This work presents some numerical results concerning simulation of failure of laminate composite specimens. In the article two tests to determine ultimate strength in an orthotropic layer, are considered: tension (TT1) and compression (TC1) test. The outcome is compared with experimental data provided by [9,10].

Mechanical behaviour was compared for glass/ polyester laminates manufactured in the boatbuilding plant using three methods: hand lay-up, vacuum bagging, infusion. Specimens were tested in dry condition and following accelerated water immersion test (70°C- corresponding to the exposure of 30 years at 19°C). In three point bending test 40-50% reduction in laminate strength was observed due to water immersion. The highest degradation...

Przedstawiono przegląd sposobów poprawy tolerancji udarów w nowoczesnych laminatach polimerowych. Są to: wytrzymalsze i bardziej ciągliwe materiały osnowy, dobieranie odpowiedniego powiązania osnowy i włókien, stosowanie włókien w postaci tkanin, zszywanie preform z wielu warstw tkanin, łączenie włókien ciągłych w preformy za pomocą kompozytowych szpilek, stosowanie tkanin NCF z włókien ciągłych łączonych na grubości dodatkowym...

The paper presents a FEM simulation of failure of laminate subjected to the three point bending. The numeri-cal model is based on the equivalent single layer approach with 6-paramater non-linear shell theory kinematics. It is implemented in the non-commercial FEM code. The failure initiation is detected with the use of Tsai-Wu criterion. After the failure onset the progressive failure process is modelled through the appropriate...

Zbadano wpływ kompatybilizatorów na morfologię i właściwości mechaniczne mieszanin PE/PA. Okreslono właściwości recyklatu uzyskanego z odpadów barierowej folii wielowarstwowej zawierającej 80% PE i 20% PA. Po dodaniu kompatybilizatorów układ stał się bardziej jednorodny, zmniejszeniu uległy domeny PA oraz poprawiły się właściwości mechaniczne.