ZnFe2O4/ZnO nanoparticles obtained by coprecipitation route, XPS and TEM study
Publikacja -
DETERMINATION OF SP3 FRACTION IN ta-C COATING USING XPS AND RAMAN SPECTROSCOPY
PublikacjaThe paper presents results of studies on the structure of tetrahedral amorphous carbon films (ta-C) with a thickness in the range from 20 to 280 nm, deposited using pulsed vacuum arc technique with an electromagnetic Venetian blind plasma filter. The results of the phase structure analysis, obtained using visible Raman spectroscopy and UV Raman spectroscopy methods, showed a strong dependence of the results on the presence, on...
-
Ex situ XANES, XPS and Raman studies of poly(3,4-ethylenedioxythiophene)modified by iron hexacyanoferrate
PublikacjaPraca dotyczy badań XANES, XPS i Ramana polimeru przewodzącego poli(3,4-etylenodioksytiofenu) modyfikowanego heksacyjanożelazianem żelaza. Badania XANES potwierdziły oktaedryczne otoczenie atomu żelaza, którego najbliższymi sąsiadami są atomy węgla oraz atomy azotu. Badania XPS wykazały istnienie wiązań Fe-C, Fe-N oraz chemicznego oddziaływania między atomem siarki polimeru a atomem żelaza błękitu pruskiego. Obecność oddziaływań...
-
Ex situ XANES, XPS and Raman studies of poly(3,4-ethylenedioxythiophene) modified by iron hexacyanoferrate
PublikacjaPraca dotyczy materiału hybrydowego złożonego z polimeru elektroaktywnego poli(3,4-etylenodioksytiofenu) i Błękitu Pruskiego. Wykonano pomiary spektroskopowe z użyciem technik: spektrometrii fotoelektronów wzbudzonych promieniami X (X-ray Photoelectron Spectroscopy (XPS)), spektroskopii absorpcyjnej struktury przykrawędziowej (X-ray Absorption Near Edge Structure (XANES)) oraz spektroskopii mikro-Ramana. Przeprowadzone badania...
-
Effect of cobalt addition on the corrosion behaviorof near equiatomic NiTi shape memory alloy in normal saline solution: electrochemical and XPS studies
PublikacjaThe electrochemical and corrosion (uniform and localized) behavior of a binary Ni52Ti48 shape memory alloy (SMA) and two ternary Ni52Ti48-xCox (x = 1.5 and 4.0 wt.%) SMAs were studied. Measurements were conducted in 0.9% NaCl solution at 37 oC employing various electrochemical methods. These include: linear polarization resistance (LPR), linear sweep voltammetry (LSV), chronoamperometry and dynamic electrochemical impedance spectroscopy...
-
XPS study of the YST ceramics
Dane BadawczeYttrium-doped strontium titanate was prepared via conventional solid-state reaction method from Y2O3 (Sigma Aldrich, 99,9%), TiO2 (Sigma Aldrich, 99%) and SrCO3 (Sigma Aldrich,98%). For comparision, two other techniques were used for synthesis: Pechini and wet methods. Both kind of samples were measured, after and before reduction process (in a hydrogen)....
-
XPS data of MXene catalyst
Dane BadawczeData contain results from XPS measurement of the Ti3C2Tx MXenes produced via acidic etching aluminum from MAX Phase (Ti3C2-Al-Ti3C2-Al-Ti3C2) using 48% HF etching agent (MXene HF). The X-ray spectroscopy (XPS) measurements were conducted using Mg Ka (hn = 1253.6 eV) radiation in a Prevac (Poland) system equipped with a Scienta SES 2002 (Sweden) electron...
-
XPS analysis of TBBO glass
Dane BadawczeGlasses and glass-ceramics with nominal composition 73 TeO2– 4BaO– 3Bi2O3–18SrF2-2RE2O3 (where RE = Eu, Dy) have been synthesized by conventional melt-quenching technique and subsequent heat treatment at 370 °C for 24 h in air atmosphere. Various Eu3+ to Dy3+ molar ratio have been applied to investigate luminescence properties in both glass and glass-ceramic...
-
XPS-TiO2 heated in H2
Dane BadawczeThese XPS spectra were recorded for TiO2 heat-treated at 450-600oC in H2. Surface oxygen groups were determined. Deconvolution of Ti 2p peak allowed to determine Ti3+ on the titania surface.
