A microwave method was used for the synthesis of TiO2-CuO oxide systems. A detailed investigation was made of the effect of the molar ratio of components (TiO2:CuO=9:1, 7:3, 5:5, 3:7, 1:9) on the crystalline structure and morphology. Transmission electron microscopy (TEM) confirmed the presence of octahedral and rod-shaped titania particles and sheet copper(II) oxide particles; moreover, HRTEM analysis indicated the presence of...

Core-interlayer-shell Fe3O4/SiO2/TiO2, CoFe2O4/SiO2/TiO2 and BaFe12O19/SiO2/TiO2 magnetic photocatalysts were obtained. A water-in-oil microemulsion system with suitable surfactants was used for functionalization of the magnetic core with silica interlayer and TiO2-based photocatalyst. Uncoated and coated particles were characterized by electrophoretic meaurements, X-ray diffractometry (XRD), scanning electron microscopy (SEM),...

A TiO2–ZnO binary oxide system (with molar ratio TiO2:ZnO = 8:2) was synthesized by a hydrothermal method, assisted by calcination at temperatures of 500, 600 and 700 °C, using zinc citrate as the precursor of ZnO. The morphology (SEM, TEM), crystalline structure (XRD, Raman spectroscopy), diffuse reflectance spectra (DRS), chemical surface composition (EDXRF), porous structure parameters (low-temperature N2 sorption) and characteristic...