Assessment of Tensile Strength Reserve of Asphalt Mixtures at Low Temperatures
PublikacjaDuring winter conditions, low-temperature cracks develop at the surface of the asphalt pavement when tensile thermal stress induced in the asphalt layer during cooling equals and exceeds the tensile strength of the material. The paper presents the results of tensile strength reserve assessment of asphalt mixtures with neat and SBS-polymer modified bitumen application. The tensile strength reservewas calculated as difference between...
-
Influence of Bitumen Type and Asphalt Mixture Composition on Low-Temperature Strength Properties According to Various Test Methods
PublikacjaIn regions with low-temperatures, action transverse cracks can appear in asphalt pavements as a result of thermal stresses that exceed the fracture strength of materials used in asphalt layers. To better understand thermal cracking phenomenon, strength properties of different asphalt mixtures were investigated. Four test methods were used to assess the influence of bitumen type and mixture composition on tensile strength properties...
-
Stress analysis of a strip under tension with a circular hole
PublikacjaThe paper addresses stress analysis of a strip with a circular hole under uniform uniaxial tension based oncircumferential stress expressionρπ. Stresses are analyzed in the infinite-length strips under tension with holes, the ratioof the hole radiusa to the strip half-widthb is either equal to:κ =a/b = 0.1 orκ = 0.5. Circumferential stresses aredetermined in selected cross-sections of the strip. The stress diagrams display local...
-
Examination of advanced isotropic constitutive laws under complex stress states in plain and reinforced concrete specimens
PublikacjaThe performance of advanced isotropic constitutive laws under complex stress states in plain and reinforced concrete specimens is investigated. Three different formulations are chosen: original Mazars model, Mazars mi model and model proposed by Pereira and coworkers. The degradation of the material in all formulations is described via a single variable, but a strain/stress state is taken into account via quite sophisticated relationships....
-
The experimental and numerical investigation of fracture behaviour in PMMA notched specimens under biaxial loading conditions – Tension with torsion
PublikacjaThis paper presents the results of experimental fracture test of flat PMMA specimens under biaxial loading condition tension with torsion (proportional). The specimens were made in two thicknesses: 5 and 15 mm and were weakened with V-type edge notches with different root radii: 0.5; 2 and 10 mm. Thanks to the ARAMIS 3D 4 M non-contact vision system, measurement of the elongation and twist angle were recorded. During experimental...
-
FEM simulations applied to the failure analysis of RC structure under the influence of municipal sewage pressure
PublikacjaThe paper discusses a failure mechanism of reinforced concrete (RC) structure with steel cover that failed under the influence of municipal sewage pressure. To explain the reasons of failure, in-situ measurements, laboratory experiments and comprehensive Finite Element Method (FEM) computations were performed. Non-destructive in-situ scanning tests were carried out to determine quantity and cover thickness of embedded reinforcement...
-
Petrophysical analyses of rock construction materials from the Roman rural settlement in Podšilo bay on Rab island (NE Adriatic, Croatia)
PublikacjaThis article presents the results of petrophysical analyses of limestones and sandstones used for the construction of the wall structures of a Roman rural settlement located in Podšilo Bay on Rab Island (Croatia). An on-site analysis of the walls indicated the use of different lithotypes, which is an uncommon case in the area. So far, no petrophysical properties of the applied materials have been tested, and their provenance...
-
Biomechanical causes for failure of the Physiomesh/Securestrap system
PublikacjaThis study investigates the mechanical behavior of the Physiomesh/Securestrap system, a hernia repair system used for IPOM procedures associated with high failure rates. The study involved conducting mechanical experiments and numerical simulations to investigate the mechanical behavior of the Physiomesh/Securestrap system under pressure load. Uniaxial tension tests were conducted to determine the elasticity modulus of the Physiomesh...
-
Modelling of concrete behaviour in uniaxial compression and tension with DEM.
PublikacjaW artykule omowiono wyniki modelowania betonu podczas jednoosiowego sciskania i rozciagania stosujac metode elementów dyskretnych. Beton zostal opisany jako material 3-fazowy (kruszywo, zaprawa cementowa i strefy kontaktu). Szczegolna uwage zwrocono na zjawiska mikro-strukturalne na poziomie kruszywa (lancuchy sil, wiry, obroty ziaren). Wyniki numeryczne zostaly porownano z wynikami badan doswiadczalnych.
-
Mechanical properties of the human stomach under uniaxial stress action
PublikacjaThe aim of this study was to estimate the range of mechanical properties of the human stomach in order to use the collected data in numerical modelling of surgical stapling during resections of the stomach. The biomedical tests were conducted in a self-developed tensile test machine. Twenty-two fresh human stomach specimens were used for the experimental study of its general strength. The specimens were obtained from morbidly obese...
