Doping of Na and K at La sites and of B at Si site in La10Si6O27 with oxyapatite structure and fabrication of their ceramics were made by the solid-state reaction method. It was found that partial substitution of Na+ and K+ on La sites decreased the sinterability of the La10Si6O27 based ceramics, whereas partial substitution of B3+ on the Si site improved the sinterability. Na+ and K+ substitutions in La10−xNaxSi6O27−x and La10−xKxSi6O27−x can suppress second-phase La2SiO5 formation, and, in this study, as the x value of the two substitutions reached 0.7 and 0.5, respectively, the La2SiO5 phase disappeared. Doping of Na+, K+, and B3+ all displayed the hindering effect of grain growth during sintering. Compositions of La9.3Na0.7Si6O26.3, La9.5K0.5Si6O26.5, and La10Si5.5B0.5O26.75 revealed the highest electrical conductivity in each system. La10Si5.5B0.5O26.75 ceramic sintered at 1575°C showed the highest electrical conductivity at temperatures above 600°C among all the apatite ceramics evaluated. The electrical conductivities of La10Si5.5B0.5O26.75 at 700°C and 800°C reported 0.011 S cm−1 and 0.024 S cm−1, respectively, which are superior or comparable to previous studies, and their activation energies for conduction were calculated to be 0.80 eV.
Citations
-
5
CrossRef
-
0
Web of Science
-
5
Scopus
Authors (5)
-
Sea-Fue Wang
- National Taipei University of Technology
-
Yung-Fu Hsu
- National Taipei University of Technology
-
Yi-Le Liao
- National Taipei University of Technology
-
Ting-Ting Yang
- National Taipei University of Technology
Cite as
Full text
full text is not available in portal
Keywords
Details
- Category:
- Articles
- Type:
- artykuły w czasopismach
- Published in:
-
JOURNAL OF ELECTRONIC MATERIALS
no. 48,
pages 6287 - 6297,
ISSN: 0361-5235 - Language:
- English
- Publication year:
- 2019
- Bibliographic description:
- Wang S., Hsu Y., Liao Y., Yang T., Jasiński P.: Effects of Na+, K+ and B3+ Substitutions on the Electrical Properties of La10Si6O27 Ceramics// JOURNAL OF ELECTRONIC MATERIALS -Vol. 48,iss. 10 (2019), s.6287-6297
- DOI:
- Digital Object Identifier (open in new tab) 10.1007/s11664-019-07407-z
- Verified by:
- Gdańsk University of Technology
seen 80 times
Recommended for you
Effects of Na+, K+ and B3+ Substitutions on the Electrical Properties of La10Si6O27 Ceramics
- S. Wang,
- Y. Hsu,
- Y. Liao
- + 2 authors
Effects of Ca2+, Mg2+, Na+, and K+ substitutions on the microstructure and electrical properties of GdCoO3 ceramics
- S. Wang,
- Y. Hsu,
- Y. Liao
- + 2 authors
High temperature proton conduction in LaSbO4
- P. Winiarz,
- A. Mielewczyk-Gryń,
- K. Dzierzgowski
- + 2 authors
Characteristics of La 0.8 Sr 0.2 Ga 0.8 Mg 0.2 O 3-δ -supported micro-tubular solid oxide fuel cells with LaCo 0.4 Ni 0.6-x Cu x O 3-δ cathodes
- Y. Liu,
- S. Wang,
- Y. Hsu
- + 1 authors