Details
- Project's acronym:
- LNO
- Financial Program Name:
- IUVENTUS PLUS
- Organization:
- Ministerstwo Nauki i Szkolnictwa Wyższego (MNiSW)
- Agreement:
- 0513/IP2/2016/74 z dnia 2016-10-19
- Realisation period:
- 2016-10-19 - 2020-04-18
- Project manager:
- dr hab. inż. Aleksandra Dorota Mielewczyk-Gryń
- Team members:
-
- co-investigator dr inż. Sebastian Lech Wachowski
- co-investigator dr inż. Marta Prześniak-Welenc
- Realised in:
- Department of Solid State Physics
- Project's value:
- 281 998.00 PLN
- Request type:
- National Research Programmes
- Domestic:
- Domestic project
- Verified by:
- Gdańsk University of Technology
Papers associated with that project
Filters
total: 4
Catalog Projects
Year 2023
-
Vibrational Properties of LaNb0.8M0.2O4-δ (M=As, Sb, V, and Ta)
PublicationLaNb0.8M0.2O4-δ (where M=As, Sb, V, and Ta) oxides with pentavalent elements of different ionic sizes were synthesized by a solid-state reaction method. The vibrational properties of these oxides have been investigated. These studies revealed that the substituent element influences both Debye temperature value as well as the Raman active vibrational modes. Additionally, the low-temperature vibrational properties of LaNb0.8Sb0.2O4-δ...
Year 2019
-
Synthesis, microstructure and electrical properties of nanocrystalline calcium doped lanthanum orthoniobate
PublicationThe single phase lanthanum orthoniobate with tetragonal structure has been synthesized by the means of mechanosynthesis method. The studies have shown the crystal structure of La0.98Ca0.02NbO4 depends on the synthesis stage. The samples were predominantly in the tetragonal phase with a trace amount of the monoclinic phase. The SEM studies of morphology and microstructure have shown nanocrystallinity of the materials. The Raman...
-
Terbium Substituted Lanthanum Orthoniobate: Electrical and Structural Properties
PublicationThe results of electrical conductivity studies, structural measurements and thermogravimetric analysis of La1−xTbxNbO4+δ (x = 0.00, 0.05, 0.1, 0.15, 0.2, 0.3) are presented and discussed. The phase transition temperatures, measured by high-temperature x-ray diffraction, were 480 °C, 500 °C, and 530 °C for La0.9Tb0.1NbO4+δ, La0.8Tb0.2NbO4+δ, and La0.7Tb0.3NbO4+δ, respectively. The impedance spectroscopy results suggest mixed conductivity...
-
Water uptake analysis of acceptor-doped lanthanum orthoniobates
PublicationIn this work, lanthanum orthoniobates doped with either antimony, calcium, or both have been synthesized and studied. The water uptake of the investigated materials has been analyzed by means of thermogravimetric studies. The results show the difference between the thermodynamics of hydration between the lanthanum orthoniobate system and other proton conducting ceramics. The relation between the water uptake and effective acceptor...