-
Prediction of pile shaft capacity in tension based on some direct CPT methods – Vistula Marshland test site
PublikacjaThis paper presents different CPT methodologies for the prediction of the pile shaft resistance in tension on the example of three reference screw piles of the Jazowa test site in Poland. The shaft capacity was estimated based on the cone resistance, sleeve friction and CPT excess pore water pressure. Three piles with a diameter of 0.4 m and the length...
-
Prediction of Pile Shaft Capacity in Tension Based on Some Direct CPT Methods—Vistula Marshland Test Site
PublikacjaThis paper presents different CPT methodologies for the prediction of the pile shaft resistance in tension on the example of three reference screw piles of the Jazowa test site in Poland. The shaft capacity was estimated based on the cone resistance, sleeve friction and CPT excess pore water pressure. Three piles with diameter 0.4 m and the length varied from 8 m to 14.6 m were subjected to static load tests in tension. Their...
-
Metric entropy and digital image correlation in deformation dynamics analysis of fibre glass reinforced composite under uniaxial tension
Publikacja -
The elasto-plastic numerical study of crack initiation in notched PMMA specimens under uniaxial loading conditions – Tension and torsion
PublikacjaThis paper presents the results of FEM numerical calculations aimed at describing the plastic strain and stress fields under critical loading conditions: tensile force or torsional moment. The calculations were carried out with reference to the results of experimental tensile and torsional tests of flat PMMA specimens weakened with V-notches of different root radii: 0.5, 2 and 10 mm. The procedure for conducting nonlinear numerical...
-
NON-LINEAR MASTIC CHARACTERISTICS BASED ON THE MODIFIED MSCR (MULTIPLE STRESS CREEP RECOVERY) TEST
PublikacjaMastic containing asphalt in its composition is an example of a viscoelastic material. It is an effective binder in asphalt. It consists of a filler (<0.063 mm) and asphalt mixed in the right proportions. Just like in asphalt, its response depends on the temperature level, the load and stress time. Changing the stress stiffness of the mastic affects the non-linear course of the stress-strain relationship. Modelling of the non-linear...
-
OPTICAL STRAIN MEASUREMENT OF CONCRETE VERSUS MANUAL EXTENSOMETER MEASUREMENT BASED ON THE TEST RC DEEP BEAM IN A COMPLEX STATE OF STRESS
PublikacjaThe purpose of this study is to compare the strain measurement techniques of concrete in R-C element subjected to the monotonic load up to the failure. In the analysis manual extensometer methods of measurements and the optical system ARAMIS for non-contact three-dimensional measurements of deformation was used. The test sample was a cantilever deep beam loaded throughout the depth which was a part of the reinforced concrete deep...
-
Investigations of size effect in concrete at aggregate level - experiments and calculations results using discrete element method
PublikacjaSize effect is a fundamental phenomenon in concrete. It is characterised by decreasing strength and increasing brittleness of concrete with increasing size. The thesis includes experimental and theoretical elements. The main goal of the thesis were investigations of a size effect at the aggregate level by taking fracture into account with the discrete element method (DEM) for various failure modes. Comprehensive experiments on...
-
Parameters’ Identification of Perzyna and Chaboche Viscoplastic Models for Aluminum Alloy at Temperature of 120◦C
PublikacjaThe main purpose of this paper is the parameters identification of the Perzyna and the Chaboche models for the aluminum alloy at elevated temperature. The additional purpose is comparison of the results for these viscoplastic models. The results have been verified by the numerical simulation of the laboratory tests. The material parameters have been calculated on the basis of the uniaxial tension test. The determination of the...
-
Assessment of Thermal Stresses in Asphalt Mixtures at Low Temperatures Using the Tensile Creep Test and the Bending Beam Creep Test
PublikacjaThermal stresses are leading factors that influence low-temperature cracking behavior of asphalt pavements. During winter, when the temperature drops to significantly low values, tensile thermal stresses develop as a result of pavement contraction. Creep test methods can be suitable for the assessment of low-temperature properties of asphalt mixtures. To evaluate the influence of creep test methods on the obtained low-temperature...
-
Fracture prediction in flat PMMA notched specimens under tension - effectiveness of the equivalent material concept and fictitious material concept
PublikacjaThe fracture of notched elements under mode I loading (tension) remains an inexhaustible research topic, especially when it comes to the fracture of thermoplastic materials such as polymethylmethacrylate (PMMA), which experience considerable plastic strains under tension. The paper points out that traditional brittle fracture criteria such as mean stress (MS) or maximum tangential stress (MTS) criteria used to predict this phenomenon do...
