Operational causes of fatigue failures within the passages of gas turbine engines
PublikacjaThe short profile of a fatigue wear process of gas turbine engine's constructional elements has been introduced in the article. The primary causes of a fatigue cracks formation within the mechanical system as well as within the passages of the engine have been showed. Especial attention was devoted to the low-cycle fatigue, what is associated with unsteady thermal-flow processes being worked out in the passages.The selected damages...
-
Problems of analytical determination of journal bearing bush fatigue strength estimates
PublikacjaProblems connected with determination of stress distribution in sliding layer of thinwalled bearing bushes, investigated in bearing fatigue test rigs, have been presented. Using an example of plain bearings tested in the fatigue machine SMOK (built at the Gdask University of Technology) problems with obtaining a convergence of iterative procedure for determining the fatigue strength estimators of bearing alloy surface layer are...
-
The Possibilities of Improving the Fatigue Durabilityof the Ship Propeller Shaft by Burnishing Process
PublikacjaHeavily loaded structural elements operating in a corrosive environment are usuallyquickly destroyed. An example of such an element is a ship propeller operating in a seawaterenvironment. This research presents a fatigue resistance test performed on elements operating inseawater. Different processing parameters applied on the samples in particular were compared withthe specimens whose surface had been burnished differently and...
-
Fatigue fracture morphology of AISI H13 steel obtained by additive manufacturing
PublikacjaThe paper focuses on researching the effect of fatigue loading on metallic structure, lifetime, and fracture surface topographies in AISI H13 steel specimens obtained by selective laser melting (SLM). The topography of the fracture surfaces was measured over their entire area, according to the entire total area method, with an optical three-dimensional surface measurement system. The fatigue results of the SLM 3D printed steel...
-
Assessment of fatigue damage of organic coatings subjected to cyclic mechanical stress
PublikacjaTechnika szumu elektrochemicznego od ponad 20 lat stanowi przedmiot intensywnych badań mających na celu jej praktyczne zastosowanie w monitorowaniu korozji. U podstaw omawianej metody leży odpowiednia analiza rejestrowanych symultanicznie przebiegów prądowych i potencjałowych. W zależności od użytej techniki obróbki danych uzyskane mogą być informacje dotyczące ilościowych (szybkość) i jakościowych (rodzaj zaatakowania) cech procesu...
-
Exercise-induced fatigue impairs visuomotor adaptability in physical education students
Publikacja -
Multiaxial fatigue behaviour of maraging steel produced by selective laser melting
Publikacja -
Course of fatigue among patients previously hospitalised due to COVID-19
Publikacja -
Fatigue after COVID‐19 in non‐hospitalized patients according to sex
Publikacja -
An investigation on residual stress and fatigue life assessment of T-shape welded joints
PublikacjaThis paper aims to quantitatively evaluate the residual stress and fatigue life of T-type welded joints with a multi-pass weld in different direction. The main research objectives of the experimental test were to test the residual stress by changing direction along with multiple wielding passes and determine the fatigue life of the welded joints. The result shows that compressive residual stress increases in the sample gradually...
-
The conception of energetic investigations of the multisymptom fatigue of the simple mechanical systems' constructional materials
PublikacjaThe article presents the basic assumptions of the research project aimed, as the main scientific purpose, an identification of the slow-changeable energy processes surrounding the high-cycle fatigue of constructional materials within the plain mechanical system, especially the marine one, for diagnostic purposes. There is foreseen an application of alternative diagnostic methods based on energetic observations of the multi-symptom,...
-
Spectral criterion of infinite fatigue life of beams under asymmetric random loads
PublikacjaRozpatrywana jest trwałość zmęczeniowa belek poddanych stałym i zmiennym obciążeniom osiowym, giętnym i skrętnym o znanych gęstościach widmowych mocy. Założono, że materiał posiada granicę zmęczenia i jest zgodny z modelem Kelvina-Voigta, oraz że składowe naprężenia są stacjonarne, stacjonarnie skorelowane i różniczkowalne w sensie średniokwadratowym. Zdefiniowano naprężenie równoważne i sformułowano kryterium nieograniczonej trwałości...
-
Spectral criterion of infinite fatigue life of beams under combined random loads
PublikacjaRozpatrywana jest trwałość zmęczeniowa belek poddanych zmiennym obciążeniom osiowym, giętnym i skrętnym o znanych gęstościach widmowych mocy i zerowych wartościach średnich. Założono, że materiał posiada granicę zmęczenia i jest zgodny z modelem Kelvina-Voigta, oraz że składowe naprężenia są stacjonarne, stacjonarnie skorelowane i różniczkowalne w sensie średniokwadratowym. Zdefiniowano naprężenie równoważne i sformułowano kryterium...
