A study on a novel material - manganese borosilicate glass without alkali metals, was reported. It was found that the obtained samples containing high amount of manganese oxide (60MnO–xSiO2–(40 − x)B2O3, x = 5, 10, 15, 20 and 30 mol%) were amorphous and homogeneous. XPS measurements showed that most of manganese ions are at oxidation level of Mn2 + ions and the mean oxidation level slightly moves toward higher value, with increasing...

Electrical properties of beryllium-alumino-tellurite glasses and glass–ceramics doped with iron ions were studied using impedance spectroscopy. The conductivity was measured over a wide frequency range from 10 mHz to 1 MHz and the temperature range from 213 to 473 K. The D.C. conductivity values showed a correlation with the Fe-ion concentration and ratio of iron ions on different valence states in the samples. On the basis of...

Nonlinear a.c. impedance measurements were performed in Cu2O-Al2O3-SiO2 glass in wide frequency range. The obtained results shows that a large nonlinearity in the impedance signal is observed at moderate electric fields of an order 1V/mm. The contents of the third harmonics reaches about 10% and strongly depends on temperature and frequency. The investigated glass exhibits mixed electronic-ionic conductivity. Electronic conduction...

The structure and electrical properties of manganese borosilicate glasses of a composition of xMnO-(0.8-x)SiO2-(0.2)B2O3 (x=0.4, 0.5 and 0.6 in mol) were investigated by impedance spectroscopy, SEM, XRD and confocal microscopy methods. The influence of composition on the glass structure and electrical properties was discussed. A separation of two amorphous phases was observed and it was concluded that one phase is SiO2-rich and...

V2O5–TeO2 glass–ceramics (VTGC) were prepared by controlled annealing of the V2O5–TeO2 glass (VTG), which illustrates a parent glass matrix with a single charge carrier. The annealing proceeded at six temperatures selected between the glass transition and the maximum of the frst crystallization process to obtain various nanocrystallite sizes. Heat treatment caused an increase in DC conductivity by 2.5–3.5 (250–285 °C) order of...