Influence of reduction process on the structural and mechanical properties of (Pb,Bi)-(Si,Ge)-O oxide glasses
PublikacjaThe effect of the reduction process in H2 at 380 °C on the microstructure and elemental composition of a glass Bi0.4Pb0.2Si0.4Ox has been investigated. It has been shown that after reduction a clearly separated top layer with a thickness of approx. 50 µm was formed on the surface of the sample. This layer is depleted of oxygen and has higher electrical conductivity than the interior of the glass. It has also been found that some...
-
Determination of Failure Causes of a Steam Turbine Casing
PublikacjaThe paper presents results of research and failure analysis undertaken to determine failure causes of a steam turbine casing. After 130,000 hours of service the crack in a outer shell of the turbine casing was found. The inner shell of the casing was made of cast steel grade G21CrMoV5-7, and the outer shell of grade G20CrMo4-5. Following research were performed in order to determine causes of the casing failure: chemical analysis;...
-
Underwater Welding of Duplex Stainless Steel
PublikacjaThe present work was conducted to assess the weldability of duplex stainless steel at underwater conditions. Interest of underwater welding of this steel grade is connected with necessity of preparing welding repair technologies for subsea pipelines widely used in offshore oil and gas industry. The GMA local cavity welding method was used in the investigations. Welded beads were performed underwater at 0.5 m depth and in the air....
-
An adaptive approach to non-destructive evaluation (NDE) of cast irons containing precipitated graphite particles with the help of magnetoacoustic emission
PublikacjaPhysical properties of cast irons strongly depend on both their microstructure and the presence of casting defects. The paper analyses the possibility of application of magnetoacoustic emission (MAE) for nondestructive detection of flawed cast iron components. The investigated samples containing dross, chunky graphite and lamellar graphite were compared with the reference, flawless, spheroidal cast iron sample. The optimisation...
-
Effect of Processing Parameters on Strength and Corrosion Resistance of Friction Stir-Welded AA6082
PublikacjaThe friction stir welding method is increasingly attracting interest in the railway sector due to its environmental friendliness, low cost, and ease of producing high-quality joints. Using aluminum alloys reduces the weight of structures, increasing their payload and reducing fuel consumption and running costs. The following paper presents studies on the microstructure, strength, and corrosion resistance of AA6082 aluminum alloy...
-
Kinetics of Intermetallic Phase Precipitation in Manual Metal Arc Welded Duplex Stainless Steels
PublikacjaThe article presents the influence of heat treatment on the kinetics of transformations in lean duplex LDX2101 steel and a weld made of standard duplex 2209 material, which was welded by manual metal arc welding. Changes in the microstructure, hardness, and magnetic phase content were analyzed after heat treatment was conducted at a temperature of 800 °C for a period ranging from 15 to 1440 min. Light and scanning microscopy, Vickers...
-
N-doped carbon materials as electrodes for highly stable supercapacitors
PublikacjaThis article reports a strategy to use nitrogen-doped carbon materials as electrodes for supercapacitors. Depending on the carbon precursor, the porous structure is changed with specific surface area reached up to 2270 m2 g−1. The capacitance of carbon materials used as electrodes is related strictly to pore size. The microstructure and nitrogen functionalities enable a high capacitance (327 F g−1) and cycle durability. The nanoporous...
-
Właściwości elektryczne szkło-ceramiki zawierającej ferroelektryczną fazę BiV
PublikacjaKompozyty szklano - ceramiczne zawierające nanokryształy posiadają właściwości fizyczne, które nie są możliwe do uzyskania w innych materiałach. Dzięki możliwości wytworzenia szkło - ceramik posiadających kryształy o różnej wielkości (nano, mikro...) i różnorodnego typu, można w istotny sposób kontrolować właściwości elektryczne takich materiałów. Stała dielektryczna faz ferroelektrycznych jest bardzo wrażliwa na zmiany rozmiarów...
