Thermgravimetric analysis (TGA) data of cement pastes containing pristine and silica-coated bismuth oxide and gadolinium oxide particles - Open Research Data - Bridge of Knowledge

Your account

login

Search

Thermgravimetric analysis (TGA) data of cement pastes containing pristine and silica-coated bismuth oxide and gadolinium oxide particles

Description

Thermogravimetric (TGA) data of cement pastes after 2, 7 and 28 days. Samples designations: Control, BG, BG-A and BG-B are associated with the specimen names in the associated publication.

Control - Pristine Portland cement paste

BG - Cement paste containing 10 wt% replacement of cement with Bi2O3+Gd2O3 structures

BG-A -  Cement paste containing 10 wt% replacement of cement with silica-coated Bi2O3+Gd2O3 (synthesis method A) structures

BG-B -  Cement paste containing 10 wt% replacement of cement with silica-coated Bi2O3+Gd2O3 (synthesis method B) structures

Thermogravimetric analysis (TGA) of cement pastes after 2 d, 7 d and 28 d of curing was performed using TA Instruments 5500 in nitrogen, with a heat rate 10 °C/min, up to 1000 °C. To perform the measurement, the cubic specimens were crushed and immersed in the solvent (isopropanol) to stop the hydration process for 1 h. Afterward, the material was dried using a vacuum dryer (40 °C) and milled to fine powder. 

Each folder contains raw data in *.tri format accesible using Trios software (5.4.0.300) - https://www.tainstruments.com/support/software-downloads-support/downloads/ and *.txt file

Dataset file

TGA.zip
31.7 MB, S3 ETag e5a93f9fe2a421a050e04eec67a34840-1, downloads: 12
The file hash is calculated from the formula
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.

Example script for calculation:
https://github.com/antespi/s3md5
download file TGA.zip

File details

License:
Creative Commons: by 4.0 open in new tab
CC BY
Attribution
Raw data:
Data contained in dataset was not processed.
Software:
Trios 5.4.0.300

Details

Year of publication:
2024
Verification date:
2024-03-04
Dataset language:
English
Fields of science:
  • materials engineering (Engineering and Technology)
  • chemical engineering (Engineering and Technology)
  • civil engineering, geodesy and transport (Engineering and Technology)
DOI:
DOI ID 10.34808/fx5a-cp08 open in new tab
Funding:
Verified by:
West Pomeranian University of Technology in Szczecin

Keywords

References

Cite as

Authors

seen 61 times