XPS (X-ray photoelectron spectroscopy) of titanium dioxide coated nickel foams and heated 400,500, 600C
Open Research DataThis data set contains XPS spectra recorded for nickel foams coated with titanium dioxide and heated at 400, 500 and 600 degrees celcius.
-
SEM (Scanning Electron Microscopy) and SEM-EDS (Scanning Electron Microscopy with Energy Dispersive X-ray Spectroscopy) images of nickel (Ni) foam as received, after photocatalysis and after oxidation at 500_C.
Open Research DataThis dataset contains SEM (Scanning Electron Microscopy) and SEM-EDS (Scanning Electron Microscopy with Energy Dispersive X-ray Spectroscopy) images of Ni (nickel) foam as received from the supplier, after photocatalytic treatment and after oxidation at 500C. The detailed equipment and measurement data was described in "readme SEM.txt" file
-
AFM (Atomic Force Microscopy) analysis of surface topography loaded with nickel nanoparticles.
Open Research DataThis dataset presents AFM (Atomic Force Microscopy) images depicting the surface topography loaded with nickel powdered nanoparticles. The detailed equipment and measurement data was described in "AFM readme.txt" file
-
Photocatalytic degradation of acetaldehyde in high temperature reaction chamber
Open Research DataThis dataset contains chromatograms recorded during the decomposition of acetaldehyde in a high-temperature reaction chamber under UV irradiation using TiO2 (titanium dioxide) as photocatalysts. It includes data on the influence of flow rate, TiO2 (titanium dioxide) filling the entire reactor, a thin layer of TiO2 (titanium dioxide) supported on KBr...
-
Photocatalytic decomposition of acetaldehyde over TiO2 (titanium dioxide) supported on nickel foam and Ni-doped (nickel-doped) TiO2
Open Research DataThis dataset contains chromatograms recorded during the decomposition of acetaldehyde in a high-temperature reaction chamber under UV irradiation using as photocatalytic systems TiO2 (titanium dioxide) supported on nickel foam, TiO2 supported on oxidized nickel foam and TiO2 doped by metallic nickel (Ni) powder. The detailed equipment and measurement...
-
XPS-Ni foam as received, after photocatalysis and after oxidation at 500_C.
Open Research DataThis dataset contains XPS spectra recorded for nickel foam as received from supplier, after photocatalytic process and after oxidation at 500C. Each set contains: survery spectrum, O1, C1s, Ni2p. The detailed equipment and measurement data was described in "readme XPS.txt" file
-
SEM-EDS images of expanded polystyrene spheres coated with silicon dioxide (SiO2) and/or titanium dioxide (TiO2)
Open Research DataData contain SEM and SEM-EDS images of expanded polystyrene spheres coated with silicon dioxide (SiO2) and/or titanium dioxide (TiO2). The detailed equipment and measurement data was described in measurement info.txt file.
-
SEM - Expanded polystyrene coated by TiO2 or SiO2-TiO2
Open Research DataData contain SEM images taken in SEM Hitachi SU8000 with voltage of 5.0 kV. SEM images show expanded plystyrene spheres coated by a thin layer of TiO2 or bilayer SiO2-TiO2.
-
SEM of TiO2 heated at 400-600oC in Ar or H2
Open Research DataData contain some SEM images of TiO2 taken after its heat treatment in Ar or H2 at 400-600oC. Treated TiO2 was crystalline anatase phase with 3-4 % of rutile nclei.
-
XPS-TiO2 heated in H2
Open Research DataThese XPS spectra were recorded for TiO2 heat-treated at 450-600oC in H2. Surface oxygen groups were determined. Deconvolution of Ti 2p peak allowed to determine Ti3+ on the titania surface.