-
The effect of preliminary creep-strain on material behavior under LCF tension/compression and pure torsion regimes
PublikacjaThis paper presents the results of experimental tests of monotonic tension and torsion, creep-rupture and preliminary creep at 200C and 300C, as well as low-cycle fatigue of 2024 T3511 aluminum alloy. The fatigue process was conducted at room temperature for uniaxial tension/compression and torsion. The as-received material and pre-deformed material were also investigated during creep at elevated temperature. Basic monotonic,...
-
Identification of Bodner-Partom Viscoplastic Model Parameters for Some Aluminum Alloys at Elevated Temperature
PublikacjaThe paper presents the identification process of inelastic (viscoplastic) properties for two aluminum alloys at a temperature of 120°C. The material parameters are calculated on the basis of uniaxial tension tests. Twelve tests at elevated temperature for each alloy have been performed—three tests for four different strain rates. The main purpose of the paper is to identify the Bodner-Partom viscoplastic model parameters for two...
-
CHARACTERIZATION STUDY ON MECHANICAL PROPERTIES OF POLYESTER COATED FABRIC
PublikacjaThe scope of the paper is to determine the mechanical properties of the Precontraint 1302 polyester coated fabric under uniaxial and biaxial tensile tests. The results are compared for Precontraint 1302 fabric and other types of coated fabrics. The author applied an orthotropic model and a dense net model to reflect the polyester coated fabric performance under uniaxial and biaxial tensile tests. Material parameters are specified...
-
Influence of Selected Warm Mix Asphalt Additives on Cracking Susceptibility of Asphalt Mixtures
PublikacjaWarm mix asphalt (WMA) has been widely accepted as a future asphalt paving technology. Besides clear advantages, there are still some concerns regarding durability and long-term performance of pavements made with this type of asphalt mixtures. One of the most important issues is low temperature behaviour of WMA because certain additives used for temperature reduction can aect bitumen properties. This paper presents the evaluation...
-
Mechanical Properties of Polyester Coated Fabric Subjected to Biaxial Loading
PublikacjaThe paper is focused on the comparison between uniaxial and biaxial laboratory test results for polyester coated fabric. A short literature review concerning coated woven fabrics with emphasis on biaxial tensile tests is presented. A description of the polyester-coated fabric under biaxial test by means of constitutive models and material parameter values is proposed. To establish the right values of the ultimate tensile strength,...
-
Hydrogen induced degradation of structural steel exposed to the technical liquid hydrocarbons
PublikacjaSusceptibility of the differently heat treated 26H2MF steel to stress corrosion cracking has been evaluated in the constant strain rate tension tests done at the strain rate 10-6s-1 and in the constant load tests done at the 0,98 of fracture load. The boiler fuel and the aged mineral oil at 135C and 80C respectively, have been used as the aggressive environments.
-
Experimental and theoretical study on high-temperature creep of VT6 titanium alloy under multi-axial loading conditions
PublikacjaIn the framework of damage mechanics, we discuss a new mathematical model that describes the kinetics of the stress–strain state and damage accumulation during material degradation by the mechanism of long-term strength under complex multiaxial stress state. An experimental and theoretical technique is proposed for determination of material parameters and scalar constitutive functions for damaged media based on specially set experiments...
-
Buckling and shape control of prestressable trusses using optimum number of actuators
PublikacjaThis paper describes a method to control the nodal displacement of prestressable truss structures within the desired domains. At the same time, the stress in all members is unleashed to take any value between the allowable tensile stress and critical buckling stress. The shape and stresses are controlled by actuating the most active members. The technique considers the members’ initial crookedness, residual stresses, and slenderness...
-
Numerical simulation of laminate composite specimens failure
PublikacjaThis work presents some numerical results concerning simulation of failure of laminate composite specimens. In the article two tests to determine ultimate strength in an orthotropic layer, are considered: tension (TT1) and compression (TC1) test. The outcome is compared with experimental data provided by [9,10].
-
A brief note on monotonic and fatigue fracture events investigation of thin-walled tubular austenitic steel specimens via fracture surface topography analysis (FRASTA)
PublikacjaThe main objective of this short communication is to show the fracture progression in each loading case and complement knowledge about fracture mechanisms underpinning the tensile and fatigue performance of thin-walled tubes. For this purpose, the fracture surface topography analysis (FRASTA) method was used in the thin-walled tubular austenitic stainless-steel specimens. Two cases were analyzed: monotonic tension, and uniaxial...