-
The 3d Ce XPS spectra of Ce0.9M0.1O2
Dane BadawczeThe dataset consists of 3d Ce XPS of Ce0.9M0.1O2 where (M=Mn, Fe, Co, Ni, Cu). X-ray Photoelectron Spectroscopy analysis (XPS) was performed using X-ray photoelectron spectrometer Omnicron NanoTechnology with 128-channel collector. XPS measurements were undertaken in ultra-high vacuum conditions, below 1.1x10-8 mbar. Photoelectrons were excited by an...
-
The XPS spectra of LSCNT sintered at 1200C
Dane BadawczeThe dataset includes XPS spectra of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s sintered at various temperatures under air atmosphere for 12 h. Samples were produced using aqueous soft chemistry methods (Pechini). The XPS spectra were collected for all species.
-
XPS analysis of the GO based materials
Dane BadawczeGraphene oxides samples were measured by XPS method. The X-ray photoemission spectroscopy measurements were carried out with Omicron NanoTechnology UHV equipment. The hemispherical spectrophotometer was equipped with a 128-channel collector. The XPS measurements were performed at room temperature at a pressure below 1.1 × 10−8 mBar. The photoelectrons...
-
Depth XPS profile of vanadium pentoxide
Dane BadawczeVanadium pentoxide sample was manufactured by sol-gel method and deposited on a substrate by spin coating technique. To determine depth profile of chemical composition of thin film, etching by Argon ion gun was used. Thin film was etched three times. Chemical composition was measured by XPS method.
-
XPS analysis of strontium titanate ceramics
Dane BadawczeThe chemical composition of the strontium titanite doped with yttrium and iron ceramic samples was investigated. Samples of Y0.07Sr0.93Ti0.8Fe0.2 were prepared by solid phase reaction and sintered for 24 and 48 hours. Chemical composition was measured by UHV OmicronNanotechnology XPS system. The analysis confirmed the chemical composition of the ceramics...
-
SPTNO ceramics measured by XPS method
Dane BadawczeSPTNO (Sr-Pr-Ti-Ni-O) ceramic were manufactured by solid state reaction, from oxides compounds. Synthesis conducted in air atmosphere at temperature in a range of 800-900 deg. Chemical composition of prepared materials were measured by XPS (X-Ray photoemision spectroscopy) method. UHV OmicronNanotechnology system with 128 channel Argus hemispherical...
-
XPS study of the NH4-VOx powders
Dane BadawczeVanadium pentoxide samples were prepared by sol-gel method. The starting solution was prepared by mixing vanadium (V) oxytripropoxide (Aldrich) in an anhydrous ethanol as solvent and acetylacetone. By drying the sol at 323 K for 48 h, it transforms via gel into a xerogel powder. Next, the precursor powder was pressed into the disk-shaped pellets. Samples...
-
XPS study of the TiO2-WO2 composites
Dane BadawczeValence state of W and Ti was measured in a TiO2-WO3 composites with a various composition.Powder samples of pure titanium dioxide, tungsten oxide and mix of 50% titanium oxide and 50% od tungsten oxide were measured. Oxides were annealed at the temperature in the range of 300 Celsius degree up to 900 deg. Measurements were performed by XPS UHV Omicron...
-
The 2p XPS spectra of transition metals in Ce0.9M0.1O2
Dane BadawczeThe dataset consists of 2p XPS spectra of transition metals in Ce0.9M0.1O2 where (M=Mn, Fe, Co, Ni, Cu). X-ray Photoelectron Spectroscopy analysis (XPS) was performed using X-ray photoelectron spectrometer Omnicron NanoTechnology with 128-channel collector. XPS measurements were undertaken in ultra-high vacuum conditions, below 1.1x10-8 mbar. Photoelectrons...
-
XPS measurement of the Fe-Ti based materials
Dane BadawczeThe mono‐ and bimetal‐modified (Pd, Cu) titanium(IV) oxide and iron oxide (III) photocatalysts were prepared by chemical reduction method and characterized using XPS method. The composition of elements incorporated in the surface layer of mono- and bimetallic photocatalysts was determined by XPS analysis, as well as the valence state of elements. Measurements...
-
XPS studies of PDA-modified TiO2 nanotubes
Dane BadawczeThis dataset contains the XPS results (survey and high-resolution spectra) of the samples from TiO2 nanotubes modified with polydopamine. The studies were presented as a part of the research on "Band Gap Engineering toward Semimetallic Character of Quinone-Rich Polydopamine" (DOI: 10.1021/acs.jpcc.2c08804).