, the slurry erosion tests were carried out to investigate the influence of heat treatment on slurry erosion process of ferritic X10CrAlSi18 stainless steel using a slurry pot test rig. X10CrAlSi18 stainless steel was tested in as-received condition and after annealing at three different temperatures: 600°C, 800°C and 1000°C. Degradation of materials due to slurry erosion depends on many factors connected with...
-
Influence of parameters of deep grinding on nanohardness and surface roughness of C45 steel
PublikacjaPrzedstawiono wyniki badań wpływu głębokości współbieżnego szlifowania powierzchni płaskich na chropowatość i nanotwardość warstwy wierzchniej stali C45 o strukturze ferrytyczno-perlitycznej i średniej wielkości ziarna 20 μm. Dla wszystkich wartości głębokości szlifowania uzyskano znaczny wzrost twardości warstwy wierzchniej przedmiotu obrabianego.
-
Identification i simulation of initial geometric imperfection of steel cylindrical tanks
PublikacjaPrzedstawiono stochastyczną analizę stalowych zbiorników walcowych ze wstępnymi imperfekcjami geometrycznymi. Wykorzystano pomierzone odchyłki rzeczywistych zbiorników. Imperfekcje opisano za pomocą nienorodnych pól losowych. Wygenerowano realizacje odpowiadające pomierzonym imperfekcjom a także imperfekcjom ekstremalnym. Wykonano obliczeniach geometrycznie i materiałowo nieliniowe zbiornika z imperfekcjami. Wykazano, że imperfekcje...
-
Cavitation erosion of X5CrNi18-10 austenitic stainless steel alloyed with TiC
PublikacjaPraca prezentuje zmianę odporności kawitacyjnej stali X5CrNi18-10 po laserowym stopowaniu jej warstwy wierzchniej węglikiem TiC. Laserowe stopowanie przeprowadzono dla 2 wariantów. W pierwszym przypadku stal stopowano do zawartości 1,55 TiC a w drugim do zawartości 3,97% TiC. Uzyskane rezultaty wskazują że przy zawartości 3,97 TiC nastopiło znaczące zwiększenie odporności na plastyczne odkszyałcenie warstwy wierzchniej pod wpływem...
-
Stress analysis in the steel tank shell at its connection with product pipeline
PublikacjaPrzeanalizowano zaburzenia stanu błonowego w powłoce zbiornika walcowego pionowego w strefie przyłączenia do płaszcza rurociągu produktowego
-
Multiaxial fatigue behaviour of maraging steel produced by selective laser melting
Publikacja -
Influence of sulphur on high temperature degradation of steel structures in the refinery industry
PublikacjaArtykuł stanowi przegląd skutków wpływu związków siarki, znajdujących się w mediach procesowych instalacji rafineryjnych, na elementy konstrukcji ze stali węglowych i stopowych. Wyróżniono dwa aspekty wysokotemperaturowej korozji siarkowej: związany z tworzeniem się zgorzeliny siarczkowej i ubytkami masy oraz dotyczący wewnętrznej degradacji elementu w wyniku zmian mikrostruktury stali. Przedstawiono tzw. zmodyfikowane krzywe McConomy...
-
Problems of strength modelling of steel sandwich panels under in-plate load
PublikacjaW pracy omówiono zagadnienia wytrzymałości statycznej stalowych paneli typu sandwich spawanych laserowo. Omówiono charakterystyki sztywności podczas zginania, przedstawiono zachowanie pod obciążeniem równomiernie rozłożonym a także sposób niszczenia pod obciążeniem ściskającym. Omówiono możliwości stosowania takich konstrukcji na podstawie wniosków z badań.
-
Hydrogen induced degradation of structural steel exposed to the technical liquid hydrocarbons
PublikacjaBadano degradacje stali 26H2MF w mieszaninach węglowodorów. Badania były prowadzone pod stałym obciążeniem i przy małej prędkości 10-6s-1
-
Interlayer defect evolution in an coating system on steel under hydromechanical loading
PublikacjaZaprezentowano wyniki pomiarów impedancyjnych obszaru międzywarstwowego w systemie powłokowym poddanym naprężeniom. Przedstawiono nowy sensor który jest zdolny do detekcji defektów w obszarze międzywarstwowym. Dwuwarstwowy system powłokowy przeznacziony do zastosowań morskich zbadano w celu określenia jego odporności na oddziaływanie cyklicznych naprężeń i zanurzeń w 3% roztworze NaCl.
-
Guided waves in steel rails - experimental works and wavelet signal processing
PublikacjaW artykule zaprezentowano analizę falkową pomierzonych eksperymentalnie fal sprężystych wzbudzanych w szynach kolejowych.
-
Evaluation of porous 430L stainless steel for SOFC operation at intermediate temperatures
PublikacjaW pracy przedstawiono badania porowatej stali nierdzewnej typu 430L do zastosowań w tlenkowych ogniwach paliwowych jako podłoża. Podłoża były poddawane utlenianiu w powietrzu oraz w wodorze i analizowane z wykorzystaniem mikroskopu elektronowego, dyfrakcji rentgenowskiej i termograwimetrii cyklicznej.
-
Response of a steel tank during earthquakes and mining tremors - experimental investigation
PublikacjaCylindrical steel tanks are very popular shell structures used to store the products of chemical and petroleum industries. Any failure might have disastrous consequences, therefore their safety and reliability is essential. Earthquakes are the most dangerous and also the most unpredictable dynamic loads acting on such structures. On the other hand, mining tremors are usually considered to be less severe due to lower acceleration...