X-ray diffraction of ZnIn2S4 layers on FTO deposited using PLD
Dane BadawczeData show XRD results for ZnIn2S4 layers deposited using pulsed laser deposition (PLD) on FTO glass.
-
Results of accelerometer measurements in rail passenger transport vehicles
Dane BadawczeAs part of the project, field research was done to better understand how unbalanced accelerations affect passenger comfort in rail transport and to compare this with passengers’ actual, subjective feelings. Data were collected from different types of rail vehicles, like trains and trams, using common mobile devices with MEMS accelerometer sensors.
-
STL files of all-3D-printable electrochemical cell
Dane BadawczeThis dataset contains STL files required for fabrication of an all 3D printed electrochemical cell, that can be used in electroanalytical studies.
-
Correction of far-field measurements obtained in non-anechoic test site
Dane BadawczeThe dataset contains raw and processed measurements of radiation pattern characteristics performed in non-anechoic regime for two geometrically small antenna structures: a spline-parameterized Vivaldi structure and a compact spline-based monopole. The responses have been obtained at the selected frequencies of interest as a function of mentioned structures...
-
Case Study NEB Atlas / part II - Autodesk Forma analysis / King’s Cross, London, UK.
Dane BadawczeThe data present the results of the work on the analysis of modern settlements. The goal of this part of the research was to analyze housing estates already in place in various European cities. Analyses were performed in real time using artificial intelligence, and responses were searched for sun hours, daylight potential, noise, wind, and microclimate....
-
Case Study NEB Atlas / part II - Autodesk Forma analysis / Hammarby-Sjöstad, Stockholm, Sweden.
Dane BadawczeThe data present the results of the work on the analysis of modern settlements. The goal of this part of the research was to analyze housing estates already in place in various European cities. Analyses were performed in real time using artificial intelligence, and responses were searched for sun hours, daylight potential, noise, wind, and microclimate....
-
Case Study NEB Atlas / part II - Autodesk Forma analysis / Västra Hamnen, Malmö, Sweden.
Dane BadawczeThe data present the results of the work on the analysis of modern settlements. The goal of this part of the research was to analyze housing estates already in place in various European cities. Analyses were performed in real time using artificial intelligence, and responses were searched for sun hours, daylight potential, noise, wind, and microclimate....
-
Case Study NEB Atlas / part II - Autodesk Forma analysis / Garnizon district in Gdansk, Poland
Dane BadawczeThe data present the results of the work on the analysis of modern settlements. The goal of this part of the research was to analyze housing estates already in place in various European cities. Analyses were performed in real time using artificial intelligence, and responses were searched for sun hours, daylight potential, noise, wind, and microclimate....
-
Case Study NEB Atlas / part II - Autodesk Forma analysis / Pilestredet Park, Oslo, Norway.
Dane BadawczeThe data present the results of the work on the analysis of modern settlements. The goal of this part of the research was to analyze housing estates already in place in various European cities. Analyses were performed in real time using artificial intelligence, and responses were searched for sun hours, daylight potential, noise, wind, and microclimate....
-
Case Study NEB Atlas / part II - Autodesk Forma analysis / Seestadt Aspern, Vienna, Austria
Dane BadawczeThe data present the results of the work on the analysis of modern settlements. The goal of this part of the research was to analyze housing estates already in place in various European cities. Analyses were performed in real time using artificial intelligence, and responses were searched for sun hours, daylight potential, noise, wind, and microclimate....
-
Case Study NEB Atlas / part II - Autodesk Forma analysis / Oceanhamnen, Helsingborg, Sweden
Dane BadawczeThe data present the results of the work on the analysis of modern settlements. The goal of this part of the research was to analyze housing estates already in place in various European cities. Analyses were performed in real time using artificial intelligence, and responses were searched for sun hours, daylight potential, noise, wind, and microclimate....
-
Case Study NEB Atlas / part II - Autodesk Forma analysis / La Courrouze district in Rennes, France
Dane BadawczeThe data present the results of the work on the analysis of modern settlements. The goal of this part of the research was to analyze housing estates already in place in various European cities. Analyses were performed in real time using artificial intelligence, and responses were searched for sun hours, daylight potential, noise, wind, and microclimate....
-
Case Study NEB Atlas / part II - Autodesk Forma analysis / ZAC de Bonne, Grenoble, France
Dane BadawczeThe data presents the results of work on the analysis of contemporary neighbourhoods. The aim of this part of the research was to analysis housing estates already existed in various cities in Europe. The analyses ware done in real time with AI and powered for key factors such as sun hours, daylight potential, noise, wind, and microclimate. These data...
-
Case Study NEB Atlas / part II - Autodesk Forma analysis / Brunnshög district in Lund, Sweden
Dane BadawczeThe data presents the results of work on the analysis of contemporary neighbourhoods. The aim of this part of the research was to analysis housing estates already existed in various cities in Europe. The analyses ware done in real time with AI and powered for key factors such as sun hours, daylight potential, noise, wind, and microclimate. These data...
-
Case Study NEB Atlas / part II - Autodesk Forma analysis / BedZED, London
Dane BadawczeThe data presents the results of work on the analysis of contemporary neighbourhoods. The aim of this part of the research was to analysis housing estates already existed in various cities in Europe. The analyses ware done in real time with AI and powered for key factors such as sun hours, daylight potential, noise, wind, and microclimate. These data...
-
Case Study NEB Atlas / part II - Autodesk Forma (formerly Spacemaker) / Battersea Power Station Development, London
Dane BadawczeThe data presents the results of work on the analysis of contemporary neighbourhoods. The aim of this part of the research was to analysis housing estates already existed in various cities in Europe. The analyses ware done in real time with AI and powered for key factors such as sun hours, daylight potential, noise, wind, and microclimate. These data...
-
Analytical data on molecular umbrella: cispentacin and molecular umbrella: fluorescent probe conjugates
Dane BadawczeAnalytical data (NMR, MS, FTIR) for nine conjugates of molecular umbrella with cispentacin, Lys(Mca) or Nap-NH2. The conjugates have been rationally designed as potential antifungal agents. 1H NMR and 13C NMR spectra were obtained at 500 MHz Varian Unity Plus spectrometer and the deuterated solvents were used as internal locks. High-resolution mass...
-
Starogard Gdański 2019, Lubichowska – Kościuszki - Chojnicka street - video data - pedestrian, bicycles, vehicles
Dane BadawczeThe data contain video traffic data (pedestrian, cyclists, vehicles) registered at Lubichowska street. Date 13.06.2019, 6:00-18:00. The video camera was installed around intersections at Lubichowska Kościuszki and Chojnicka street. Camera was mounted on 7-meter-high mast.
-
SiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B34/#A33
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...
-
TiN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B48/#A45
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 12 min....
-
TiN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A45/#B48
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 12 min....
-
TiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B41/#A39
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 9 min....
-
TiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A39/#B41
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
SiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B37/#A35
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
SiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A35/#B37
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
CrN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B21/#A21
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 25 min....
-
CrN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A25/#B21
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 9 min....
-
TiN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A45/#A47
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 20 min. The test...
-
TiN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A45/#B45
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 90 min. The test...
-
TiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B39/#A41
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...
-
TiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A41/#B39
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The...
-
SiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A33/#B34
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...
-
CrN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B22/#A23
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 6 min. The test...
-
CrN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A23/#B22
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 12 min. The...