The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 900 deg.C in hydrogen
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 1000 deg.C in hydrogen
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 1100 deg.C in hydrogen
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials after reduction at 900 deg.C in hydrogen
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...