Investigation of low-temperature cracking in newly constructed high-modulus asphalt concrete base course of a motorway pavement
PublicationThe paper presents the issue of low-temperature transverse cracks which have developed in newly constructed base courses made of high-modulus asphalt concrete mix (HMAC). Numerous transverse cracks developed in the analysed HMAC base during the winter season before the pavement was actually completed, both at the transverse joint locations and in the areas between them. This had not happened so far on such a scale during road construction...
-
Effect of polymer fibres reinforcement on selected properties of asphalt mixtures
PublicationThe paper presents selected results of the research program concerning fibre reinforced asphalt concrete. Aramid-polyalphaolefin fibres was used in this study. Selected properties responsible for low temperature cracking and resistance to permanent deformation are presented in this paper. Low temperature cracking susceptibility was evaluated with the results obtained from bending test of rectangular beams with constant rate of...
-
New polish catalogue of typical flexible and semi-rigid pavements
PublicationThe paper covers the following topics important for the development of the new Polish Catalogue of typical flexible and semi-rigid pavements: reasons for preparing the new issue of the Catalogue of typical flexible and semi-rigid pavements, items introduced in the new issue, organise the terminology related to pavements, design traffic calculations and new equivalent axle load factors,...
-
Initial Field Validation of Poroelastic Pavement Made with Crumb Rubber, Mineral Aggregate and Highly Polymer-Modified Bitumen
PublicationTire/road noise in most driving conditions dominates other sources of traffic noise. One of the most efficient ways of reducing tire/road noise is to use the so-called “low noise pavement”. According to numerous studies, at present, poroelastic road pavement that is composed of rubber and mineral aggregate and polyurethane or bituminous binder gives the best noise reduction up to 12 dB. Unfortunately, there are many problems with...
-
Influence of Selected Warm Mix Asphalt Additives on Cracking Susceptibility of Asphalt Mixtures
PublicationWarm mix asphalt (WMA) has been widely accepted as a future asphalt paving technology. Besides clear advantages, there are still some concerns regarding durability and long-term performance of pavements made with this type of asphalt mixtures. One of the most important issues is low temperature behaviour of WMA because certain additives used for temperature reduction can aect bitumen properties. This paper presents the evaluation...
-
Investigation of Acoustic Properties of Poroelastic Asphalt Mixtures in Laboratory and Field Conditions
PublicationMeasures for the improvement of acoustic conditions in the vicinity of roads include the construction of pavement structures with low-noise surfaces with optimal macrotexture and the highest possible sound absorption coefficient. Laboratory evaluation of acoustic properties of a designed asphalt mixture before its placement in the pavement is a good solution. Currently, the most popular method for the determination of the sound...
-
Influence of selected WMA additives on viscoelastic behaviour of asphalt mixes and pavements
PublicationWarm mix asphalt additives are effective in decreasing production, laying and compaction temperatures of asphalt mixes. However, there are still questions concerning influence of warm mix additives on properties of asphalt mixes and pavement performance. This paper presents results of the comprehensive research of viscoelastic behaviour of asphalt mixes and pavement structures with layers made with warm mix asphalt additives at...
-
Numerical simulation of asphalt mixtures fracture using continuum models
PublicationThe paper considers numerical models of fracture processes of semi-circular asphalt mixture specimens subjected to three-point bending. Parameter calibration of the asphalt mixture constitutive models requires advanced, complex experimental test procedures. The highly non-homogeneous material is numerically modelled by a quasicontinuum model. The computational parameters are averaged data of the components, i.e. asphalt, aggregate...
-
Influence of bitumen type on cracking resistance of asphalt mixtures used in pavement overlays
PublicationCracking is one of the predominant distresses occurring in flexible pavements, especially in old pavements that were rehabilitated with an asphalt overlay. In such cases asphalt mixtures should be designed to ensure high resistance to reflective cracking because new asphalt layers are exposed to existing cracks of the old pavement. The nature of these cracks can be various (transverse, longitudinal as well as crazy cracking). One...
-
The Impact of Homogeneity of High Modulus Asphalt Concrete Layer on Low-Temperature Cracking
PublicationDuring winter season of 2012 numerous transverse cracks developed in high-modulus asphalt concrete (HMAC) base of newly constructed motorway. Pavement cracked both in transverse joint locations and in the area between them. Research which was conducted during investigation of the causes and mechanisms of cracking consisted of: field examination, laboratory testing of specimens cored out of the existing pavement, computational analyses...
