Chemical diffusion coefficient of oxygen (D*) of the SrxTi0.30Fe0.70O3 (x=0.90, 0.95 and 1.00) at different temperatures

Description

In this dataset are presented D* values designated based on the electrical conductivity relaxation (ECR) mesurement of the SrxTi0.30Fe0.70O3 (x=0.90, 0.95, 1.00) materials. The applied temperatures were 800 °C, 750 °C, 700 °C, 650 °C, and 600 °C. Studies were performed in a small tube furnace (internal diameter ~20 mm) with 64 cm³ gas volume. During the four-point single frequency electrochemical impedance spectroscopy measurement (1 Hz), the oxygen partial pressures were changed from 20% O₂ to 10% O₂ and the reverse.

D* was designated for both cases incorporation and removal of oxygen.

Dataset file

D vs temp.xlsx

8.8 kB, S3 ETag 90e1d26416228931ca90aecd3395c9b3-1, downloads: 8

The file hash is calculated from the formula
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.

Example script for calculation:
https://github.com/antespi/s3md5

download

File details

License:: open in new tab

CC BY

Attribution

Details

Year of publication:

2022

Verification date:

2024-11-27

Dataset language:

English

Fields of science:

Automation, electronic and electrical engineering (Engineering and Technology)
materials engineering (Engineering and Technology)

DOI:

10.34808/9bbn-ar91

Funding:

Understanding and minimization of ohmic and polarization losses in solid oxide cells by nanocrystalline ceramic and cermet functional layers

Series:

Impact of strontium non-stoichiometry of SrxTi0.3Fe0.7O3-δ

Verified by:

Gdańsk University of Technology

Keywords

Cite as

Authors

seen 45 times

Search