Description
The structure of iron-doped glasses and glass-ceramics were studied. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated (573 K) brass plate and pressed by an another plate to obtain flat circular samples of 1–2 mm thickness and 20–30 mm in diameter. The quenched pellets were annealed at the temperature of 673 K for 3
h and cooled with the furnace. The presence of crystalline phases was examined by the X-ray diffraction method with the use of a Philips X'Pert Pro MPD system with CuKα radiation. Detailed information can be found in: http://dx.doi.org/10.1016/j.ssi.2014.01.042
Dataset file
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.Example script for calculation:
https://github.com/antespi/s3md5
File details
- License:
-
open in new tab
CC BYAttribution - Raw data:
- Data contained in dataset was not processed.
Details
- Year of publication:
- 2014
- Verification date:
- 2021-05-06
- Dataset language:
- English
- Fields of science:
-
- materials engineering (Engineering and Technology)
- DOI:
- DOI ID 10.34808/gpc8-c326 open in new tab
- Verified by:
- Gdańsk University of Technology
Keywords
References
Cite as
Authors
seen 109 times