Filtry
wszystkich: 6591
wybranych: 870
-
Katalog
- Publikacje 5082 wyników po odfiltrowaniu
- Czasopisma 42 wyników po odfiltrowaniu
- Konferencje 1 wyników po odfiltrowaniu
- Wydawnictwa 1 wyników po odfiltrowaniu
- Osoby 144 wyników po odfiltrowaniu
- Projekty 11 wyników po odfiltrowaniu
- Laboratoria 1 wyników po odfiltrowaniu
- Kursy Online 87 wyników po odfiltrowaniu
- Wydarzenia 11 wyników po odfiltrowaniu
- Dane Badawcze 1211 wyników po odfiltrowaniu
Filtry wybranego katalogu
Wyniki wyszukiwania dla: SPHERE MAPS
-
Simulation of a linear pneumatic actuator with 100 mm piston diameter, 32 mm piston rod diameter and 25 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 63 mm piston diameter, 20 mm piston rod diameter and 500 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 63 mm piston diameter, 20 mm piston rod diameter and 50 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 63 mm piston diameter, 20 mm piston rod diameter and 25 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 63 mm piston diameter, 25 mm piston rod diameter and 200 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 100 mm piston diameter, 25 mm piston rod diameter and 100 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 100 mm piston diameter, 25 mm piston rod diameter and 200 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 32 mm piston diameter, 12 mm piston rod diameter and 50 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 32 mm piston diameter, 14 mm piston rod diameter and 25 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 100 mm piston diameter, 32 mm piston rod diameter and 100 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 100 mm piston diameter, 32 mm piston rod diameter and 500 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 32 mm piston diameter, 14 mm piston rod diameter and 200 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 100 mm piston diameter, 25 mm piston rod diameter and 25 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 63 mm piston diameter, 25 mm piston rod diameter and 500 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 100 mm piston diameter, 25 mm piston rod diameter and 50 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 32 mm piston diameter, 12 mm piston rod diameter and 100 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 100 mm piston diameter, 32 mm piston rod diameter and 50 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 32 mm piston diameter, 14 mm piston rod diameter and 100 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 32 mm piston diameter, 12 mm piston rod diameter and 500 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 100 mm piston diameter, 32 mm piston rod diameter and 200 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 63 mm piston diameter, 25 mm piston rod diameter and 100 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 32 mm piston diameter, 12 mm piston rod diameter and 200 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 32 mm piston diameter, 14 mm piston rod diameter and 50 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Simulation of a linear pneumatic actuator with 63 mm piston diameter, 25 mm piston rod diameter and 25 mm stroke
Dane BadawczeThe aim of the simulation was to determine the dynamics of linear pneumatic actuators with different sizes and flow properties. The simulation used the actuator dynamics model as described in [1] and the St Venant - Wantzel's mass flow rate model. The simulation experiment was to calculate the pressure changes in both chambers of the actuator as well...
-
Rheology studies of poly(lactic acid)-carbon black-nanodiamond composites
Dane BadawczeThis dataset contains rheology measurements carried out on new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The investigated techniques was performed by melt mass-flow rates (MFR)....
-
Floating treatment wetland with Equisetum hyemale - performance in nutrients and potentially toxic elements removal
Dane BadawczeThis data set contains the results of a microcosm experiment with floating treatment wetlands (FTW) conducted under artificial conditions. The goal of this experiment was to determine the effect of stress factors (Pb, As, increased salinity) on the nutrient uptake capacity of Equisetum hyemale in FTW. The ability of E.hyemale to uptake Pb and As was...
-
Nonlinear high temperature impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 glass
Dane BadawczeThe nonlinear high temperature impedance of iron- phosphate glasses doped with niobium oxide was measured. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG)...
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.88 mm was measured at 693 K with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of temperature and frequency for Bi2VO5.5 ceramic of thickness 2.52 mm was measured at different A.C. voltage with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 1.63 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 1.63 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 813 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeNonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 813 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass heat-treated for 3 hours at 693 K, measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of partially crystallized 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 4.03 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 4.03 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.91 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.91 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of frequency for Bi2VO5.5 ceramic of thickness 2.88 mm was measured at high temperature range with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance of 5(2Bi2O3-V2O5)-95SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 5(2Bi2O3-V2O5)-95SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass heat-treated for 10 hours at 693 K, measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of partially crystallized 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage and temperature for Bi2VO5.5 ceramic of thickness 2.52 mm (after first heat-treatment at 913 K) was measured at different frequencies with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Harmonic Analysis
Dane BadawczeWe construct a decomposition of the identity operator on a Riemannian manifold M as a sum of smooth orthogonal projections subordinate to an open cover of M. This extends a decomposition on the real line by smooth orthogonal projection due to Coifman and Meyer (C. R. Acad. Sci. Paris, Sér. I Math., 312(3), 259–261 1991) and Auscher, Weiss, Wickerhauser...
-
Measurement data of cyclic voltammetry and electrochemical impedance measurements of carbon samples synthesized on axes and off axes
Dane BadawczeThe electrochemical performance of the multielectrode samples were investigated by cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) using a VMP-300 BioLogic galvanostat potentiostat (France) under the EC-lab software. All electrochemical investigations were carried out in a three-electrode cell system. The carbon multi-electrode,...
-
The structure of the enterprise sector by size in Poland and the EU-28 in 2017
Dane BadawczeEnterprises from the SME sector constitute the majority of companies in Poland and in the European Union countries. However, the structure of domestic enterprises in terms of size and industry differs from the EU average. Taking into account the nature of the business in Poland, more companies operate in trade, and lower in services. However, it should...
-
Au nanoparticles identifiction with the use of AFM Volta potential mapping
Dane BadawczeThe specific physical, chemical and electrochemical electrical properties of gold nanoparticles have led to their extensive use as high-performance chemical and biochemical sensors. The described properties relate to surface plasmon resonance, fluorescence quenching or enhancement, high electrical conductivity and light scattering. The described nanoparticles...
-
SEM images of Mo2Ga2C MAX material
Dane BadawczeIn the dataset, are included SEM images of molybdenum gallium carbide MAX materials.
-
Tax revenues as part of GDP in selected countries
Dane BadawczeThe following dataset contains information on the share of taxes in the GDP of selected countries (Baltic countries - Lithuania, Latvia and Estonia as well as Poland) in the years 2005 - 2020).
-
Long-term hindcast simulation of sea ice in the Baltic Sea
Dane BadawczeThe data set contains the results of numerical modeling of sea ice over a period of 50 years (1958-2007) in the Baltic Sea. A long-term hindcast simulation was performed using a three-dimensional hydrodynamic model PM3D (Kowalewski and Kowalewska-Kalkowska, 2017), a new version of the M3D model (Kowalewski, 1997). A numerical dynamic-thermodynamic model...
-
Hydrodynamic reanalysis of ice conditions in the Baltic Sea using the PM3D model
Dane BadawczeThe dataset contains the results of numerical modeling of sea ice in the Baltic Sea since 1998. A long-term reanalysis was performed using the three-dimensional hydrodynamic model PM3D (Kowalewski and Kowalewska-Kalkowska, 2017), a new version of the M3D model (Kowalewski, 1997). A numerical dynamic-thermodynamic model of sea ice (Herman et al. 2011)...
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured at high temperature range with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 613 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeNonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 613 K was measured by impedance spectroscopy method.