Cyclic deformation and fracture behaviour of additive manufactured maraging steel under variable-amplitude loading
Abstract
The cyclic deformation and fracture behaviour of 18Ni300 maraging steel produced by laser beam powder bed fusion is studied under variable-amplitude loading. The tests were conducted under fully-reversed strain-controlled conditions with a loading sequence comprising three ascending cycles and three descending cycles repeated sequentially until failure. After the tests, fracture surfaces were examined using height and volume surface topography parameters to characterise the fractographic features. Fracture surfaces were also analysed through scanning electron microscopy to identify the main failure modes. Fatigue life was predicted by using the Smith-Watson-Topper and the Basquin-Coffin-Manson models with the Palmgren-Miner damage rule. The former approach was more accurate leading to mean errors close to zero. The values of the kurtosis parameter obtained from both sides of the fracture surfaces correlated well with the fatigue life. SEM analysis showed a mixed ductile-brittle mode of fracture with a predominance of brittle fracture. Crack initiation occurred from manufacturing defects located at the surface or near-surface.
Citations
-
2
CrossRef
-
0
Web of Science
-
2
Scopus
Authors (5)
-
Zbigniew Marciniak
-
Ricardo Branco
-
C. Malça
Cite as
Full text
full text is not available in portal
Keywords
Details
- Category:
- Articles
- Type:
- artykuły w czasopismach
- Published in:
-
THEORETICAL AND APPLIED FRACTURE MECHANICS
no. 129,
ISSN: 0167-8442 - Language:
- English
- Publication year:
- 2024
- Bibliographic description:
- Marciniak Z., Branco R., Macek W., Dobrzyński M., Malça C.: Cyclic deformation and fracture behaviour of additive manufactured maraging steel under variable-amplitude loading// THEORETICAL AND APPLIED FRACTURE MECHANICS -Vol. 129, (2024), s.104207-
- DOI:
- Digital Object Identifier (open in new tab) 10.1016/j.tafmec.2023.104207
- Sources of funding:
-
- Free publication
- Verified by:
- Gdańsk University of Technology
seen 73 times
Recommended for you
Strain energy density and entire fracture surface parameters relationship for LCF life prediction of additively manufactured 18Ni300 steel
- W. Macek,
- R. Branco,
- J. de Jesus
- + 4 authors