-
Multiaxial Fatigue Behaviour of SLM 18Ni300 Steel
PublikacjaFatigue behaviour of SLM 18Ni300 steel under proportional bending-torsion loading is studied. The fatigue tests are conducted under pulsating loading conditions using tubular specimens with a transversal circular hole. Three ratios of the normal stress to shear stress are considered, namely σ/τ=4,σ/τ=2 and σ/τ = 4/3. Crack initiation sites were found for two diametrically opposite points around the hole, whose locations are governed...
-
4-Point beam tensile test on a soft adhesive
PublikacjaAn adhesive butt joint with a soft bondline has been studied. A series of experiments was conducted on test pieces constituted of aluminium adherends bonded with a low modulus epoxy adhesive, ScotchWeld™ 2216. The joint was subjected to four point bending, in tension/compression loading, under constant deflection rate, with the bondline being parallel to the applied load. The objective was to examine and evaluate crack nucleation...
-
Effect of microstructure on mechanical properties and corrosion resistance of 2205 duplex stainless steel
PublikacjaThis paper presents results of the research on impact of microstructure of austenitic-ferritic steel of duplex type on its mechanical properties and susceptibility to stress corrosion cracking. As showed, improper processing technologies more and more often used in shipbuilding industry for plates and other half-finished products made of duplex steel may cause significant lowering their properties, which frequently makes their...
-
Corrigendum to “Fatigue life improvement using low transformation temperature weld material with measurement of residual stress” [Int. J. Fatigue 164 (2022) 107137]
PublikacjaWelding processes often produce high levels of tensile residual stress. Low transformation temperature (LTT) welding wires utilise phase transformation strains to overcome the thermal contraction of a cooling weld. In this paper, the residual stress within each weld was quantified using the milling/strain gauge method, being the strain change measured as the weldment was milled away. The fatigue tests were conducted under uniaxial...
-
Fatigue life improvement using low transformation temperature weld material with measurement of residual stress
PublikacjaWelding processes often produce high levels of tensile residual stress. Low transformation temperature (LTT) welding wires utilise phase transformation strains to overcome the thermal contraction of a cooling weld. In this paper, the residual stress within each weld was quantified using the milling/strain gauge method, being the strain change measured as the weldment was milled away. The fatigue tests were conducted under uniaxial...
-
Orientation effects on the fracture behaviour of additively manufactured stainless steel 316L subjected to high cyclic fatigue
PublikacjaIn this paper, stainless steel 316L (SS316L) bars were additively manufactured (AM) in three orientations (Z – vertical, XY – horizontal, ZX45 – midway between vertical and horizontal) by using the Laser Powder Bed Fusion Melting (LPBF-M) method. The AM specimens were subjected to load control fatigue testing under full tension and compression (R = -1) at stress amplitudes ±350, ±400 and ±450 MPa. The XY and ZX45 printing orientations...
-
Corrigendum to “An investigation on residual stress and fatigue life assessment of T-shape welded joints” [Eng. Fail. Anal. 141 (2022) 106685]
PublikacjaThis paper aims to quantitatively evaluate the residual stress and fatigue life of T-type welded joints with a multi-pass weld in different direction. The main research objectives of the experimental test were to test the residual stress by changing direction along with multiple wielding passes and determine the fatigue life of the welded joints. The result shows that compressive residual stress increases in the sample gradually...
-
An investigation on residual stress and fatigue life assessment of T-shape welded joints
PublikacjaThis paper aims to quantitatively evaluate the residual stress and fatigue life of T-type welded joints with a multi-pass weld in different direction. The main research objectives of the experimental test were to test the residual stress by changing direction along with multiple wielding passes and determine the fatigue life of the welded joints. The result shows that compressive residual stress increases in the sample gradually...
-
Comparison of calculated and measured thermal stresses in asphalt concrete
PublikacjaThe paper presents the comparison of calculated and measured thermal stresses induced in restrained asphalt concrete specimens by cooling. Thermal stresses were measured in the Thermal Stress Restrained Specimen Test. The calculations of thermal stresses were performed with the use of a theoretical formula based on the temperature dependent stiffness modulus. The novel approach applied in this paper was that the stiffness modulus...
-
Tensile modulus of human orbital wall bones cut in sagittal and coronal planes
PublikacjaIn the current research, 68 specimens of orbital superior and/or medial walls taken from 33 human cadavers (12 females, 21 males) were subjected to uniaxial tension untill fracture. The samples were cut in the coronal (38 specimens) and sagittal (30 specimens) planes of the orbital wall. Apparent density (ρapp), tensile Young’s modulus (E-modulus) and ultimate tensile strength (UTS) were identified. Innovative test protocols were...
