Details
- Project's acronym:
- CorPorAl
- Financial Program Name:
- SONATA_BIS
- Organization:
- Narodowe Centrum Nauki (NCN) (National Science Centre)
- Agreement:
- UMO-2018/30/E/ST8/00821 z dnia 2019-07-01
- Realisation period:
- 2019-07-01 - 2024-09-30
- Project manager:
- dr hab. inż. Sebastian Molin
- Team members:
-
- PhD student mgr inż. Agnieszka Drewniak
- PhD student Damian Koszelow
- Post doc dr inż. Samih Haj Ibrahim
- Realised in:
- Laboratorium Materiałów Funkcjonalnych ETI
- Project's value:
- 1 977 000.00 PLN
- Request type:
- National Research Programmes
- Domestic:
- Domestic project
- Verified by:
- Gdańsk University of Technology
Papers associated with that project
Filters
total: 5
Catalog Projects
Year 2023
-
High-temperature Corrosion of ~ 30 Pct Porous FeCr Stainless Steels in Air: Long-Term Evaluation Up to Breakaway
PublicationIn this work, a long-term (up to 6000 hours) corrosion evaluation of three porous (~ 30 pct of initial porosity) ferritic iron-chromium alloys with different Cr contents (20, 22, and 27 wt pct of Cr) was carried out at 600 C, 700 C, 800 C, and 900 C in air. Mass gain measurements and SEM analyses revealed that at temperatures above 600 C, all alloys exhibit breakaway corrosion, whereas at 600 C, none of the alloys were heavily...
Year 2022
-
Morphology changes in Fe-Cr porous alloys upon high-temperature oxidation quantified by X-ray tomographic microscopy
PublicationThe effect of high-temperature oxidation at 850 C (10 h, 30 h, 100 h) and 900 C (10 h) on porous (30 % porosity) ferritic stainless steel (Fe22Cr) has been investigated using synchrotron tomographic microscopy, which allowed for visualisation, separation and quantitative analysis of the metallic core, closed pores, open pores and oxide scale phase. The same regions within the samples were investigated before and after oxidation...
-
Glass-ceramic joining of Fe22Cr porous alloy to Crofer22APU: interfacial issues and mechanical properties
PublicationThis work deals with the joining of porous Fe22Cr ferritic stainless steel to a dense Crofer22APU plate by using a silica-based, Ba-containing glass-ceramic. The chemical and interfacial stability and the mechanical properties of the joints were evaluated before and after thermal ageing at 700 ◦C for 500hrs. The sintering behaviour of the glass was assessed by using heating stage microscopy (HSM) to study the influence of a porous...
Year 2021
-
High temperature corrosion evaluation and lifetime prediction of porous Fe22Cr stainless steel in air in temperature range 700–900 °C
PublicationThis work describes a high temperature corrosion kinetics study of ~30% porous Fe22Cr alloys. The surface area of the alloy (~0.02 m2 g-1) has been determined by tomographic microscopy. The weight gain of the alloys was studied by isothermal thermogravimetry in the air for 100 hours at 700 - 900 °C. Breakaway oxidation was observed after oxidation at 850 °C (~100 hours) and 900 °C (~30 hours). The lifetime prediction shows the...
-
Glass-ceramic sealants and steel interconnects: accelerated interfacial stability and reactivity tests at high temperature
PublicationHigh-temperature reactions between glass-ceramic sealants and Fe-Cr alloy interconnects may lead to the formation of undesirable phases, and consequently degradation of solid oxide fuel/electrolyser devices. In this work, three different glass-ceramic sealants (Na-containing, Ba-containing, Sr-containing compositions) and Fe22Cr stainless steel powders (raw and pre-oxidised) are considered in order to test their chemical reactivity...