Effects of Na+, K+ and B3+ Substitutions on the Electrical Properties of La10Si6O27 Ceramics

Abstract

Doping of Na and K at La sites and of B at Si site in La10Si6O27 with oxyapatite structure and fabrication of their ceramics were made by solid-state reaction method. It was found that partial substitution of Na+ and K+ on La sites decreased the sinterability of the La10Si6O27 based ceramics, whereas partial substitution of B3+ on Si site imporved the sinterability. Na+ and K+ substitutions in La10-xNaxSi6O27-x and La10-xKxSi6O27-x were found to suppress second-phase La2SiO5 formation. La10Si5.5B0.5O26.75 ceramic sintered at 1575ºC showed the highest electrical conductivity at temperatures above 600ºC among all the apatite ceramics evaluated. The electrical conductivities of La10Si5.5B0.5O26.75 at 700ºC and 800ºC reported 0.011 and 0.024 S cm-1, respectively, which are superior or comparable to previous studies, and their activation energies for conduction were calculated to be 0.80 eV.

Citations

  • 2

    CrossRef

  • 0

    Web of Science

  • 2

    Scopus

Authors (5)

Cite as

Full text

full text is not available in portal

Keywords

Details

Category:
Articles
Type:
artykuły w czasopismach
Published in:
ECS Transactions no. 91, pages 1223 - 1228,
ISSN: 1938-5862
Language:
English
Publication year:
2019
Bibliographic description:
Wang S., Hsu Y., Liao Y., Yang T., Jasiński P.: Effects of Na+, K+ and B3+ Substitutions on the Electrical Properties of La10Si6O27 Ceramics// ECS Transactions -Vol. 91,iss. 1 (2019), s.1223-1228
DOI:
Digital Object Identifier (open in new tab) 10.1149/09101.1223ecst
Verified by:
Gdańsk University of Technology

seen 79 times

Recommended for you

Effects of Na+, K+ and B3+ Substitutions on the Electrical Properties of La10Si6O27 Ceramics

  • S. Wang,
  • Y. Hsu,
  • Y. Liao
  • + 2 authors
2019

Impact of strontium non-stoichiometry of SrxTi0.3Fe0.7O3-δ on structural, electrical, and electrochemical properties for potential oxygen electrode of intermediate temperature solid oxide cells

2023

Characteristics of La 0.8 Sr 0.2 Ga 0.8 Mg 0.2 O 3-δ -supported micro-tubular solid oxide fuel cells with LaCo 0.4 Ni 0.6-x Cu x O 3-δ cathodes

  • Y. Liu,
  • S. Wang,
  • Y. Hsu
  • + 1 authors
2018

Effects of Ca2+, Mg2+, Na+, and K+ substitutions on the microstructure and electrical properties of GdCoO3 ceramics

  • S. Wang,
  • Y. Hsu,
  • Y. Liao
  • + 2 authors
2020
Meta Tags