Mercury intrusion porosimetry (MIP) results of cement pastes containing iron oxide (Fe3O4) nanoparticles (nanomagnetite)
Description
Mercury intrusion porosimetry (MIP) data - curves of cement pastes containing iron oxide (Fe3O4) nanoparticles (nanomagnetite) in *.opju (Origin) format.
A MIP test was performed after 28 days of curing, with the use of Pascal 140 and 240 series (Thermo Scientific) mercury intrusion porosimeters. Prior to testing, small-cored specimens taken from the samples were immersed in isopropanol and then freeze-dried to stop hydration. The mercury density was 13.55 g/mL, the surface tension was taken as 0.48 N/m, while the selected contact angle was 140°.
Specimen designation is associated with samples designation in the associated manuscript.
NM0 - control specimen
NM5, NM5, NM10, NM15, NM20, NM30 - digit presents the percentage amount of cement replacement with Fe3O4 nanoparticles
Dataset file
hexmd5(md5(part1)+md5(part2)+...)-{parts_count}
where a single part of the file is 512 MB in size.Example script for calculation:
https://github.com/antespi/s3md5
File details
- License:
-
open in new tabCC BYAttribution
- Raw data:
- Data contained in dataset was not processed.
Details
- Year of publication:
- 2023
- Verification date:
- 2023-11-06
- Dataset language:
- English
- Fields of science:
-
- civil engineering, geodesy and transport (Engineering and Technology)
- DOI:
- DOI ID 10.5281/zenodo.7622612 open in new tab
- Funding:
- Verified by:
- West Pomeranian University of Technology in Szczecin
Keywords
References
Cite as
Authors
seen 104 times