The luminescence study of Sr2TiO4:Sm3+ coumpounds.

Description

A luminescent material based on the strontium orthotitanate (Sr₂TiO₄) matrix doped with 1% of a mole of samarium was obtained using the typical solid-state synthesis method under a neutral atmosphere of nitrogen. The sample was investigated using powder X-ray diffraction (XRD) and several luminescence techniques to study the phase composition, luminescence properties as well as to determine the position of the energetic states of Sm³⁺ in relation to the valence and conduction bands of Sr₂TiO₄. The XRD result shows that the product of the synthesis is pure Sr₂TiO₄. From the PL spectra, it can be seen that the phosphor can be effectively excited at 409 and 342 nm to emit significantly different emission spectra. The luminescence obtained under 409 nm excitation is typical of Sm³⁺ in Sr₂TiO₄ and attributed to the nonsymmetrical luminescent center (A-center). In contrast, the luminescence obtained under excitation at 342 nm originates from the symmetrical center (B-center) and has not been reported in the literature so far. The presence of the two emission centers related to Sm³⁺ ions in the Sr₂TiO₄ matrix characterized by only one crystallographic site of Sr²⁺ was explained by considering the different ways of charge compensation: Sm³⁺ in the A-center via strontium vacancy (V′′_sr), and Sm³⁺ in the B-center via Ti³⁺ (Ti′_Ti).

In that dataset, the scientific article, raw data of X-ray diffraction, photoconductivity, excitation and emission spectra, and temperature-dependent photoluminescence and decay profiles are provided.

Dataset file

Energetic structure of Sm3+ luminescence centers.rar

4.8 MB, S3 ETag 6ab5304688a3fae9202427c38cfc57d5-1, downloads: 68

The file hash is calculated from the formula
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.

Example script for calculation:
https://github.com/antespi/s3md5

download

File details

License:: open in new tab

CC BY

Attribution
Raw data:: Data contained in dataset was not processed.
Software:: HPD-TA

Details

Year of publication:

2022

Verification date:

2022-03-04

Dataset language:

English

Fields of science:

physical sciences (Natural sciences)

DOI:

10.34808/yf83-rg27

Verified by:

No verification

Keywords

Cite as

Authors

seen 174 times

Search