Complex modulus of Cement Bitumen Treated Material Mixture C3E5.5 (over 28 days of curing at 20C)

Description

Dataset presents data of complex modulus determined for cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement and 5.5% emulsion (C3E5.5). Mixture was designed according to Polish requirements for the base course of pavement. Mixture contains 60% of RAP material. Specimen size: f=100 mm, h=130 mm. Specimen were cured in laboratory for more than 28 days at temperature of +20°C and relative humidity range from 40-70%.

Data was obtained in the Simple Performance Tester (IPC global) for 3 temperatures (+4°C, +20°C and +40°C). Cyclic compression test was used acc. to AASHTO TP79 standard). Gauge length was 70 mm. Three replicates were tested. 

Test load was selected as haversine compression with constant target strain range – 40-50µstrain.

Dataset file

000_DATASET (SPT Dynamic modulus test).xlsx
21.2 kB, S3 ETag dfd7d1f94faa609da436e361fe1a8167-1, downloads: 54
The file hash is calculated from the formula
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.

Example script for calculation:
https://github.com/antespi/s3md5

File details

License:
Creative Commons: by 4.0 open in new tab
CC BY
Attribution

Details

Year of publication:
2024
Verification date:
2024-04-05
Creation date:
2024
Dataset language:
English
Fields of science:
  • civil engineering, geodesy and transport (Engineering and Technology)
DOI:
DOI ID 10.34808/7vac-zp58 open in new tab
Funding:
Series:
Verified by:
Gdańsk University of Technology

Keywords

Cite as

Authors

seen 78 times