Influence of hydrogen on a nanocrystalline high-entropy oxide with application potential in hydrogen technologies
Abstract
The influence of hydrogen on a (Co0⋅2Cu0⋅2Mg0⋅2Ni0⋅2Zn0.2)O HEO with a rock salt structure was studied. Two forms of this HEO (nanopowder and sinter) were prepared via mechanochemical synthesis (MS) and additional heat treatment, respectively. The chemical stability of the synthesized samples in a pure hydrogen atmosphere was investigated using Sievert’s technique. High-pressure hydrogenation at 250 ◦C had no noticeable effect on the HEO sinter. The sintered sample was chemically, structurally, and morphologically stable, as confirmed via the XRD, Raman spectroscopy, SEM, and XPS techniques. Thermogravimetric analysis (TGA) showed the sinter to be stable in an argon gas mixture with 5 vol% of hydrogen and over the temperature range of up to 400 ◦C.
Citations
-
2
CrossRef
-
0
Web of Science
-
2
Scopus
Authors (6)
-
Kamil Domaradzki
- Akademia Górnczo-Hutnicza
-
Marek Nowak
- Politechnika Poznańska
-
Maciej Sitarz
- Akademia Górnczo-Hutnicza
-
Tomasz Brylewski
- Akademia Górnczo-Hutnicza
-
Mieczysław Jurczyk
- Uniwersytet Zielonogórski
Cite as
Full text
full text is not available in portal
Keywords
Details
- Category:
- Articles
- Type:
- artykuły w czasopismach
- Published in:
-
CERAMICS INTERNATIONAL
no. 49,
pages 15544 - 15552,
ISSN: 0272-8842 - Language:
- English
- Publication year:
- 2023
- Bibliographic description:
- Domaradzki K., Nowak M., Sitarz M., Łapiński M., Brylewski T., Jurczyk M.: Influence of hydrogen on a nanocrystalline high-entropy oxide with application potential in hydrogen technologies// CERAMICS INTERNATIONAL -Vol. 49,iss. 10 (2023), s.15544-15552
- DOI:
- Digital Object Identifier (open in new tab) 10.1016/j.ceramint.2023.01.142
- Sources of funding:
-
- Free publication
- Verified by:
- Gdańsk University of Technology
seen 77 times
Recommended for you
Synergistic effects of nitrogen-doped carbon and praseodymium oxide in electrochemical water splitting
- P. Grabowska,
- M. Szkoda,
- M. Skorupska
- + 2 authors