Wyniki wyszukiwania dla: UNIAXIAL TENSION STRESS TEST (UTST)
-
CrN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A25/#B21
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 9 min....
-
CrN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B22/#A23
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 6 min. The test...
-
SiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A33/#B34
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...
-
Influence of cooling rate and additives on low-temperature properties of asphalt mixtures in the TSRST
PublikacjaThe paper presents the results and analysis of low-temperature properties of asphalt mixtures according to Thermal Stress Restrained Specimen Test (TSRST) and Indirect Tensile Test methods. Different groups of bitumen were investigated: neat, SBS-modified and highly SBS-modified. Influence of cooling rates (1 C/h, 3 C/h, 5 C/h and 10 C/h) and additives (aramid fibres and crumb rubber) was identified as well. Moreover, for each...
-
CrN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B21/#A21
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 25 min....
-
TiN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A45/#A47
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 20 min. The test...
-
TiN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A45/#B45
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 90 min. The test...
-
Effects of deviations from thermo-rheologically simple behavior of asphalt mixes in creep on developing of master curves of their stiffness modulus
PublikacjaThe paper presents the deviations from the thermo-rheologically simple behavior of asphalt mixes and their effects on the developing of master curves of stiffness modulus. Eleven different mixes were tested in three point bending test under constant load at temperatures –20°C, –10 °C and 0 °C, and in some cases at +10 °C. The test method was developed at the Gdansk University of Technology, Poland. The applied stress level was...
-
Microstructure and Mechanical Properties of Carboxylated Nitrile Butadiene Rubber/Epoxy/XNBR-grafted Halloysite Nanotubes Nanocomposites
PublikacjaThe effect of various amounts of carboxylated nitrile butadiene rubber (XNBR) functionalized halloysite nanotubes (XHNTs) on the cure characteristics, mechanical and swelling behavior of XNBR/epoxy compounds was experimentally and theoretically investigated. The morphology of the prepared XNBR/epoxy/XHNTs nanocomposites was imaged using scanning electron microscopy (SEM). The effects of various XNBR-grafted nanotubes on the damping...
-
FEM ANALYSIS AND EXPERIMENTAL TESTS OF RIGID RISER HANGING SYSTEM
PublikacjaThe article presents the analysis, project, and experimental examination of an original rigid riser for Coil Tubing Pipes. The principle of riser operation is based on the use of friction forces. The research included the FEM analysis of the designed riser, calculations of the required bolt tensions, and checking the effect of the clamping force on stress distribution in the pipeline. The results of computer simulation were verified...
-
ADAPTATION OF ENGINEERING FEA-BASED ALGORITHMS TO LCF FAILURE AND MATERIAL DATA PREDICTION IN OFFSHORE DESIGN
PublikacjaThere is an ever growing industrial demand for quantitative assessment of fatigue endurance of critical structural details. Although FEA-based calculations have become a standard in engineering design, problems involving the Low-To-Medium cycle range (101-104) remain challenging. This paper presents an attempt to optimally choose material data, meshing density and other algorithm settings in the context of recent design of the...
-
Modelling hydraulic and capillary-driven two-phase fluid flow in unsaturated concretes at the meso-scale with a unique coupled DEM-CFD technique
PublikacjaThe goal of the research was to demonstrate the impact of thin porous interfacial transition zones (ITZs) between aggregates and cement matrix on fluid flow in unsaturated concrete caused by hydraulic/capillary pressure. To demonstrate this impact, a novel coupled approach to simulate the two-phase (water and moist air) flow of hydraulically and capillary-driven fluid in unsaturated concrete was developed. By merging the discrete...
-
Evaluation of Mechanical Properties of Two-Stage Concrete and Conventional Concrete Using Nondestructive Tests
PublikacjaDifferent types of concrete mixtures are used as building materials. The manufacturing process of two-stage concrete (TSC) differs from that of conventional concrete. This study investigated conventional mechanical properties derive empirical relations for estimation of the mechanical parameters of TSC and conventional concrete mixtures. TSC was used to prepare 216 specimens and conventional concrete was used to prepare 108 specimens...