-
Effects of loading pattern and lubricant pressure influence on bearing alloy fatigue characteristics
PublikacjaOpisano wyniki testów zmęczeniowych przeprowadzonych dla stopu łożyskowego AlSn (11,3 Cu 1,2) osadzonego na taśmie stalowej. Doświadczalnie określono wartości obciążeń niszczących dla różnych warunków obciążenia: dla obciążeń zginających wahadłowych, dla obciążeń zginających wahadłowych przy równoczesnym działaniu słabego lub zmiennego ciśnienia w komorze olejowej.
-
Fatigue resistance investigation of the mb46 plain bearings under conditions of dynamic loadings
PublikacjaOdporność materiału łożyskowego MB46 na pęknięcia zmęczeniowe badano na stanowisku SMOK, w którym generowane jest zmienne jednokierunkowe obciążenie badanego łożyska. Materiał łożyskowy MB46 składa sie z warstwy brązu CuPb22Sn 3 spiekanego na taśmie stalowej, stanowiącej podłoże. Na warstwę brązu nałożona jest galwanicznie cienka warstwa stopu SnCu6 stanowiąca powłokę. Każde z badanych łożysk poddawane było 20-godzinnemu testowi...
-
Acoustic Emission Monitoring of Structural Elements of a Ship for Detection of Fatigue and Corrosion Damages
PublikacjaUszkodzenia korozyjne i pęknięcia zmęczeniowe są głównymi przyczynami defektów strukturalnych we wszystkich środkach transportu takich jak statki, cysterny drogowe i kolejowe. Oba typy degradacji tzn. degradacja materiału i konstrukcji są przedmiotem badań przeprowadzanych w projekcie badawczym VII Programu Ramowego Unii Europejskiej o nazwie ''Monitorowanie efektywnych kosztów korozji i zmęczenia w środkach transportu'' (akronim...
-
The crack surface morphology investigation of S355J2 steel after bending-torsion fatigue
Publikacja -
Higher luteal progesterone is associated with low levels of premenstrual aggressive behavior and fatigue
Publikacja -
Safe Operation of Underground Mining Vehicles Based on Cyclic Fatigue Monitoring of Powertrains
Publikacja -
Spectral criterion for high-cycle fatigue of engine parts under asymmetricrandom load
PublikacjaPrzedstawiono kryterium ograniczonej trwałości zmęczeniowej wysokocyklowej części silników poddanych stacjonarnemu obciążeniu stochastycznemu o niezerowej wartości średniej. Wyznaczono naprężenie równoważne w postaci procesu okresowego w sensie średnio kwadratowym i zastosowano równanie Goodmana/So-derberga. Ukazano wpływ rozciągającego naprężenia resztowego na wartość oczekiwaną czasu do chwili uszkodzenia zmęczeniowego.
-
Spectral criterion for high-cycle fatigue of metals under multiaxial random loading
PublikacjaPrzedstawiono kryterium projektowe elementów z metali ciągliwych, poddanych w zakresie wytrzymałości zmęczeniowej wysokocyklowej wieloosiowemu naprężeniu o zerowej wartości średniej. Jest ono oparte na równaniu krzywej Whleradla symetrycznego rozciągania-ściskania i gęstościach widmowych mocy składowych naprężenia. W tym celu wyznaczono równoważne naprężenie w dziedzinie częstości przy założeniu, że składowe rzeczywistego naprężenia...
-
Laser Beam as a Precision Tool to Increase Fatigue Resistance in an Eyelet of Undercarriage Drag Strut
PublikacjaThe article contains the results of tests on a laser-processed eyelet of undercarriage drag strut to increase its fatigue strength. Laser processing concentrated on both sides around the hole of eye for connecting the undercarriage drag strut caused that the material in this area withstood more than twice the number of load cycles established for this material. In order to determine the reasons for the increase in fatigue strength,...
-
Consideration of Pseudo Strain Energy in Determination of Fatigue Life and Microdamage Healing of Asphalt Mastics
PublikacjaRest periods between cyclic loads can lead to recovery of damage and extension of fatigue life. This phenomenon is referred to as healing. Healing is clearly observed in bituminous materials, such as asphalt mastics, which belong to the components of asphalt mixtures. Due to the nature of road pavement traffic loading, which is characterized by series of intermittent pulses with rest periods, consideration of healing is necessary...
-
Quasistatic and fatigue behavior of an AISI H13 steel obtained by additive manufacturing and conventional method
PublikacjaThis work aims to compare the mechanical behavior of an AISI H13 steel obtained by additive manufacturing with that obtained by conventional manufacturing methods. The average values of the ultimate tensile strength (UTS) and ductility obtained for the specimens produced by the conventional method were equal to 658 MPa and 18%, respectively, which compares with 503 MPa and 0.75% registered for the selective laser melting (SLM)...
