FTIR-TiO2 heated at 400-600oC in Ar or H2
Dane BadawczeData contain FTIR diffuse eflectance spectra of TiO2, which was heat-treated at 400-600oC in Ar or H2. Hydrogen reduced TiO2 revealed new bands due to the adsorption of some species on the titania oxygen vacancy sites.
-
The structure of vanadate glass-ceramics containing BaTiO3 measured with X-ray diffraction method
Dane BadawczeThe structure of vanadate glass-ceramics doped with BaTiO3 was measured by XRD. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated...
-
Photoluminescence spectra of TiO2
Dane BadawczeThese data contain photoluminescence spectra of TiO2 measured at the temperature of liquid nitrogen. There is a comparison of the photoluminescence spectra of TiO2 heat treated at 400-600oC in the ambient (Ar) and reduced (H2) atmospheres. These emission spectra were recorded after TiO2 excitation with a wavelength of 290 nm
-
The structure of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides measured with X-ray diffraction method
Dane BadawczeThe structure of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides was measured by XRD.
-
Energy Security of Polish Consumers in 2004-2021
Dane BadawczeEnergy security is one of the most important components of economic security. It is influenced not only by access to energy sources and the economic situation of the state and the individual consumer. In the years 2004–2021, energy security of the individual consumer in the economic dimension significantly improved. This was due to several factors:1....
-
TG-hydroxyl groups in TiO2-P25
Dane BadawczeTG analyses were performed for powdered TiO2 - commercial P25 sample, which was heat-treated from room temperature to 500 C in the nitrogen atmosphere. Mass loss at lower temperature such as 120 C was related to the physisorbed water, and that one occurring at 500 C to the chemisorbed hydroxyl groups.
-
SEM/EDX data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe
Dane BadawczeThis Data set include SEM and EDX results of (Mn,Co,Fe,Ni,Cr)3O4 high-entropy spinel oxide prepared in the form of a ~ 500 nm thin film utilising a facile spray pyrolysis technique. The structural and electrical properties of the layers were characterised after exposure to temperatures in the range of 400–900 ◦C. The as-deposited layers were amorphous,...
-
TEM data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe
Dane BadawczeThis Dataset include presentation of summarized TEM investigation of (Mn,Co,Fe,Ni,Cr)3O4 high-entropy spinel oxide prepared in the form of a ~ 500 nm thin film utilising a facile spray pyrolysis technique. The structural and electrical properties of the layers were characterised after exposure to temperatures in the range of 400–900 ◦C. The as-deposited...
-
Measurements of the heat of hydration released by concrete specimens cured under adiabatic conditions
Dane BadawczeThe DataSet contains measurements of heat of hydartion of concrete cubes (150 x 150 x 150 mm) cured under adiabatic conditions. The specimens were moulded from six types of concrete mixtures produced in the laboratory conditions. Mix #1: Portland cement CEM I 42.5R and gravel aggregate, mix #2: CEM I 42.5R and basalt aggregate, mix#3: Portland-composite...
-
Testing an evaporator operation with a concave manifold, condenser temperature 30, evaporator temperature 70 and preheater temperature 60
Dane BadawczeThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
Testing an evaporator operation with a bifurcation manifold, condenser temperature 20 and evaporator temperature 85
Dane BadawczeThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
Testing an evaporator operation with a concave manifold, condenser temperature 30, evaporator temperature 70 and preheater temperature 40
Dane BadawczeThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
Testing an evaporator operation with a trapezoidal manifold, condenser temperature 90 and evaporator temperature 90
Dane BadawczeThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
Testing an evaporator operation with a bifurcation manifold, condenser temperature 20 and evaporator temperature 70
Dane BadawczeThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
Testing an evaporator operation with a rectangular manifold, condenser temperature 30 and evaporator temperature 90
Dane BadawczeThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
Testing an evaporator operation with a trapezoidal manifold, condenser temperature 70 and evaporator temperature 60
Dane BadawczeThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
Testing an evaporator operation with a bifurcation manifold, condenser temperature 20 and evaporator temperature 95
Dane BadawczeThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
Testing an evaporator operation with a bifurcation manifold, condenser temperature 20 and evaporator temperature 90
Dane BadawczeThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
The topography of as-quenched and heat treated 50(2Bi2O3-V2O5)-50SrB4O7 and 50Bi2VO5.5-50SrB4O7 glasses measured with confocal microscope
Dane BadawczeThe topography of as-quenched and heat treated 50(2Bi2O3-V2O5)-50SrB4O7 and 50Bi2VO5.5-50SrB4O7 glasses measured with confocal microscope.
-
The topography of as-quenched and heat treated 50(2Bi2O3-V2O5)-50SrB4O7 and 50Bi2VO5.5-50SrB4O7 glasses measured with AFM
Dane BadawczeThe topography of as-quenched and heat treated 50(2Bi2O3-V2O5)-50SrB4O7 and 50Bi2VO5.5-50SrB4O7 glasses measured with AFM.
-
Total electrical conductivity data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe
Dane BadawczeThis dataset includes electrical conductivity measurements results measured by van der pauw technique up to 900oC.