-
Evaluation of Praseodymium and Gadolinium Doped Ceria as a Possible Barrier Layer Material for Solid Oxide Cells
PublikacjaIn this work, nanocrystalline layers based on the Pr, Gd co-doped CeO2 were investigated. For the preparation of thin layers, lowtemperature spray pyrolysis technique was used. Different stoichiometries of the layers were produced for comparison on polished sapphire substrates. The microstructure of the prepared thin layers was studied by scanning electron microscopy (SEM), energydispersive X-ray spectroscopy (EDS) and X-ray diffractometry (XRD)....
-
Cavitation Erosion Resistance Influence of Material Properties
PublikacjaThe cavitation erosion is the phenomena that causes degradation of fluid flow machinery components due to repetitive implosion of cavitation bubbles adjacent to the solid surface. Cavitation erosion is a complex phenomenon, which includes not only hydrodynamic factors of liquid, but also properties of erodible material e.g. microstructure, hardness or Young modulus. In order to reduce the negative impact of erosion on machine components,...
-
Temperature Fiber-Optic Sensor with ZnO ALD Coating
PublikacjaThis study presents a microsphere-based fiber-optic sensor with a ZnO Atomic Layer Deposition (ALD) coating thickness of 100 nm for temperature measurements. Metrological properties of the sensor were investigated over the temperature range of 100 °C to 300 °C, with a 10 °C step. An interferometric signal is used to control whether the microstructure is whole. Spectrum shift of a reflected signal is used to ascertain changes in...
-
Induction Assisted Hybrid Friction Stir Welding of Dissimilar Materials AA5052 Aluminium Alloy and X12Cr13 Stainless Steel
PublikacjaThis research aimed to study the induction in-situ heated hybrid friction stir welding (IAFSW) method to join AA5052 aluminium alloy with X12Cr13 stainless steel (SS) to enhance joint strength. The potency of this method on the mechanical properties and microstructural characterizations were also investigated. The results show that the transverse tensile strength gained was 94% of the AA5052 base metal that is 229.5 MPa. This superior...
-
Corrosion degradation impact on mechanical properties of structural steel
PublikacjaRecently, extensive research was conducted regarding the impact of corrosion degradation on the mechanical properties of structural steel. Studies show that at the material level, the microstructure is somewhat unchanged due to corrosion degradation. However, the corrosion causes pits and structural surface irregularities that consequently impact the mean stress-strain response of typical coupon specimens subjected to tensile loading....
-
Influence of Heat Treatment Temperature on Fatigue Toughness in Medium-Carbon High-Strength Steels
PublikacjaCurrent research has demonstrated that the tempering temperature affects the martensitic transformation of medium-carbon high-strength steels. This temperature plays an important role in the final microstructure, percentage ratios of martensite to ferrite phases and, consequently, in the mechanical properties and the fatigue response. So far, the relationship between the martensitic tempering temperature and the cyclic deformation...
-
Analysis of features of stainless steels in dissimilar welded joints in chloride inducted corrosion
PublikacjaStainless steels of femtic-austenitic microstructure that means the duplex Cr-Ni-Mo steels, in comparison with austenitic steel includes less expensive nickel and has much better mechanical properties with good formability and corrosion resistance, even in environments containing chloride ions. Similar share of high chromium ferrite and austenite, which is characterized by high ductility, determines that the duplex steels have...
-
Investigation of Mechanical and Microstructural Properties of Welded Specimens of AA6061-T6 Alloy with Friction Stir Welding and Parallel Friction Stir Welding Methods
PublikacjaThe present study investigates the effect of two parameters of process type and tool offset on tensile, microhardness, and microstructure properties of AA6061-T6 aluminum alloy joints. Three methods of Friction Stir Welding (FSW), Advancing Parallel-Friction Stir Welding (AP-FSW), and Retreating Parallel-Friction Stir Welding (RP-FSW) were used. In addition, four modes of 0.5, 1, 1.5, and 2 mm of tool offset were used in two welding...
-
AFM imaging of surface of modern soldering alloy
Dane BadawczeFollowing the announcement in 2006 of European Union directives aimed at limiting the use of lead in electronic products, there was an urgent need to use lead-free solders in the electronics industry. Due to production requirements, it is necessary to use solders with different melting points. To replace the low-melting eutectic Sn 37 wt. Pb, the most...
