In this paper, the entire fracture surface approach was used to assess an effect of 280,000 h of exploitation under internal pressure of 2.9 MPa and high temperature of 540 °C on the fatigue response of 10H2M (10CrMo9–10) power engineering steel. The mechanical testing was carried out on the hourglass specimens produced from the as-received, unused pipeline and the same material after long-time exploitation. The uniaxial tensile tests were performed to establish the stress amplitude for subsequent force controlled, fatigue testing in the range from ±250 MPa to ±400 MPa under the frequency of 20 Hz. Since the exploited 10H2M steel was characterized by significantly lower mechanical properties, different damage mechanisms responsible for specimen failure were revealed through fracture surface analysis. The fracture surface topography evaluation was performed with a 3D non-contact measuring system. It was found, that the exploitation state has a strong impact on the fatigue life and fracture characteristics since the significant drop in lifespan of about 300 %–400 % was found for the material after prolonged service. Finally, the proposed surface topography parameter was related to the stress amplitude in order to estimate the fatigue life for the steel in question.
Citations
-
1
CrossRef
-
0
Web of Science
-
2
Scopus
Authors (4)
-
Mateusz Kopec
-
Zbigniew Kowalewski
Cite as
Full text
full text is not available in portal
Keywords
Details
- Category:
- Articles
- Type:
- artykuły w czasopismach
- Published in:
-
JOURNAL OF CONSTRUCTIONAL STEEL RESEARCH
no. 221,
ISSN: 0143-974X - Language:
- English
- Publication year:
- 2024
- Bibliographic description:
- Macek W., Kopec M., Laska A., Kowalewski Z.: Entire fracture surface topography parameters for fatigue life assessment of 10H2M steel// JOURNAL OF CONSTRUCTIONAL STEEL RESEARCH -, (2024), s.108890-
- DOI:
- Digital Object Identifier (open in new tab) 10.1016/j.jcsr.2024.108890
- Sources of funding:
-
- Free publication
- Verified by:
- Gdańsk University of Technology
seen 45 times
Recommended for you
Fatigue fracture morphology of AISI H13 steel obtained by additive manufacturing
- W. Macek,
- R. F. Martins,
- R. Branco
- + 3 authors
Fracture surface topography investigation and fatigue life assessment of notched austenitic steel specimens
- W. Macek,
- G. Robak,
- K. Żak
- + 1 authors
Effect of bending-torsion on fracture and fatigue life for 18Ni300 steel specimens produced by SLM
- W. Macek,
- R. Masoudi Nejad,
- S. Zhu
- + 5 authors