-
Effect of bending-torsion on fracture and fatigue life for 18Ni300 steel specimens produced by SLM
PublikacjaIn this study, different fracture surfaces caused by fatigue failure were generated from 18Ni300 steel produced by selective laser melting (SLM). Hollow round bars with a transverse hole were tested under bending-torsion to investigate the crack initiation mechanisms and fatigue life. Next, the post-failure fracture surfaces were examined by optical profilometer and scanning electron microscope. The focus is placed on the relationship...
-
Application a laboratory stand for multi-symptoms tests for high cyclic fatigue of constructional material
PublikacjaThis paper describes a need of diagnostics present ship plants according to current technical state. In order to reach competent physical quantity describing fatigue of materials by congregated energy. This paper describes using some diagnostics methods (acoustic emission AE, vibration, thermovision, deformation) in order to definition fatigue state of construction material. The author tries to find correlation between measured...
-
Application of acoustic emission for detection of fatigue microdemage in main and crank bearings for diesel engines
PublikacjaThe article presents reasons for applying the acoustic emission (AE) to detect fatigue microdamage in main bearings and crank bearings of ship main engines. Problem of determination of the fatigue life for slide bearing bushes was characterized in general. There were demonstrated properties of the objects of research, which were bushings made of the MB58 alloy, as well as an overall description of the research. It was shown that...
-
Laboratory fatigue assessment of large geocomposite-reinforced double-layered asphalt concrete beams
PublikacjaGeosynthetic reinforcement of asphalt layers has been used for several decades. Evaluation of the influence of these materials on pavement fatigue life is still ongoing, especially for new types of geocomposites. This paper presents the evaluation of fatigue performance of large asphalt concrete beams reinforced with a new type of composite in which square or hexagonal polypropylene stiff monolithic paving grid with integral junctions...
-
Laboratory fatigue assessment of large geocomposite-reinforced double-layered asphalt concrete beams
PublikacjaGeosynthetic reinforcement of asphalt layers has been used for several decades. Evaluation of the influence of these materials on pavement fatigue life is still ongoing, especially for new types of geocomposites. This paper presents the evaluation of fatigue performance of large asphalt concrete beams reinforced with a new type of composite in which square or hexagonal polypropylene stiff monolithic paving grid with integral junctions...
-
Fracture surface formation of notched 2017A-T4 aluminium alloy under bending fatigue
PublikacjaThe effect of cyclic loading on facture surface topology in notched components made by aluminium alloys is not completely clear. Fractogra-phy and fracture mechanics can help to understand this interdependency. This paper aims to study the distribution of the fracture surface roughness of notched 2017A-T4 aluminium alloy after bending fatigue using an optical focus-variation surface measurement technique by applying the fracture...
-
Influence of Heat Treatment Temperature on Fatigue Toughness in Medium-Carbon High-Strength Steels
PublikacjaCurrent research has demonstrated that the tempering temperature affects the martensitic transformation of medium-carbon high-strength steels. This temperature plays an important role in the final microstructure, percentage ratios of martensite to ferrite phases and, consequently, in the mechanical properties and the fatigue response. So far, the relationship between the martensitic tempering temperature and the cyclic deformation...
-
Fatigue Performance of Double-Layered Asphalt Concrete Beams Reinforced with New Type of Geocomposites
PublikacjaThe reinforcement of asphalt layers with geosynthetics has been used for several decades, but proper evaluation of the influence of these materials on pavement fatigue life is still a challenging task. The presented study investigates a novel approach to the reinforcement of asphalt layers using a new type of geogrid composite, in which square or hexagonal polypropylene stiff monolithic paving grid with integral junctions is bonded...
-
Prediction of the fatigue lifetime of PUR structural elements using a combined experimental-numerical approach
PublikacjaThis paper presents a method for estimating the fatigue life of polyurethane elastomeric components. A rubber replacement - polyurethane of hardness 80ShA commonly used in vibration damping systems, for example, in motor vehicle suspensions, was used for the study. A metal-rubber bushing component was selected for analysis, and numerical analysis was carried out along with a fatigue model proposal based on a modification of the...
-
Fracture surface topography investigation and fatigue life assessment of notched austenitic steel specimens
PublikacjaThe objectives of this study were to investigate the fracture surface topography of X8CrNiS18-9 austenitic stainless-steel specimens for different loadings and notch radii and to supplement the knowledge about the fracture mechanisms for fatigue performance. Cases with three different values of the notch radius ρ and the stress amplitude σa were analysed. The fracture topographies were quantified by the areas over their entire...
-
The energy approach to fatigue crack growth of S355 steel welded specimens subjected to bending
PublikacjaThe study presents the results of the research on the rate of fatigue crack growth subjected to bending in the ferritic-pearlitic structure. The studies were carried out at a constant amplitude of the moment and at various values of the load ratios R and at the operating frequency of the machine of 28.4 Hz. Flat specimens made of S355 steel and with fillet welds and with double-sided blunt external notches as well as concave...
