The DataSet contains the emission and excitation spectra of TeOx-Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of dysprosium ions were added, the nitrates were used as a source of rare-earth ions. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised to 75°C for the next 2h. Next, the sol was used to prepared thin films by a spin coating method. The corning glass with 8 nm alumina oxide was used as a substrate. After deposition, the thin films were dried at 200°C under an argon atmosphere, then were annealing at 400°C under oxidizing atmosphere.
Luminescence emission and excitation spectra of gel were collected in a Horiba Yvon spectrofluorometer (Fluorolog 3).
Dataset file
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.Example script for calculation:
https://github.com/antespi/s3md5
File details
- License:
-
open in new tab
CC BYAttribution - Raw data:
- Data contained in dataset was not processed.
Details
- Year of publication:
- 2021
- Verification date:
- 2021-07-19
- Dataset language:
- English
- Fields of science:
-
- materials engineering (Engineering and Technology)
- DOI:
- DOI ID 10.34808/3vs1-2529 open in new tab
- Series:
- Verified by:
- Gdańsk University of Technology
Keywords
Cite as
Authors
seen 103 times