-
Tensile validation tests with failure criteria comparison for various GFRP laminates
PublikacjaThe paper studies the mechanical properties of glass fibre reinforced polymers (GFRP) with various types and orientation of reinforcement. Analyzed specimens manufactured in the infusion process are made of polymer vinyl ester resin reinforced with glass fibres. Several samples were examined containing different plies and various fibres orientation [0, 90] or [+45, –45]. To assess the mechanical parameters of laminates, a series...
-
Size effect in concrete under splitting tension
PublikacjaThe size effect is a fundamental phenomenon in concrete materials. It denotes that both the nominal structural strength and material ductility always decrease with increasing element size under tension. In the paper splitting tensile tests on cylindrical concrete specimens with the different diameter were carried out. Two types of the loading strip (plywood board and steel cylinder) were used. The concrete strength and ductility...
-
The influence of stainless steels microstructure evolution on the mechanical properties of pressure installation elements
PublikacjaIn this paper results of FEM analysis performed for pipe and 90o elbow, made of super duplex stainless steel, after precipitation of sigma phase (),were presented. Heat treatment conditions simulate accidental overheating that can occur in nuclear installations after cooling circulation fails. For initial and modified microstructure tensile test was performed and numerical description of work hardening curves was done. Verification...
-
The influence of stainless steels microstructure evolution on the mechanical properties of pressure installation elements
PublikacjaIn this paper results of FEM analysis performed for pipe and 90o elbow, made of super duplex stainless steel, after precipitation of sigma phase (s), were presented. Heat treatment conditions simulate accidental overheating that can occur in nuclear installations after cooling circulation fails. For initial and modified microstructure tensile test was performed and numerical description of work hardening curves was done. Verification...
-
Theoretical examination of the fracture behavior of BC3 polycrystalline nanosheets: Effect of crack size and temperature
Publikacja2D carbon graphene nanostructures are elements of advanced materials and systems. This theoretical survey provides explanation to the mechanical and fracture behavior of mono- and polycrystalline BC3 nanosheets (denoted as MC- and PCBC3NS, respectively) as a function of temperature and the type of crack defects. The mechanical performance of PCBC3NS at elevated temperatures was monitored varying the number of grain boundaries (the...
-
Green strength (buildability performance) of concretes containing magnetite aggregate (M0-M100) mixes
Dane BadawczeRaw data for determination of buildability (green strength) properties of concrete mixes determined by squeezing test using QuantumX MX840B with CATMAN-EASY software, determined after 15, 30, 45 and 60 minutes. Values present force and two displacement measurements by LVDT.Additionally, an Origin (*.opju) file with processed data presenting stress-strain...
-
SiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B37/#A35
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
TiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A39/#B41
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
SiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A35/#B37
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
Numerical investigations of discrete crack propagation in Montevideo splitting test using cohesive elements and real concrete micro-structure
PublikacjaThe paper is aimed at accurately predicting the discrete fracture process in concrete specimens under complex stress states in two dimensional (2D) simulations. Plain concrete specimens subjected to Montevideo splitting test (MVD) were used for consideration due to non-negligible shear stresses impact in this type of test. In order to reflect the heterogeneous nature of the concrete, the meso-structure of the samples was included...
-
The effect of external load on ultrasonic wave attenuation in steel bars under bending stresses
PublikacjaThe stress state in deformed solids has a significant impact on the attenuation of an ultrasonic wave propagating through the medium. Measuring a signal with certain attenuation characteristics can therefore provide useful diagnostic information about the stress state in the structure. In this work, basic principles behind a novel attenuation-based diagnostic framework are introduced. An experimental study on steel bars under three-point...
-
EVALUATING THE INFLUENCE OF BENDING STRESS ON A 1H18N9 STEEL SHAFT WEAR PROCESS IN A WATER LUBRICATED SLIDING BEARING WITH A RUBBER BUSHING
PublikacjaThe issue of excessive wear of shaft journals co-working with a rubber bearing has been unexplained so far. Premature and sometimes very intensive wear of ship sliding bearings in water conditions is the reason for carry out very expensive and more frequent than expected repairs. The authors (E. Piątkowska, W. Litwin) made an attempt to find a case that influences the value of this wear described in the paper “Attempt at Evaluating...
-
Edgewise Compressive Behavior of Composite Structural Insulated Panels with Magnesium Oxide Board Facings
PublikacjaEdgewise compression response of a composite structural insulated panel (CSIP) with magnesium oxide board facings was investigated. The discussed CSIP is a novel multifunctional sandwich panel introduced to the housing industry as a part of the wall, floor, and roof assemblies. The study aims to propose a computational tool for reliable prediction of failure modes of CSIPs subjected to concentric and eccentric axial loads. An advanced...