-
Quasistatic and fatigue behavior of an AISI H13 steel obtained by additive manufacturing and conventional method
Publikacja -
Three-Dimensional Fractography for Conventional and Additive Manufactured Steels After Bending-Torsion Fatigue
PublikacjaIn this study, fracture surface topography parameters were measured to investigate the effects of multiaxial loading. In order to assess the metrological aspects of fracture for notched specimens made of high-strength steels processed by both conventional and additively manufacturing (AM) techniques, an optical surface profilometer was used. Three bending moment to torsion moment ratios (B/T) were studied, i.e. 2, 1 and 2/3. The...
-
Effect of pavement roughness and vehicle dynamic loads on decrease of fatigue life of flexible pavements
PublikacjaDue to the fact that pavement surfaces are not ideally even, dynamic loads of vehicle axles deviate from static loads. Higher dynamic loads contribute to faster pavement distress. The distribution of dynamic loads is similar to normal distribution and can be described by static load and factors DI (dynamic impact) and DLC (dynamic load coefficient). With the deterioration of pavement condition its evenness decreases as well and...
-
Spectral criterion for high-cycle fatigue of anisotropic metals under multiaxial random loads
PublikacjaPraca dotyczy oceny ograniczonej trwałości zmęczeniowej metali ciągliwych, poddanych wieloosiowym obciążeniom statycznym i dynamicznym. Zakłada się, że kartezjańskie składowe tensora naprężenia są sumą losowych wartości średnich o znanych drugich momentach statystycznych i stacjonarnych procesów stochastycznych o znanych gęstościach widmowych mocy. Przyjmując, że procesy te są stacjonarnie skorelowane, różniczkowalne w sensie średnio-kwadratowym...
-
Prediction of corrosion fatigue crack propagation life for welded joints under cathodic potentials
PublikacjaPrzy ochronie katodowej poniżej potencjału optymalnego obserwuje się przyspieszenie propagacji pęknięcia korozyjno-zmęczeniowego w porównaniu do konstrukcji nie chronionej. Zaproponowano własną formułę empiryczną na wpływ potencjału ochronnego na prędkość propagacji pęknięcia oraz własny wzór na [delta]K w złączu pachwinowym. Wyprowadzono wzór na krzywą ''S-Np'' (naprężenie - długość okresu propagacji pęknięcia). Zaprezentowana...
-
Comparative study with magnetic techniques of P91 and 13HMF steels properties subjected to fatigue tests
PublikacjaWykonano badania porównawcze technikami magnetycznymi właściwości stali P91 i 13HMF poddanych testowi zmęczenia
-
Polymer‐silica additive as a modifier of tribological properties of ecological grease, improvement of fatigue resistance
Publikacja -
Multiaxial fatigue life assessment in notched components based on the effective strain energy density
Publikacja -
The Control System Based on FPGA Technology For Fatigue Test Stand MZGS-100 PL
Publikacja -
Surface topography analysis based on fatigue fractures obtained with bending of the 2017A-T4 alloy
Publikacja -
THE INFLUENCE OF DIFFERENT VEGETABLE DISPERSION PHASES ON THE ROLLING CONTACT FATIGUE OF BIODEGRADABLE LUBRICATING GREASES
Publikacja -
Equivalent axle load factors for design of rigid pavements derived from fatigue criteria
PublikacjaArtykuł przedstawia określenie współczynników równoważności osi dla nawierzchni sztywnych na podstawie kryteriów zmęczeniowych stosowanych w mechanistyczno-empirycznej metodzie projektowania nawierzchni drogowych. Przedstawiono kryteria zmęczeniowe z wybranych metod projektowania i analizy nawierzchni sztywnych. Kryteria te zostały użyte do wyprowadzenia wzorów do obliczania współczynników równoważności obciążenia osi. Stwierdzono,...
-
Effect of Aluminizing on the Fatigue and High-Temperature Corrosion Resistance of Inconel 740 Nickel Alloy
Publikacja -
The Influence of Laser Surface Alloying on the Thermal Fatigue Resistance of Hot Work Tool Steels
Publikacja -
Hydrogen-enhanced stress corrosion cracking and corrosion fatigue of HSLA steels in sea-water
PublikacjaPrzedstawiono ocenę podatności stali o wysokiej wytrzymałości na naprężeniowe pękanie korozyjne i zmęczenie korozyjne wspomagane przez wodór. Wykonano próby powolnego rozciągania i zmęczenia niskoczęstotliwościowego na stalach 17HMBVA i 14HNMBCu oraz ich złączach spawanych, w środowisku wody morskiej, przy polaryzacji katodowej. Zamieszczono wyniki badań elektrochemicznych oraz przełomów na skaningowym mikroskopie elektronowym.