X-Ray Diffraction, Mössbauer Spectroscopy and Magnetoelectric Effect Studies of Multiferroic Bi5Ti3FeO15 Ceramics

Abstract

Bi5Ti3FeO15 ceramics belongs to multiferroic class of materials. In this work it was prepared by solid-state sintering method and investigated by X-ray diffraction, Mössbauer spectroscopy, and magnetoelectric effect measurements. As it was proved by X-ray diffraction studies the single-phase Bi5Ti3FeO15 compound was obtained. The Mössbauer investigations revealed paramagnetic character of the compound at room temperature as well as at 80 K. Magnetoelectric measurements were carried out at room temperature using lock-in dynamic method and they proved presence of magnetoelectric coupling in this material. Additional magnetoelectric studies were carried out after subsequent electric poling of the sample. It was found that the maximum value of the coupling coefficient was almost twice bigger than in the case without the initial poling and reached a value of αME ≈ 20.7 mV cm-1 Oe-1.

Citations

  • 1 7

    CrossRef

  • 0

    Web of Science

  • 1 9

    Scopus

Authors (5)

Keywords

Details

Category:
Articles
Type:
artykuły w czasopismach
Published in:
ACTA PHYSICA POLONICA A no. 127, pages 296 - 299,
ISSN: 0587-4246
Language:
English
Publication year:
2015
Bibliographic description:
Pikula T., Guzdek P., Dzik J., Lisińska-Czekaj A., Jartych E.: X-Ray Diffraction, Mössbauer Spectroscopy and Magnetoelectric Effect Studies of Multiferroic Bi5Ti3FeO15 Ceramics// ACTA PHYSICA POLONICA A -Vol. 127,iss. 2 (2015), s.296-299
DOI:
Digital Object Identifier (open in new tab) 10.12693/aphyspola.127.296
Verified by:
Gdańsk University of Technology

seen 80 times

Recommended for you

Meta Tags