-
Analysis of passenger car crash with a cable barrier installed with anti-glare screens on a horizontal convex road curve with 400 m radius
PublikacjaHigh-tension cable barriers have been used on roads for a relatively short period compared with other types of road barriers. Hence, there remains a need for further research on various crash scenarios. An important issue is the performance of a cable barrier on a road curve, particularly when a vehicle impacts the convex side of the barrier. To address this issue, the analysis in this study considers a system of anti-glare screens...
-
One Year Evaluation of Material Properties Changes of Polylactide Parts in Various Hydrolytic Degradation Conditions
PublikacjaBiodegradable biocompatible materials are widely used in medical applications. Determining the possibility of using biodegradable materials depends on determining the changes in their parameters over time due to degradation. The current scientific research on biodegradable materials has presented results based on research methods characterized by the different geometry and cross-section size of the specimen, type of degradation...
-
Process zone in the Single Cantilever Beam under transverse loading. - Part I: Theoretical analysis
PublikacjaSingle Cantilever Beam (SCB) specimen loaded with a transverse force parallel to the crack front is proposed for the analysis of crack propagation phenomena under mixed mode conditions. The stress redistribution in the adhesive layer in the vicinity of the crack front so as the beam deformation are estimated using a Timoshenko beam on elastic foundation model. This model emphasizes the Mode II contribution due to flexural beam...
-
Brain circuit imprints of developmental 17α-Ethinylestradiol exposure in guppies (Poecilia reticulata): Persistent effects on anxiety but not on reproductive behaviour
PublikacjaThe effects of endocrine disruptors may vary with the timing of exposure. The physiological implications of adult exposure are present during and shortly after exposure while embryonic exposure can imprint changes manifested in adulthood. In this study, guppy (Poecilia reticulata) embryos were exposed to 2 and 20 ng/L of 17α-ethinylestradiol during development via the mother and reared in clean water from gestation until 6 months...
-
Instrumented End Notched Flexure - Crack propagation and process zonemonitoring. Part I: Modelling and analysis
PublikacjaAnalysis of the three-point bending, End Notched Flexure (ENF), test is presented for exploitation with a new experimental methodology using the backface strain monitoring technique. The model consists oftwo Timoshenko beams joined with a two parameter elastic foundation, to evaluate stress and strain fields in both adherends and the adhesive layer, together with the specimen compliance and energyrelease rate. This model is compared...
-
Static load test on concrete pile – instrumentation and results interpretation
PublikacjaFor some time (since 8-10 years in Poland) a special static load tests on instrumented piles are carried out. Such studies are usually of a scientific nature and provide detailed quantitative data on the load transfer into the ground and characteristics of particular soil layers interaction with a pile shaft and pile base. Deep knowledge about the pile-subsoil interaction can be applied for a various design purposes, e.g. numerical...
-
Static Load Test on Instrumented Pile – Field Data and Numerical Simulations
PublikacjaFor some time (since 8-10 years in Poland) a special static load tests on instrumented piles are carried out. Such studies are usually of a scientific nature and provide detailed quantitative data on the load transfer into the ground and characteristics of particular soil layers interaction with a pile shaft and pile base. Deep knowledge about the pile-subsoil interaction can be applied for a various design purposes, e.g. numerical...
-
FEM modelling of screw displacement pile interaction with subsoil
PublikacjaPredicting the-settlement characteristics of piles is an important element in the designing of pile foundations. The most reliable method in evaluating pile-soil interaction is the static load test, preferably performed with instrumentation for measuring shaft and pile base resistances. This, however, is a mostly post-implementation test. In the design phase, prediction methods are needed, in which numerical simulations play an...
-
Fracture in Asymmetric Bonded Joints
PublikacjaAdhesion was studied in asymmetric bonded joints using fracture mechanics tests. The asymmetric bonded joints consist of two different type and/or thickness materials bonded by an adhesive. Mentions of asymmetric bonded joint tests employed so far are rare in the literature. They are imperfect and therefore are not standardized. Accordingly three new tests were introduced in this work to study bonded joints. The new metrological...