-
The topography of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides measured with SEM method
Dane BadawczeThe topography of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides was measured by SEM.
-
Thermal conductivity of M0-M100 specimens
Dane BadawczeThermal conductivity and volumetric heat capacity values of M0, M20, M40, M60, M80, M100 samples
-
Dilatometry results of SrTi0.50Fe0.50O3-d powder
Dane BadawczeThis dataset contains results of dilatometry measurements of SrTi0.50Fe0.50O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.50Fe0.50O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Dilatometry results of SrTi0.65Fe0.35O3-d powder
Dane BadawczeThis dataset contains results of dilatometry measurements of SrTi0.65Fe0.35O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.65Fe0.35O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Dilatometry results of SrTi0.30Fe0.70O3-d powder
Dane BadawczeThis dataset contains results of dilatometry measurements of SrTi0.30Fe0.70O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.30Fe0.70O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
BET of TiO2 heated at 400-600 C degrees
Dane BadawczeThese data refer to the results of BET surface area of TiO2, which was treated firstly in autoclave at 150 C degrees for 1h (sample marked as A150), then was further heat treated in Ar or H2 at 400-600 C degrees. As a raw material TiO2 was used, which was a semiproduct from the industrial production of titania white by sulphur method. The raw material...
-
Linear impedance as a function of A.C. voltage for 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K measured with impedance spectroscopy method at 273 K
Dane BadawczeThe linear electrcial properties as a function of A.C. voltage for 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K was measured by impedance spectroscopy method.
-
Linear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 613 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe linear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 613 K was measured by impedance spectroscopy method.
-
Linear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K was measured by impedance spectroscopy method.
-
Linear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times measured with impedance spectroscopy method at low temperatures
Dane BadawczeThe linear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times was measured by impedance spectroscopy method.
-
Linear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe linear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K was measured by impedance spectroscopy method.
-
DSC measurments of ammonium vanadate nanocrystals
Dane BadawczeThe DataSet contains the thermal behavior of the ammonium vanadate nanostructures obtained by the hydrothermal method with different conditions. Differential scanning calorimetry (DSC) measurement was carried out under an argon atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The results reveal the differences...
-
Linear impedance as a function of A.C. voltage for 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 813 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe linear electrcial properties as a function of A.C. voltage of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 813 K was measured by impedance spectroscopy method.
-
Brunauer-Emmett-Teller (BET) surface analysis of titanium dioxide (TiO2) and silicon dioxide (SiO2) used for coating of expanded polystyrene spheres (EPS)
Dane BadawczeData refer to the results of BET surface area of TiO2 and SiO2 powders used for coating of expanded polystyrene spheres. The detailed measurement and equipment data was described in readme BET.txt file.TiO2 was treated firstly in autoclave at 150 C degrees for 1h, then was further heat treated in Ar at 400 C degrees. As a raw material TiO2 was used,...
-
Electrical measurements of the dewetting of metal thin films
Dane BadawczeIn situ observations of dewetting of thin films is very complicated. One of the method, that helps to observe it, could be electrical measurements. For experiments, thin gold, silver and gold-silver nanoalloy films were deposited by magnetron sputtering method. Films were deposited on a Corning glass substrates. Samples were measured by four point method...
-
SiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B37/#A35
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
TiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A39/#B41
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
SiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A35/#B37
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured by impedance spectroscopy method.
-
XRD data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe, annealed in a range from 400 to 900oC
Dane BadawczeDataset include collected XRD data of (Cr,Fe,Mn,Co,Ni)3O4 high-entropy spinel oxide thin films deposited by spray pyrolysis technique on amorphous SiO2 substrates and annealed from 400 to 900oC. Samples were prepared in the form of a ~ 500 nm thin film utilising a facile spray pyrolysis technique. The structural and electrical properties of the layers...
-
The morphology of vanadate glass-ceramics containing BaTiO3 measured with the use of AFM
Dane BadawczeThe structure of vanadate glass-ceramics doped with BaTiO3 was measured by AFM technique. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on...
-
Thermal properties of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides measured with DSC method
Dane BadawczeThermal properties of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides was measured by DSC.
-
Effect of particle size of aluminosilicate microspheres on the change of hydration heat of cement mortars and selected physical, chemical, and mechanical properties.
Dane BadawczeThis subject of the work is the study of selected properties of cement mortars containing two fractions of aluminosilicate microspheres with grain size in the range of 125 to 250 μm and from 250 to 500 μm. Mortar mixtures with ordinary Portland cement (OPC 42.5R) and three substitution rates of cement by microspheres, 1.5%, 3.5%, and 5.0%, were investigated....
-
The exemplary Kelvin probe microscopy studies of sensitized austenitic stainless steels
Dane BadawczeThe dataset summarizes the results of imaging the surface potential distribution using the Kelvin probe scanning technique. Due to the fact that the potential measured in this way is proportional to the electrochemical potential of metals or intermetallic phases, it is possible to assess the nobility differences of various alloy components. In the case...
-
TiN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B48/#A45
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 12 min....
-
TiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B41/#A39
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 9 min....
-
CrN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A23/#B22
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 12 min. The...
-
TiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B39/#A41
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...
-
SiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B34/#A33
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...