-
Optimisation and field assessment of poroelastic wearing course bond quality
PublicationCompared to typical asphalt mixtures, poroelastic mixtures are characterised by high porosity and high flexibility, which are desirable for traffic noise reduction. However, the same properties increase the risk of debonding from the lower layer, which is a significant source of premature damage. The study investigates which of the factors – tack coat agent, type and texture of the lower layer – have the greatest impact on interlayer...
-
Fatigue Performance of Double-Layered Asphalt Concrete Beams Reinforced with New Type of Geocomposites
PublicationThe reinforcement of asphalt layers with geosynthetics has been used for several decades, but proper evaluation of the influence of these materials on pavement fatigue life is still a challenging task. The presented study investigates a novel approach to the reinforcement of asphalt layers using a new type of geogrid composite, in which square or hexagonal polypropylene stiff monolithic paving grid with integral junctions is bonded...
-
The effect of multiaxial geocomposite reinforcement on fatigue performance and crack propagation delay in double-layered asphalt beams
PublicationThe presented study investigates the effect of a recently developed multiaxial geocomposite made of polypropylene geogrid and non-woven fabric on the delay of crack propagation, based on four-point bending tests of large asphalt concrete beams – both for reinforced and non-reinforced specimens. Several approaches are described in this study, including analysis of stiffness modulus decrease and analysis of crack propagation using...
-
The use of a two-phase Monte Carlo material model to reflect the dispersion of asphalt concrete fracture parameters
PublicationThe work covers comprehensive laboratory tests of semi-circular bending (SCB) of asphalt concrete samples. The results of two test series, including four and 32 SCB specimens, indicate a substantial scatter of force–deflection (F-d) histories. The numerical analysis is aimed to reflect the maximum breaking load and fracture energy of the samples, pointing out their random character. The original simulation-based fictitious Monte...
-
Bitumen-Based Poroelastic Pavements: Successful Improvements and Remaining Issues
PublicationThis article presents the development process of designing and testing poroelastic pavement based on highly polymer-modified bitumen. Poroelastic wearing course was composed of mineral and rubber aggregate mixed with highly polymer-modified bitumen, in contrast to previous trials, during which polyurethane resins were mainly used as binder, which led to several serious technological problems concerning difficult production, insufficient...
-
The Use of Direct Shear Test for Optimization of Interlayer Bonding Under a Poroelastic Layer
PublicationPoroelastic Road Surfaces (PERS) are characterised by porous structure with air void content of 20% or higher and stiffness almost 10 times lower than that of a standard asphalt course. Such properties enable noise reduction by up to 12 dB in comparison to SMA 11 mixture. However, the disadvantage of a poroelastic pavement is its low durability, which partially results from delamination from the lower layer. The paper aims to investigate...
-
Monte Carlo simulations of the fracture resistance degradation of asphalt concrete subjected to environmental factors
PublicationThe paper presents the results of laboratory tests of SCB (semi-circular beam) samples of asphalt concrete, subjected to the destructive effect of water and frost as well as the aging processes. The determined values of material parameters show significant dispersions, which makes the design of mixtures difficult. Statistical analysis of the test results supplemented by computer simulations made with the use of the proprietary...
-
Design of poroelastic wearing course with the use of direct shear test
PublicationPoroelastic Road Surfaces (PERS) are characterized by porous structure with at least 20% of air void content and stiffness almost 10 times lower than typical asphalt course. Such properties enable noise reduction up to 12 dB in comparison to SMA 11 mixture. However, the main disadvantage of previously used poroelastic mixtures, based on resin type binders, was their low durability, which resulted in raveling and delamination from...
-
The statistical impact of experimental result scatter of asphalt mixtures on their numerical modelling
PublicationThe paper presents selected test results of asphalt mixture conducted in low temperatures. The obtained parameters are highly diverse. It concerns ultimate breaking loads, stiffness parameters related to Young's modulus but also the fracture course. Statistical analysis upon the results makes it possible to relevantly estimate the material-defining parameter values. Such a random approach leads to the mean values of breaking and...
-
Laboratory fatigue assessment of large geocomposite-reinforced double-layered asphalt concrete beams
PublicationGeosynthetic reinforcement of asphalt layers has been used for several decades. Evaluation of the influence of these materials on pavement fatigue life is still ongoing, especially for new types of geocomposites. This paper presents the evaluation of fatigue performance of large asphalt concrete beams reinforced with a new type of composite in which square or hexagonal polypropylene stiff monolithic paving grid with integral junctions...