-
Multicomponent layers for aluminium alloys surface consolidation
PublikacjaThe main reason of the surface modification of the components such as pistons and cylinder blocks made of cast aluminium alloys is to obtain high hardness, wear and corrosion resistance of the working surface for larger lifetime of the motor-car and aircraft engines. In that aspect, the new conception of development - by hybrid method - of surface layers containing manganese, nitrogen, sulphur (Mn-N-S) and manganese, nitrogen,...
-
On the correlation between magnetoacoustic emission and magnetostriction dependence on the applied magnetic field
PublikacjaThe correlation between magnetoacoustic emission signal envelopes and magnetostriction curves is investigated. Two sets of samples are being considered: tempered martensitic steel and plastically deformed ferritic steel. It is shown that even though some general relations may be observed, as was demonstrated in the literature, the correlation is not always present. One may not expect to change both quantities in the same way if...
-
On the influence of a surface roughness on propagation of anti-plane short-length localized waves in a medium with surface coating
PublikacjaWe discuss the propagation of localized surface waves in the framework of the linear Gurtin–Murdoch surface elasticity and taking into account a roughness of a free boundary. We derive a boundary-value problem for anti-plane motions with curvilinear boundary and surface stresses. Using the asymptotic technique developed earlier, we obtain the form of a localized wave and analyze its amplitude evolution. As the main result we present...
-
Water sorption and blistering of GFRP laminates with varying structures
PublikacjaThe microstructures, water absorption as well as blistering was studied for bi- and tri- axial glass fibre vinyl ester and polyester -matrix laminates coated with gel coat layer and uncoated. The effect of manufacturing technique on water sorption characteristics was considered. It was found that water sorption characteristics of GFRP depend on manufacturing methods. The least water intake was found for specimens having perfect...
-
Characterization of CaTi0.9Fe0.1O3/La0.98Mg0.02NbO4 composite
PublikacjaA composite of CaTi0.9Fe0.1O3 and electrolyte material, i.e. magnesium doped La0.98Mg0.02NbO4 was prepared and studied. The phase content and the sample microstructure was examined by an X-ray diffraction method and scanning electron microscopy. EDS measurements were done both for composite samples and the diffusion couple. The electrical properties were studied by four terminal DC method. The Ahigh-temperature interaction between...
-
Characterization of magnesium doped lanthanum orthoniobate synthesized by molten salt route
PublikacjaMolten salt synthesis method has been used to prepare the single phase magnesium doped lanthanum orthoniobate. The phase composition has been checked by X-ray diffraction method and the microstructure studies have been performed by scanning electron microscopy. The high temperature properties of the material have been investigated by thermogravimetry and electrochemical impedance spectroscopy. A dependence between sample total...
-
Nanocrystalline cathode functional layer for SOFC
PublikacjaRecently, it was shown that thin functional layers introduced between an electrolyte and cathode might improve cathode performance. However, the mechanism of this improvement still needs analysis. In this paper, a thin (∼140 nm), spin-coated perovskite layer (La0.6Sr0.4Co0.2Fe0.8O3-δ) was placed between a cathode (La0.6Sr0.4Co0.2Fe0.8O3-δ) and an electrolyte (Ce0.8Gd0.2O2-δ) and the effects of this investigated. The microstructure...
-
Failure of austenitic stainless steel tubes during steam generator operation
PublikacjaThe article presents the failure process of austenitic stainless steels used in power devices, such as heat exchangers, steam generators, in terms of local corrosion: pitting, stress and intergranular corrosion, paying particular attention to welded joints area. The effect of steel chemical composition, microstructure, welding process and work environment was analyzed. The second part of the article presents the results of the...
-
Chitosan/poly(4-vinylpyridine) coatings formed on AgNPs-decorated titanium
PublikacjaElectrophoretic deposition (EPD) of chitosan/poly(4-vinylpyridine) (chit/P4VP) coatings on titanium substrates previously decorated with silver nanoparticles (AgNPs) was performed at different content of P4VP in the suspension and different voltage values. The results revealed that the composite coatings were formed, well-adjacent to the titanium substrate, of suitable roughness, hydrophilicity, and corrosion resistance. The voltage...
