Linear impedance of strontium–borate glass measured with impedance spectroscopy method at high temperature region
Description
The linear electrcial properties of strontium–borate glass was measured by impedance spectroscopy method.
SBO glass samples were prepared from reagent-grade SrCO3 and H3BO3. Samples of glass were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at 1373 K for 2 hours. The melt was poured onto a preheated (573 K) brass plate and pressed by another plate to obtain flat circular disks of 1–2 mm thickness and 20–30 mm in diameter.
For the electrical measurements gold electrodes were evaporated at the preheated samples. Impedance measurements were carried out in the frequency range from 1 mHz to 1 MHz and the temperature range from 273 K to 813 K, with the ac voltage of 1 Vrms with Concept 40 broadband dielectric spectrometer and a high temperature Controller Novotherm HT 1600. The measurements were carried out both while increasing and decreasing the temperature. Measurements were done two times.
Dataset file
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.Example script for calculation:
https://github.com/antespi/s3md5
File details
- License:
-
open in new tab
CC BYAttribution - Raw data:
- Data contained in dataset was not processed.
Details
- Year of publication:
- 2015
- Verification date:
- 2021-06-21
- Dataset language:
- English
- Fields of science:
-
- materials engineering (Engineering and Technology)
- DOI:
- DOI ID 10.34808/g4eh-bw88 open in new tab
- Verified by:
- Gdańsk University of Technology
Keywords
References
- publication Electronic and ionic relaxations in strontium-borate glass and glass-ceramics containing bismuth and vanadium oxides
- publication STRUKTURA ORAZ WŁAŚCIWOŚCI ELEKTRYCZNE MATERIAŁÓW SZKLISTYCH ZAWIERAJĄCYCH GRANULE FERROELEKTRYKA Bi2VO5,5
Cite as
Authors
seen 103 times