La-modified Bi4Ti3O12 is a typical ferroelectric, piezoelectric and electro-optic material, having relatively low coercive field, low dielectric constant, high Curie temperature and high breakdown strength. Goal of the present research was to apply mixed oxide method for fabrication of BiTLax ceramics, study its chemical composition, crystalline structure and microstructure. The compound BiTLax for x=0, 0.25, 0.5, 0.75 ceramic powders were prepared from mixture of oxides by a solid state reaction at T=1000°C for t=3h. Ceramic powders of BiTLax were next press and the compacts were sintered by the free sintering at temperature T=1000°C with the soaking time t=2h. A crystal structure Bi-layered structured of ferroelectrics was confirmed by a X-ray diffraction. It was found that La-doped BiT ceramics sintered at T=1000°C adopted the monoclinic symmetry. Influence of La-doping on chemical composition and microstructure of BiTLa ceramics was studied by scanning electron microscopy HITACHI S-4700 and energy dispersion spectroscopy.
Citations
-
0
CrossRef
-
0
Web of Science
-
0
Scopus
Authors (5)
-
Henryk Bernard
-
Katarzyna Osińska dr
-
Jolanta Dzik dr
Cite as
Full text
full text is not available in portal
Keywords
Details
- Category:
- Articles
- Type:
- artykuły w czasopismach
- Published in:
-
MATERIALS SCIENCE FORUM
pages 105 - 110,
ISSN: 0255-5476 - Language:
- English
- Publication year:
- 2012
- Bibliographic description:
- Lisińska-Czekaj A., Bernard H., Osińska K., Dzik J., Czekaj D.: Fabrication of La-Doped Bi4Ti3O12 Ceramics// MATERIALS SCIENCE FORUM -,iss. 730-732 (2012), s.105-110
- DOI:
- Digital Object Identifier (open in new tab) 10.4028/www.scientific.net/msf.730-732.105
- Verified by:
- Gdańsk University of Technology
seen 105 times
Recommended for you
X-RAY DIFFRACTION STUDY OF BISMUTH LAYER-STRUCTURED MULTIFERROIC CERAMICS
- A. Lisińska-Czekaj,
- D. Czekaj,
- B. Garbarz
- + 2 authors
STUDY OF CuO AND V2O5 EFFECT ON IR SPECTRA OF POLYCRYSTALLINE BISMUTH NIOBATE
- I. Kuźniarska-Biernacka,
- A. Lisińska-Czekaj,
- D. Czekaj