DC and AC Conductivity, Biosolubility and Thermal Properties of Mg-Doped Na2O–CaO–P2O5 Glasses
PublikacjaBioactive glasses have recently been extensively used to replace, regenerate, and repair hard tissues in the human body because of their ability to bond with living tissue. In this work, the effects of replacing Na2O with MgO on the electrical, biosolubility, and thermal properties of the target glass 10Na2O–60P2O5–30CaO (in mol%) were investigated. The electrical properties of the glasses were studied with the impedance spectroscopy...
-
Two-step synthesis of niobium doped Na–Ca–(Mg)–P–Si–O glasses
PublikacjaNiobium doped biosolubility glasses in the Na–Ca–(Mg)–P–Si–O system were prepared by using an untypical two-step synthesis route. The parent glass was melted in air atmosphere at 1350 °C followed by re-melting the glass in Nb crucible with the addition of metallic Mg/Ca powder in the nitrogen atmosphere. The second melting step was carried out at 1450–1650 °C, using an induction furnace. The topography and structure of the obtained...
-
Chitin and derivative chitosan-based structures — Preparation strategies aided by deep eutectic solvents: A review
PublikacjaThe high molecular weight of chitin, as a biopolymer, challenges its extraction due to its insolubility in the solvents. Also, chitosan, as the N-deacetylated form of chitin, can be employed as a primary material for different industries. The low mechanical stability and poor plasticity of chitosan films, as a result of incompatible interaction between chitosan and the used solvent, have limited its industrialization. Deep eutectic...