-
Metallurgical characterization and high-temperature tensile failure of Inconel 617 alloy welded by GTAW and SMAW—a comparative study
PublikacjaTwo types of the weld joint of Inconel 617 alloy were produced using gas tungsten arc welding (GTAW) and shielded metal arc welding (SMAW) processes with ERNiCrCoMo-1 filler metal and ENiCrCoMo-1 electrode, respectively. The weld metal showed the segregation of the principle alloying elements like Mo and Cr along the inter-dendritic spaces, triggering the formation of secondary phases. The microstructure characterization of the...
-
Corrosion of evaporator tubes in low emission steam boilers
PublikacjaPurpose of this paper is to reveal the mechanisms of corrosion processes of outer surfaces of low-emission steam boiler evaporator tubes. Examinations were performed to find the reasons of different corrosion susceptibility of tubes situated at combustion chamber on various levels. Examinations were conducted on several segments of 57 x 5.0 mm evaporator tubes made of 16M (16Mo3) steel grade. Segments were taken from level of...
-
Nonlinear and linear impedance of bismuth vanadate ceramics and its relation to structural properties
PublikacjaThe nonlinear and linear electrical properties, topography, and microstructure of bismuth-vanadate ceramics, were studied. The structurewas observed with the use of X-ray diffraction (XRD), scanning electronmicroscopy (SEM), atomic force microscopy (AFM) and confocal microscopy methods. The obtained results showed that ceramic is porous. Two phase transitionswere determinedwith the use of DSC measurements. The linear and nonlinear ac...
-
Binder-induced surface structure evolution effects on Li-ion battery performance
PublikacjaA comparative investigation on binder induced chemical and morphological evolution of Li4Ti5O12 electrodes was performed via X-ray photoemission spectroscopy, scanning electron microscopy, and electrochemical measurements. Composite electrodes were obtained using three different binders (PAA, PVdF, and CMC) with 80:10:10 ratio of active material:carbon:binder. The electrochemical performances of the electrodes, were found to be...
-
Performance and Stability in H2S of SrFe0.75Mo0.25O3-δ as Electrode in Proton Ceramic Fuel Cells
PublikacjaThe H2S-tolerance of SrFe0.75Mo0.25O3-δ (SFM) electrodes has been investigated in symmetric proton ceramic fuel cells (PCFC) with BaZr0.8Ce0.1Y0.1O3-δ (BZCY81) electrolyte. The ionic conductivity of the electrolyte under wet reducing conditions was found to be insignificantly affected in the presence of up to 5000 ppm H2S. The fuel cell exhibited an OCV of about 0.9 V at 700 °C, which dropped to about 0.6 V and 0.4 V upon exposure...
-
Properties of Barium Cerate-Zirconate Thin Films
PublikacjaIn this work, we review several experimental results showing the electrical properties of barium cerate-zirconate thin films and discuss them in view of the possible influence of various factors on their properties. Most of the presented Ba(Ce, Zr, Y)O3 thin films were formed by the pulsed laser deposition (PLD) technique, however thin films prepared using other methods, like RF magnetron sputtering, electron-beam deposition, powder...
-
Cavitation Erosion Resistance of Austenitic Stainless Steel after Glow-Discharge Nitriding Process
PublikacjaThis paper presents investigation of cavitation erosion resistance of nitrided austenitic stainless steel X5CrNi18-10. The diffusion layers were produced by using different parameters of atmosphere (N2:H2). The microstructure, chemical composition and phase identification of the modified layer were examined using scanning electron microscopy, glow-discharge optical emission spectrometer and X-ray diffractometry, respectively. Cavitation...
-
Application of the X-ray micro computed tomography to the analysis of the structure of polymeric materials
PublikacjaIn this paper the application of X-ray micro-computed tomography (micro-CT) as a non-destructive testing method of polymeric materials is presented. Increasing applicability of polymers in variedend-use industries such as automotive, building and construction, consumer goods, and packaging is propelling the growth of the global polymer processing market. However, controlling of the polymer structure is one of the most important...
