Praca dotyczy opracowywania nowych metod badań adhezji elastycznych klejów, na przykładzie akrylowego kleju "mastic" i porównawczo kleju epoksydowego, w oparciu o mechanikę pękania. Artykuł przedstawia wyniki badań przeprowadzonych dla złącza asymetrycznego, czyli np. składającego się z dwóch różnych materiałów lub tych samych materiałów o różnej grubości. Metody wyznaczania podstawowych parametrów w próbach mechaniki pękania przeprowadzanych...

When bonded joint is subjected to mode I fracture loading, the adhesive joints analytical solutions treats the adhesive layer, usually, as not existing or 1D Hooke elastic layer. In the case of 1D elastic layer, represented as Hookes spring element, is acting, only, in direction contrary to the applied load. Basing on the information yielded from sensitive laser profilometry technique, where deflections of bonded part of the joint...

Slow crack propagation in adhesive bonded joints has been characterised using an asymmetric wedge test. Crack position was evaluated from strain gauge measurements, both in the debonded partof the joint and in the bonded zone. Test temperature was changed during loading, giving insight into bond evolution. The technique allows accurate, and virtually continuous, determination of crack position to be made, and therefore the evaluation...

The effects of variability of intrinsic adhesion within a joint have been studied using a single cantilever beam (SCB) test. Fracture energy was found not to be a simple function of relative areas of 2 surface pre-treatments: a 'weak' zone decreased strength more than expected from simple, additive considerations. By severing the adhesive along the strong-weak transition, fracture energy increased.The prior antagonist effect appears...

Standard tests of adhesively bonded specimens are likely to produce heterogeneous stress distribution along the crack front and its vicinity. High separation rate mode I dominated fracture test is performed.Observation of post mortem fractured surfaces with an optical microscope reveals characteristic features of mixed mode I/III fracture near the sides of the specimen but not in the middle. At first, finite elements calculations...