Pulsed Laser Deposition of Bismuth Vanadate Thin Films—The Effect of Oxygen Pressure on the Morphology, Composition, and Photoelectrochemical Performance - Publication - Bridge of Knowledge

Your account

login

Search

Pulsed Laser Deposition of Bismuth Vanadate Thin Films—The Effect of Oxygen Pressure on the Morphology, Composition, and Photoelectrochemical Performance

Abstract

Thin layers of bismuth vanadate were deposited using the pulsed laser deposition technique on commercially available FTO (fluorine-doped tin oxide) substrates. Films were sputtered from a sintered, monoclinic BiVO4 pellet, acting as the target, under various oxygen pressures (from 0.1 to 2 mbar), while the laser beam was perpendicular to the target surface and parallel to the FTO substrate. The oxygen pressure strongly affects the morphology and the composition of films observed as a Bi:V ratio gradient along the layer deposited on the substrate. Despite BiVO4, two other phases were detected using XRD (X-ray diffraction) and Raman spectroscopy—V2O5 and Bi4V2O11. The V-rich region of the samples deposited under low and intermediate oxygen pressures was covered by V2O5 longitudinal structures protruding from BiVO4 film. Higher oxygen pressure leads to the formation of Bi4V2O11@BiVO4 bulk heterojunction. The presented results suggest that the ablation of the target leads to the plasma formation, where Bi and V containing ions can be spatially separated due to the interactions with oxygen molecules. In order to study the phenomenon more thoroughly, laser-induced breakdown spectroscopy measurements were performed. Then, obtained electrodes were used as photoanodes for photoelectrochemical water splitting. The highest photocurrent was achieved for films deposited under 1 mbar O2 pressure and reached 1 mA cm−2 at about 0.8 V vs Ag/AgCl (3 M KCl). It was shown that V2O5 on the top of BiVO4 decreases its photoactivity, while the presence of a bulk Bi4V2O11@BiVO4 heterojunction is beneficial in water photooxidation.

Citations

  • 8

    CrossRef

  • 0

    Web of Science

  • 7

    Scopus

Authors (7)

Cite as

Full text

download paper
downloaded 78 times
Publication version
Accepted or Published Version
License
Creative Commons: CC-BY open in new tab

Keywords

Details

Category:
Articles
Type:
artykuły w czasopismach
Published in:
Materials no. 13, pages 1 - 16,
ISSN: 1996-1944
Language:
English
Publication year:
2020
Bibliographic description:
Trzciński K., Szkoda M., Gazda M., Karczewski J., Cenian A., Grigorian G., Sawczak M.: Pulsed Laser Deposition of Bismuth Vanadate Thin Films—The Effect of Oxygen Pressure on the Morphology, Composition, and Photoelectrochemical Performance// Materials -Vol. 13,iss. 6 (2020), s.1-16
DOI:
Digital Object Identifier (open in new tab) 10.3390/ma13061360
Verified by:
Gdańsk University of Technology

seen 144 times

Recommended for you

Enhanced Photoelectrocatalytical Performance of Inorganic-Inorganic Hybrid Consisting BiVO4, V2O5, and Cobalt Hexacyanocobaltate as a Perspective Photoanode for Water Splitting

2020

The bismuth vanadate thin layers modified by cobalt hexacyanocobaltate as visible-light active photoanodes for photoelectrochemical water oxidation

2019

Micropatterning of BiVO 4 Thin Films Using Laser-Induced Crystallization

2016

Widening of the electroactivity potential range by composite formation – capacitive properties of TiO2/BiVO4/PEDOT:PSS electrodes in contact with an aqueous electrolyte

2019
Meta Tags