Results of nanoindentation test to calculate residual stress in an eyelet of undercarriage drag strut after laser treatment
Open Research DataIn order to determine the residual stress in the laser-processed an eyelet of undercarriage drag strut, a nanoindentation test was performed before and after stress relief annealing. For this purpose, after the hardness test, the sample was subjected to stress relief annealing at 270 °C for 2 hours. Annealing was performed in a vacuum furnace. Hardness...
-
SEM examination of surface layer of C45 steel after grinding on defferent depth
Open Research DataFerrite examination for the medium carbon structural steel with low content of Mn, Si, Cu, Cr and Ni after its grinding to a depth of 2 µm, 8 µm, 14 µm and 20 µm, at constant wheel circumferential speed of vs = 25 m/s and constant feed rate vft = 1 m/min. It was shown that the grinding of C45 steel causes strong work hardening of ferrite in surface...
seen 733 times