-
Nonlinear material identification of heterogeneous isogeometric Kirchhoff–Love shells
PublikacjaThis work presents a Finite Element Model Updating inverse methodology for reconstructing heterogeneous materialdistributions based on an efficient isogeometric shell formulation. It uses nonlinear hyperelastic material models suitable fordescribing incompressible material behavior as well as initially curved shells. The material distribution is discretized by bilinearelements such that the nodal values...
-
Influence of laser processing of the low alloy medium carbon structural steel on the development of the fatigue crack
PublikacjaThe paper contains the results of the structural analysis, hardness tests and fatigue tests conducted for the medium carbon structural steel with low content of Cr and Ni after its processing with CO2 laser beam. Pre-cracks were made in the round compact tension (RCT) specimen used for fatigue test. Next, four paths, parallel to each other, were melted on both sides of the samples using a laser beam. The paths were perpendicular...
-
EXPERIMENTAL STUDY OF SURFACE ROUGHNESS EFFECT ONTHE RHEOLOGICAL BEHAVIOR OF MR FLUID
PublikacjaPaper presents the results of shear stress measurements of a commercial magnetorheological fluid using a plate-plate type geometry with a modified working surface. The purpose of the study was to determine the effect of changing the roughness of the measuring plate on the obtained shear stress results. Controlled shear rate tests and Magneto Sweep measurements were carried out for three MR fluid layer heights. The tests were...
-
Discrete element method simulations of fracture in concrete under uniaxial compression based on its real internal structure
PublikacjaThe paper describes experimental and numerical results of concrete fracture under quasi-static uniaxial compression. Experimental uniaxial compression tests were performed on concrete cubic specimens. Fracture in concrete was detected at the aggregate level by means of three non-destructive methods: three-dimensional X-ray microcomputed tomography, two-dimensional scanning electron microscope and manual two-dimensional digital...
-
Mechanical Properties of Human Stomach Tissue
PublikacjaThe dataset entitled Determination of mechanical properties of human stomach tissues subjected to uniaxial stretching contains: the length of the sample as a function of the corresponding load (tensile force) and the initial values of the average width and average thickness of the sample. All tests were conducted in a self-developed tensile test machine: PG TissueTester. The dataset allows the coefficients of various models of...
-
Shaft friction from the DMT and direct shear interface tests
PublikacjaThe article presents preliminary attempt to create tri-linear transfer curves for describing pile behaviour under axial loading. Transfer curves would use the parameter measured in dilatometer test, particularly a constrained modulus MDMT. The proposed method is based on concrete rough and smooth interface tests performed in a direct shear apparatus. Based on the obtained mobilization curves, relationships were created between...
-
Mechanical testing of technical woven fabrics
PublikacjaThis article presents a review of technical fabrics testing methods used by the authors on the basis of their experience with research on properties of polytetrefluoroethylene-coated fabrics used for Forest Opera in Sopot (Poland). First, the different types of testing methods used for description of mechanical properties (uniaxial tensile tests, biaxial tensile tests and shear tests) of technical woven fabrics are described. The...
-
OCENA NOŚNOŚCI STAREGO MOSTU ŁUKOWEGO W JAGODNIKU
PublikacjaArtykuł opisuje przeprowadzoną analizę statyczno-wytrzymałościowa 95-letniego betonowego mostu łukowego zlokalizowanego w Jagodniku w północnej Polsce. Trwałość i wytrzymałość starego betonu są określane na podstawie wybranych właściwości mechanicznych, fizycznych i chemicznych. Program badań laboratoryjnych składał się z następującego zestawu badań: pomiary głębokości strefy skarbonatyzowanej i gęstości w stanie suchym, badania...
-
Strength parameters of polyester reinforced PVC coated fabric after short term creep loading in biaxial mode
PublikacjaThis study addresses the analysis of tensile strength parameters of the technical fabric VALMEX, which is composed of two orthogonal polyester thread families (named the warp and fill) and both sides PVC coated. The material was firstly subjected to 48-hour biaxial creep loading with the equal stress level in both orthogonal directions of the fabric. The stress levels were established as follows: 4.6 kN/m, 10.4 kN/m, 16.4 kN/m,...
-
LCF behavior of 2024AA under uni- and biaxial loading taking into account creep pre-deformation
PublikacjaThis study presents the results of experimental low-cycle fatigue (LCF) tests of aluminum 2024 alloy T3511 temper in uni- and biaxial loading states. Tests were carried out on both the as-received material (hardened extruded rods) and material with different pre-deformation histories. These deformations were carried out in the creep process at 200 °C and 300 °C for two different levels of at each temperature. The pre-deformed material’s...