Structure analysis and thermal degradation characteristics of bio-based poly(propylene succinate)s obtained by using different catalyst amounts

Paulina Parcheta-Szwindowska; Janusz Datta

doi:10.1007/s10973-017-6376-3

Structure analysis and thermal degradation characteristics of bio-based poly(propylene succinate)s obtained by using different catalyst amounts

Abstract

Linear bio-based polyester polyols were prepared with the use of succinic acid and 1.3-propanediol (both with natural origin). As a catalyst was used tetraisopropyl orthotitanate (TPT). In order to determine the effect of various catalyst content on the thermal degradation characteristics, three different TPT amounts, as a 1.3-propanediol equivalent, were used, namely 0.1 mass% (PPS-0.1), 0.2 mass% (PPS-0.2) and 0.25 mass% (PPS-0.25). The reference polyol was prepared without catalyst employment (PPS-0.0). Fourier transform infrared spectroscopy was used to confirm molecular structure of the resulted polyols. The structure was also corroborated by 1H NMR measurements, what confirmed nonsignificant catalyst amount impact on the structure of the prepared polyester polyols. Differential scanning calorimetry was carried out for glass transition temperature and melting point determination. The thermogravimetric analysis allowed to observe high thermal stability both under inert and oxidative atmosphere. This analysis affirmed also that the catalyst content did not influence significantly on the thermal degradation characteristics of the prepared polyols.

Citations

1 7

CrossRef
0

Web of Science
1 9

Scopus

Authors (2)

Paulina Parcheta-Szwindowska (formerly: Paulina Parcheta) dr inż.
Janusz Datta prof. dr hab. inż.

Cite as

Full text

download paper

downloaded 39 times

Publication version: Accepted or Published Version
DOI:: Digital Object Identifier (open in new tab) 10.1007/s10973-017-6376-3
License: open in new tab

full content of the article see on external site open in new tab

Keywords

Details

Category:: Articles
Type:: artykuł w czasopiśmie wyróżnionym w JCR
Published in:: JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY no. 130, edition 1, pages 197 - 206,
ISSN: 1388-6150
Language:: English
Publication year:: 2017
Bibliographic description:: Parcheta P., Datta J.: Structure analysis and thermal degradation characteristics of bio-based poly(propylene succinate)s obtained by using different catalyst amounts// JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY. -Vol. 130, iss. 1 (2017), s.197-206
DOI:: Digital Object Identifier (open in new tab) 10.1007/s10973-017-6376-3
Verified by:: Gdańsk University of Technology