The ferromagnetic superconductor Y9Co7 was chemically doped to yield the solid solution Y9Co7-xPdx for 0 < x < 0.4. The lattice parameter a does not depend on x, whereas c increases with increasing Pd content up to x ¼ 0.2, the palladium solubility limit. The transition from ferromagnetism (TC ¼ 4.25 K) to superconductivity (Tsc ¼ 2.4 K) was observed only for the parent Y9Co7 compound. For the lowest tested Pd doping level (x ¼...

The ac magnetic susceptibility of a single crystal sample of the compound Y9Co7 has been measured in applied dc fields ranging from 0–6.7 kOe by utilizing a tunnel diode resonator circuit. In agreement with previous measurements on this material, a superconducting transition has been observed to occur at TSC ≈ 2.5 K. A broad maximum has been observed in the zero field susceptibility measurements from 2.5 K < T < 8 K and its behavior...

We report the basic physical properties of monoclinic Y8Co5 determined by means of magnetic susceptibility, electrical resistivity, and specific heat measurements. The crystal structure of Y8Co5 is monoclinic (P21/c) with lattice parameters a = 7.0582(6) Å, b = 7.2894(6) Å, c = 24.2234(19) Å, and β = 102.112(6)° as refined by using synchrotron powder x-ray diffraction data. The compound shows temperature independent paramagnetism...