-
Screw displacement pile shaft deformations measured by vibrating wire and fiber optic systems during a static load test
PublikacjaThis paper describes a full scale static load test performed on a 400 mm diameter screw displacement pile equipped with four different strain measuring systems. Three types of vibrating wire strain gauges (VWSG) were used: global - retrievable, local attached to steel pipe and local concrete embedded. The fourth system was distributed fiber optic sensors based on Rayleigh back scattering (DFOS) - three in the pile cross section....
-
EXPERIMENTAL EVALUATION OF DLC/STEEL SLIDING CONTACTS’ OPERATIONAL ENVELOPE
PublikacjaIn an industrial project concerning sliding bearings, a sliding pair was selected of high alloy steel vs. industrial grade DLC coated high alloy steel as a basis for an innovative design of high performance sliding bearings lubricated with a synthetic oil for use in geared transmission units. The development process required credible data on the ultimate resistance of the sliding pair to very high contact stress. An experimental...
-
Remarks on the Subject of Back-Up Protection of Residual Current Devices
PublikacjaResidual current devices without integral overcurrent protection (RCCBs) are back-up protected by fuses or miniature circuit-breakers (MCBs). If the latter are used, special attention must be given to the coordination between an RCCB and an MCB. This paper indicates probable cases of the aforementioned devices coordination, in which back-up protection of the RCCB is not adequate. A laboratory test has shown that depending on the...
-
Opracowanie procedury i badania wytrzymałościowe połączeń spawanych pomiędzy rurą kwadratowa a elementami giętymi na zimno ze stali S355 oraz testowanie połączeń o grubości 4, 6, 8mm typu S355
PublikacjaCelem pracy było: - opracowanie procedury badania wytrzymałości połączeń spawanych rozciąganych w kierunku prostopadłym i w kierunku równoległym (ścinanych) do osi spoiny. Spoiny te łączyły elementy rur kwadratowych o różnej grubości z elementami w kształcie ceownika giętymi na zimno. - wykonanie próbek do badań wytrzymałościowych wyciętych z elementów spawanych dostarczonych przez Zakład Produkcyjny firmy Borga obciążonych prostopadle...
-
DLC coating in ring-on-ring sliding with water lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was augmented by vibration...
-
DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
DLC coating in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was augmented by vibration...
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
Wyznaczanie współczynnika przejmowania ciepła podczas wrzenia w przepływie dwutlenku węgla (Prediction of flow boling heat transfer coefficient for carbon dioxide in minichannels)
PublikacjaW pracy przedstawiono wyniki obliczeń uzyskane za pomocą własnego modelu półemirycznego dla wybranych danych eksperymentalnych dla wrzenia w przepływie dwutlenku węgla. Metoda obliczeniowa została zweryfikowana z danymi eksperymentalnymi Docoulombiera i innych (2011) oraz Mastrullo i innych (2009). Badania eksperymentalne dotyczą pełnego zakresu zmienności stopnia suchości oraz zakresu prędkości masowej G=200-1200 kg/m2s. rozwijany...
-
Problems of analytical determination of journal bearing bush fatigue strength estimates
PublikacjaProblems connected with determination of stress distribution in sliding layer of thinwalled bearing bushes, investigated in bearing fatigue test rigs, have been presented. Using an example of plain bearings tested in the fatigue machine SMOK (built at the Gdask University of Technology) problems with obtaining a convergence of iterative procedure for determining the fatigue strength estimators of bearing alloy surface layer are...
-
Development and validation of lumbar spine finite element model
PublikacjaThe functional biomechanics of the lumbar spine have been better understood by finite element method (FEM) simulations. However, there are still areas where the behavior of soft tissues can be better modeled or described in a different way. The purpose of this research is to develop and validate a lumbar spine section intended for biomechanical research. A FE model of the 50th percentile adult male (AM) Total Human Model for Safety...
-
The fracture behaviour of notched PMMA specimens under simple loading conditions – Tension and torsion experimental tests
PublikacjaThis paper presents the results of experimental testing of flat PMMA specimens during uniaxial loading conditions. Two separate tests were conducted: tensile and torsion. The specimens were weakened with V-type edge notches with different root radii: 0.5; 2 and 10 mm. The specimens were made in two thickness variants: 5 and 15 mm. Monotonic tensile and torsion tests were carried out while keeping the averaged strain rate constant,...
-
DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....