Abstract
The present paper is aimed at determining the less investigated effects of hydrogen uptake on the microstructure and the mechanical behavior of the oxidized Zircaloy-2 alloy. The specimens were oxidized and charged with hydrogen. The different oxidation temperatures and cathodic current densities were applied. The scanning electron microscopy, X-ray electron diffraction spectroscopy, hydrogen absorption assessment, tensile, and nanoindentation tests were performed. At low oxidation temperatures, an appearance of numerous hydrides and cracks, and a slight change of mechanical properties were noticed. At high-temperature oxidation, the oxide layer prevented the hydrogen deterioration of the alloy. For nonoxidized samples, charged at different current density, nanoindentation tests showed that both hardness and Young’s modulus revealed the minims at specific current value and the stepwise decrease in hardness during hydrogen desorption. The obtained results are explained by the barrier effect of the oxide layer against hydrogen uptake, softening due to the interaction of hydrogen and dislocations nucleated by indentation test, and hardening caused by the decomposition of hydrides. The last phenomena may appear together and result in hydrogen embrittlement in forms of simultaneous hydrogen-enhanced localized plasticity and delayed hydride cracking.
Citations
-
4
CrossRef
-
0
Web of Science
-
4
Scopus
Authors (6)
-
Bartosz Chmiela dr inż.
Cite as
Full text
- Publication version
- Accepted or Published Version
- License
-
open in new tab
Keywords
Details
- Category:
- Articles
- Type:
- artykuły w czasopismach
- Published in:
-
Materials
no. 13,
ISSN: 1996-1944 - Language:
- English
- Publication year:
- 2020
- Bibliographic description:
- Gajowiec G., Bartmański M., Majkowska-Marzec B., Zieliński A., Chmiela B., Derezulko M.: Hydrogen Embrittlement and Oxide Layer E ect in the Cathodically Charged Zircaloy-2// Materials -Vol. 13,iss. 8 (2020), s.1913-
- DOI:
- Digital Object Identifier (open in new tab) 10.3390/ma13081913
- Verified by:
- Gdańsk University of Technology
seen 139 times
Recommended for you
Oxidation and hydrogen behavior in Zr-2Mn alloy
- N. Zienkiewicz,
- J. Paradowska,
- W. Serbiński
- + 3 authors
Hydrogen degradation of pre-oxidized zirconium alloys
- A. Szoka,
- G. Gajowiec,
- A. Zieliński
- + 3 authors
X-Ray Computer Tomography Study of Degradation of the Zircaloy-2 Tubes Oxidized at High Temperatures
- B. Trybuś,
- J. Olive,
- N. Lenoir
- + 1 authors