Aim of the present research was to fabricate and study crystal structure and phase composition of Bi5FeTi3O15 (BTFO) ceramics exhibiting Aurivillius - type structure. By means of simultaneous thermal analysis and X-ray diffraction analysis the process of synthesis of BTFO ceramics has been studied. Mixed oxide method followed by pressureless sintering was used for ceramics preparation. Three endothermic thermal effects have been revealed on heating the stoichiometric mixture of initial powder oxides within the temperature range T=(700 – 1200)C, while only one strong endothermic peak was found on heating the powder after calcination. The weak endothermic peaks were ascribed to the melting points of intermediate surface phases based on Bi2O3-rich phase formed at low temperature. X-ray diffraction studies have shown that BFTO ceramics consisted of Bi5FeTi3O15 and Bi4Ti3O12 phases in amount of 88.3% and 11.7% (weight fraction), respectively.
Citations
-
4
CrossRef
-
0
Web of Science
-
6
Scopus
Authors (3)
-
Julian Plewa
Cite as
Full text
full text is not available in portal
Keywords
Details
- Category:
- Articles
- Type:
- artykuły w czasopismach
- Published in:
-
Ciencia & Tecnologia dos Materiais
no. 29,
pages e210 - e214,
ISSN: 0870-8312 - Language:
- English
- Publication year:
- 2017
- Bibliographic description:
- Lisińska-Czekaj A., Plewa J., Czekaj D.: Synthesis and structure of Bi 5 FeTi 3 O 15 ceramics// Ciencia & Tecnologia dos Materiais -Vol. 29,iss. 1 (2017), s.e210-e214
- DOI:
- Digital Object Identifier (open in new tab) 10.1016/j.ctmat.2016.04.006
- Verified by:
- Gdańsk University of Technology
seen 110 times
Recommended for you
X-RAY DIFFRACTION STUDY OF BISMUTH LAYER-STRUCTURED MULTIFERROIC CERAMICS
- A. Lisińska-Czekaj,
- D. Czekaj,
- B. Garbarz
- + 2 authors
Influence of Processing Conditions on Crystal Structure of Bi6Fe2Ti3O18 Ceramics
- A. Lisińska-Czekaj,
- M. Lubina,
- D. Czekaj
- + 3 authors