-
Impact of laser beam welding on mechanical behaviour of 2.25Cr–1Mo (P22) steel
PublikacjaThe use of welding processes in the manufacturing and repair of structures intended for the energy industry plays a key role in the guarantee of a continuous supply of fossil fuels, which is the basic condition for ensuring energy security. A square butt joint of 10 mm thick plate of 2.25Cr–1Mo (P22) steel was fabricated by autogenous laser beam welding process and then post-weld heat treatment (PWHT) for two sets of process parameters...
-
Mechanical and Microstructural Characterization of TIG Welded Dissimilar Joints between 304L Austenitic Stainless Steel and Incoloy 800HT Nickel Alloy
PublikacjaIn this article, the mechanical properties and microstructure of 304L austenitic stainless steel/Incoloy 800HT nickel alloy dissimilar welded joints are investigated. The joints were made of 21.3 mm × 7.47 mm tubes using the TIG process with the use of S Ni 6082 nickel filler metal. No welding imperfections were found and high strength properties of joints were obtained, meeting the assumed acceptance criteria of the product’s...
-
Effect of plasma sprayed and laser re-melted Al2O3 coatings on hardness and wear properties of stainless steel
PublikacjaCommercially available austenic stainless steel substrate was coated with commercially available, raw Al2O3 powder applied by means of plasma spraying method and then re-melted with CO2 laser beam of various parameters. Tribological and mechanical properties of the 120 J/mm and 160 J/mm laser re-melted coatings were compared with the tribological and mechanical properties of the “as-sprayed” coating. The influence of the laser...
-
Manganese Phosphatizing Coatings: The Effects of Preparation Conditions on Surface Properties
PublikacjaManganese phosphate coating could be used to protect the surface of steel products. However, it is essential to determine the effects which process parameters, as well as the types of additives used, have on the efficiency of coating deposition. Thus, we present here a process of phosphatization of low-alloy steel (for 15 min at 95 ◦C) in manganese/nickel baths followed by a passivation process with the use of a silicon and zircon...
-
Influence of High Temperature Oxidation on Hydrogen Absorption and Degradation of Zircaloy-2 and Zr 700 Alloys
PublikacjaThe present research was aimed at determining the effects of the oxide layers on hydrogen absorption, microstructure and mechanical properties of the Zircaloy- 2 and Zr 702 alloys. The oxidation was made at 350 °C, 700 °C and 900 °C for 10 to 30 min in laboratory air, followed by hydrogen cathodic charging for 72 h and annealing at 400 °C for 4 h. The slow strain rate tests were carried out on oxidized, charged and annealed specimens. The...
-
Structural and catalytic properties of ceria layers doped with transition metals for SOFCs fueled by biogas
PublikacjaThe aim of this paper was to investigate an influence of the nanocrystalline Ce0.8A0.2O2-δ (A = Mn, Fe, Co, Ni, Cu) materials on the direct internal reforming of biogas in SOFC. Structural analysis of fabricated compounds has been done. An in-situ analysis of a composition of outlet gases from operating SOFC was performed using FTIR spectroscopy with simultaneous electrical tests. It was found out, that type of dopant strongly...
-
Manganese–Cobalt Based Spinel Coatings Processed by Electrophoretic Deposition Method: The Influence of Sintering on Degradation Issues of Solid Oxide Cell Oxygen Electrodes at 750 °C
PublikacjaThis paper seeks to examine how the Mn–Co spinel interconnect coating microstructure can influence Cr contamination in an oxygen electrode of intermediate temperature solid oxide cells, at an operating temperature of 750 °C. A Mn–Co spinel coating is processed on Crofer 22 APU substrates by electrophoretic deposition, and subsequently sintered, following both the one-step and two-step sintering, in order to obtain significantly...
-
Structure and thermoelectric properties of Bi–Te alloys obtained by novel method of oxide substrates reduction
PublikacjaA novel method of thermoelectric materials fabrication has been developed. Oxide reagents have been melted at high temperature in air, quenched, milled to powder and reduced in hydrogen to form Bi–Te alloys. Structural and thermoelectric properties of samples have been investigated depending on initial composition and temperature of reduction process. Sample 25Bi2O3–75TeO2 reduced at 340 °C for 10 h has been found to be a p-type...
