Effects of V2O5 Additive on Structure and Dielectric Properties of BiNbO4 Ceramics

Abstract

Goal of the present research was to investigate the influence of V2O5 additive on the structure and dielectric properties of BiNbO4 ceramics. To fabricate BiNbO4 ceramics with V2O5 added the solid state reaction route and pressureless sintering was utilized. Thus obtained ceramics was characterized in terms of its microstructure (SEM), chemical composition (EDS), phase composition and crystalline structure (X-ray phase and structural analysis, respectively). Also dielectric properties in both temperature and frequency domains were investigated. The impedance spectroscopy was utilized for dielectric characterization and the measurements of complex impedance were performed within the frequency range =10Hz–1MHz and temperature range T =RT-550C. It was found that V2O5 additive changed slightly lattice parameters of BiNbO4 ceramics, decreased porosity of samples and revealled relaxation phenomena within the frequency ranges =102–103 Hz and =105–106 Hz at temperature T>285C.

Citations

  • 0

    CrossRef

  • 0

    Web of Science

  • 0

    Scopus

Cite as

Full text

download paper
downloaded 7 times
Publication version
Accepted or Published Version
DOI:
Digital Object Identifier (open in new tab) 10.2478/amm-2013-0180
License
Creative Commons: CC-BY-NC open in new tab

Keywords

Details

Category:
Articles
Type:
artykuły w czasopismach
Published in:
ARCHIVES OF METALLURGY AND MATERIALS no. 58, pages 1387 - 1390,
ISSN: 1733-3490
Language:
English
Publication year:
2013
Bibliographic description:
Lisińska-Czekaj A., Czekaj D., Osińska K., Adamczyk M.: Effects of V2O5 Additive on Structure and Dielectric Properties of BiNbO4 Ceramics// ARCHIVES OF METALLURGY AND MATERIALS -Vol. 58,iss. 4 (2013), s.1387-1390
DOI:
Digital Object Identifier (open in new tab) 10.2478/amm-2013-0180
Verified by:
Gdańsk University of Technology

seen 81 times

Recommended for you

Meta Tags