-
A hyperelastic model for soils with stress-induced and inherent anisotropy
PublikacjaIn this paper, modelling of the superposition of stress-induced and inherent anisotropy of soil small strain stiffness is8presented in the framework of hyperelasticity. A simple hyperelastic model, capable of reproducing variable stress-induced9anisotropy of stiffness, is extended by replacement of the stress invariant with mixed stress–microstructure invariant to10introduce constant inherent cross-anisotropic component. A convenient...
-
Effects of V2O5 Additive on Structure and Dielectric Properties of BiNbO4 Ceramics
PublikacjaGoal of the present research was to investigate the influence of V2O5 additive on the structure and dielectric properties of BiNbO4 ceramics. To fabricate BiNbO4 ceramics with V2O5 added the solid state reaction route and pressureless sintering was utilized. Thus obtained ceramics was characterized in terms of its microstructure (SEM), chemical composition (EDS), phase composition and crystalline structure (X-ray phase and structural...
-
Effect of Bi2O3 Excess on Morphology and Structure of BiNbO4 Ceramics
PublikacjaGoal of the present research was to fabricate BiNbO4 ceramics from the mixture of powders by the solid state reaction route and pressureless sintering at various temperatures (TS =8700C and TS =9100C) and study microstructure, phase composition and crystalline structure of BiNbO4 ceramics. Four batches were fabricated and examined, namely the one fabricated from the stoichiometric mixture of reagent – grade oxide powders, viz....
-
Wytwarzanie i modyfikacja powierzchni porowatych struktur tytanowych przeznaczonych na implanty
PublikacjaCelem pracy było wytworzenie stopu Ti-13Nb-13Zr z wykorzystaniem technologii selektywnego topienia laserowego (SLM) oraz jego biofunkcjonalizacja za pomocą utleniania mikrołukowego (MAO), a następnie określenie wpływu parametrów procesowych na właściwości otrzymanych materiałów pod kątem ich zastosowania na implanty. Oceniono wpływ napięcia, natężenia i czasu procesu MAO przeprowadzanego w elektrolicie zawierającym wapń i fosfor...
-
"Raport z wstępnych badań własności stali trudnościeralnej 460HB",. ang "Report on preliminary tests of the properties of wear-resistant steel 460HB"
PublikacjaMikrostrukturę badanej stali trudnościeralnej 460HB stanowi drobnoziarnisty martenzyt odpuszczony, który jest właściwy dla stali konstrukcyjnych niskowęglowych, niskostopowych ulepszonych cieplnie. W przypadku blach grubych, do których zalicza się badana stal, struktura może ulec zaburzeniu, jeżeli w hutniczym procesie wytwórczym wystąpiła niejednorodność odkształcenia plastycznego i w konsekwencji tworzenie się pasm segregacyjnych,...
-
Surface treatment of C80U steel by long CO2 laser pulses
PublikacjaThe paper presents the results of laser-melted C80U steel. The processed steel was placed between two permanent magnets and laser beam whose scanning velocity was 10 mm/s. CO2 laser beam was working in pulse mode. Pulses were generated at 100% of the average preset power of 700W, with 45 ms irradiation, zero interval between pulses and beginning of pulse repetition upon the achievement of the average laser power. During the operation,...
-
Solid-State Modification of Poly(butylene terephthalate) with a Bio-Based Fatty Acid Dimer Diol Furnishing Copolyesters with Unique Morphologies
PublikacjaCopolyesters based on poly(butylene terephthalate) (PBT) and a bio-based fatty acid dimer diol (FADD) were prepared by solid-state modification (SSM). The chemical incorporation of the FADD into the backbone of the PBT was proven using various techniques. It was clear that the incorporation rate was diffusion-limited rather than reaction-limited. From quantitative 13C NMR a nonrandom chemical microstructure was obtained at all...
-
Corrosion behavior of hydrogen charged super duplex stainless steel welded joints
PublikacjaThe electrochemical behavior of the weld metal, heat-affected zone (HAZ), and base material of super duplex stainless steel (SDSS) welded joints, made with the application of flux-cored arc welding (FCAW) and submerged arc welding (SAW), were investigated with the use of metallographic examinations (optical microscopy and scanning electron microscopy), potentiodynamic polarization measurements and total hydrogen content determination...